Anionic polymerization of methyl methacrylate (MMA), n-butyl methacrylate (nBMA) and glycidyl methacrylate (GMA) initiated by nBuCu(NCy2)Li (1) in tetrahydrofuran (THF) at -50°C to-10°C was investigated. It was found that the polymerization of MMA and nBMA initiated by 1 proceeded quantitatively in THF to afford PMMA and PBMA with polydispersity index 1.15-1.30 and nearly 100% initiator efficiencies at -10°C. The molecular weights increased linearly with the ratio of [monomer]/[1]. However, a post-polymerization experiment carried out on this system revealed a double polymer peak by GPC when fresh monomer was added after an interval of 10 min. Polymerization of styrene could be initiated by 1, but the initiator efficiency was low.