Highly Hydrolysis-Resistant Polyimide Fibers Prepared by Thermal Crosslinking with Inherent Carboxyl Groups

Shi-Xu Zhou; Jie Dong; Xiu-Ting Li; Xin Zhao; Qing-Hua Zhang

doi:10.1007/s10118-023-3015-2

Your Location：

Home >

Browse articles >

Highly Hydrolysis-Resistant Polyimide Fibers Prepared by Thermal Crosslinking with Inherent Carboxyl Groups

RESEARCH ARTICLE | Updated：2024-01-12

- Highly Hydrolysis-Resistant Polyimide Fibers Prepared by Thermal Crosslinking with Inherent Carboxyl Groups
- Highly Hydrolysis-Resistant Polyimide Fibers Prepared by Thermal Crosslinking with Inherent Carboxyl Groups
- 高分子科学（英文版） 2024年42卷第2期页码：247-255
- Affiliations：
  
  State Key Laboratory for Modification of Chemical Fibres and Polymer Materials, College of Materials Science and Engineering, Donghua University, Shanghai 201620, China
- Author bio：
  
  qhzhang@dhu.edu.cn
- Funds：
  
  This work was financially supported by the Scientific Research Innovation Plan of Shanghai Education Commission (No. 2019-01-07-00-03-E00001), the National Natural Science Foundation of China (Nos. U21A2087 and 21975040) and the Natural Science Foundation of Shanghai (No. 21ZR1400200).;Electronic supplementary information (ESI) is available free of charge in the online version of this article at http://doi.org/10.1007/s10118-023-3015-2.
- DOI：10.1007/s10118-023-3015-2
  中图分类号：
Scan for full text
Zhou, S. X.; Dong, J.; Li, X. T.; Zhao, X.; Zhang, Q. H. Highly hydrolysis-resistant polyimide fibers prepared by thermal crosslinking with inherent carboxyl groups. Chinese J. Polym. Sci. 2024, 42, 247–255

Shi-Xu Zhou, Jie Dong, Xiu-Ting Li, et al. Highly Hydrolysis-Resistant Polyimide Fibers Prepared by Thermal Crosslinking with Inherent Carboxyl Groups[J]. Chinese Journal of Polymer Science, 2024,42(2):247-255.
Zhou, S. X.; Dong, J.; Li, X. T.; Zhao, X.; Zhang, Q. H. Highly hydrolysis-resistant polyimide fibers prepared by thermal crosslinking with inherent carboxyl groups. Chinese J. Polym. Sci. 2024, 42, 247–255 DOI： 10.1007/s10118-023-3015-2.

Shi-Xu Zhou, Jie Dong, Xiu-Ting Li, et al. Highly Hydrolysis-Resistant Polyimide Fibers Prepared by Thermal Crosslinking with Inherent Carboxyl Groups[J]. Chinese Journal of Polymer Science, 2024,42(2):247-255. DOI： 10.1007/s10118-023-3015-2.

摘要

The hydrolysis resistance of polyimide fibers can be improved by crosslinking of the macromolecular chains. Crosslinked polyimide fibers were produced by intrinsic carboxyl decarboxylation. The oriented macromolecules and chemically crosslinked structure improved the tightness of the molecular chains and endowed the CPI fibers with excellent hydrolytic resistance.

Abstract

Easy hydrolysis in alkaline environments limits the use of polyimide fibers in environmental protection. The hydrolysis resistance levels of polyimide fibers can be improved by crosslinking of the macromolecular chains. In this work, crosslinked polyimide fibers (CPI fibers) were produced by intrinsic carboxyl decarboxylation for the first time. The thermal stability of the polyimide fibers containing the intrinsic carboxyl groups (PIC fibers) was studied, and the temperature of the decarboxylation-crosslinking reaction was determined to be 450 °C. The PIC fibers were hot-drawn to initiate thermal crosslinking of the carboxyl groups and molecular chain orientation at high temperature. The CPI fibers had high tensile strengths (0.72−1.46 GPa) and compressive strengths (401−604 MPa). The oriented macromolecules and chemically crosslinked structure improved the tightness of the molecular chains and endowed the CPI fibers with excellent hydrolytic resistance. The CPI-50 fiber did not dissolve in a 0.5 wt% NaOH solution during heating at 90 °C for 10 h, and the tensile strength retention reached 87% when treated in 0.5 wt% NaOH solutions at 90 °C for 1 h, providing a guarantee for its application in alkaline corrosive environments.

关键词

Keywords

PolyimideCarboxyl groupCrosslinkingHydrolysis-resistance

references

Mukhopadhyay,A.;Pandit,V.;Dhawan,K.Effectofhightemperatureontheperformanceoffilterfabric.J. Ind. Text.2015,45,1587−1602..

Liaw,D.J.;Wang,K.L.;Huang,Y.C.;Lee,K.R.;Lai,J.Y.;Ha,C.S.Advancedpolyimidematerials:syntheses,physicalpropertiesandapplications.Prog. Polym. Sci.2012,37,907−974..

Zhou,Z.X.;Zhang,Y.;Liu,S.W.;Chi,Z.G.;Chen,X.D.;Xu,J.R.Flexibleandhighlyfluorescentaromaticpolyimide:design,synthesis,properties,andmechanism.J. Mater. Chem. C2016,4,10509−10517..

Rusu,R.D.;Constantin,C.P.;Drobota,M.;Gradinaru,L.M.;Butnaru,M.;Pislaru,M.PolyimidefilmstailoredbyUVirradiation:surfaceevaluationandstructure-propertiesrelationship.Polym. Degrad. Stabil.2020,177,109182−109294..

Liu,H.;Chen,X.Y.;Zheng,Y.J.;Zhang,D.B.;Zhao,Y.;Wang,C.F.;Pan,C.F.;Liu,C.T.;Shen,C.Y.Lightweight,superelastic,andhydrophobicpolyimidenanofiber/MXenecompositeaerogelforwearablepiezoresistivesensorandoil/waterseparationapplications.Adv. Funct. Mater.2021,31,2008006−2008017..

Mai,A.T.M.;Thakur,A.;Ton,N.N.T.;Nguyen,T.N.;Kaneko,T.;Taniike,T.Photodegradationofasemi-aromaticbio-derivedpolyimide.Polym. Degrad. Stabil.2021,184,109472−109478..

Chang,Y.S.;Kumari,P.;Munro,C.J.;Szekely,G.;Vega,L.F.;Nunes,S.;Dumee,L.F.Plasticizationmitigationstrategiesforgasandliquidfiltrationmembranes-areview.J. Membr. Sci.2023,666,121125−121150..

Zhang,R.F.;Liu,C.;Hsu,P.C.;Zhang,C.F.;Liu,N.;Zhang,J.S.;Lee,H.R.;Lu,Y.Y.;Qiu,Y.C.;Chu,S.;Cui,Y.Nanofiberairfilterswithhigh-temperaturestabilityforefficientPM2.5removalfromthepollutionsources.Nano Lett.2016,16,3642−3649..

Xie,F.;Wang,Y.F.;Zhuo,L.H.;Ning,D.D.;Yan,N.;Li,J.Y.;Chen,S.S.;Lu,Z.Q.Multiplehydrogenbondingself-assemblytailoredelectrospunpolyimidehybridfilterforefficientairpollutioncontrol.J. Hazard. Mater.2021,412,125260−125260..

Wang,L.;Cui,L.;Liu,Y.;Riedel,J.;Qian,X.;Liu,Y.Electrospunpolyimidenanofiber-coatedpolyimidenonwovenfabricforhotgasfiltration.Adsorpt. Sci. Technol.2018,36,1734−1743..

Gholami,F.;Tomas,M.;Gholami,Z.;Vakili,M.Technologiesforthenitrogenoxidesreductionfromfluegas:areview.Sci. Total Environ.2020,714,136712−136737..

Honma,T.;Sato,T.HydrolysiskineticsofPMDA/ODApolyimideformonomerrecoveryusingsodiumhydroxideinhigh-temperaturewater.J. Supercrit. Fluids2020,166,105037..

Pawlowski,W.P.;Coolbaugh,D.D.;Johnson,C.J.Etchratestudiesofbase-catalyzed-hydrolysisofpolyimidefilm.J. Appl. Polym. Sci.1991,43,1379−1383..

Fang,D.;Yan,B.;Agarwal,S.;Xu,W.H.;Zhang,Q.;He,S.J.;Hou,H.Q.Electrospunpoly[poly(2,5-benzophenone)]bibenzopyrrolone/polyimidenanofibermembraneforhigh-temperatureandstrong-alkalisupercapacitor.J. Mater. Sci.2021,56,9344−9355..

Yang,K.;Ni,H.Z.;Shui,T.E.;Chi,X.Y.;Chen,W.B.;Liu,Q.;Xu,J.M.;Wang,Z.Highconductivityandalkali-resistantstabilityofimidazolesidechaincrosslinkedanionexchangemembrane.Polymer2020,211,123085−123084..

Tashvigh,A.A.;Feng,Y.;Weber,M.;Maletzko,C.;Chung,T.S.110thAnniversary:selectionofcross-linkersandcross-linkingproceduresforthefabricationofsolvent-resistantnanofiltrationmembranes:areview.Ind. Eng. Chem. Res2019,58,10678−10691..

SeeToh,Y.H.;Lim,F.W.;Livingston,A.G.Polymericmembranesfornanofiltrationinpolaraproticsolvents.J. Membr. Sci.2007,301,3−10..

Park,H.B.;Lee,C.H.;Sohn,J.Y.;Lee,Y.M.;Freeman,B.D.;Kim,H.J.Effectofcrosslinkedchainlengthinsulfonatedpolyimidemembranesonwatersorption,protonconduction,andmethanolpermeationproperties.J. Membr. Sci.2006,285,432−443..

Soroko,I.;Bhole,Y.;Livingston,A.G.Environmentallyfriendlyrouteforthepreparationofsolventresistantpolyimidenanofiltrationmembranes.Green Chem.2011,13,162−168..

Byun,S.;Lee,S.H.;Song,D.;Ryou,M.H.;Lee,Y.M.;Park,W.H.Acrosslinkednonwovenseparatorbasedonanorganosolublepolyimideforhigh-performancelithium-ionbatteries.J. Ind. Eng. Chem.2019,72,390−399..

Kratochvil,A.M.;Koros,W.J.Decarboxylation-inducedcross-linkingofapolyimideforenhancedCO2plasticizationresistance.Macromolecules2008,41,7920−7927..

Qiu,W.;Chen,C.C.;Xu,L.;Cui,L.;Paul,D.R.;Koros,W.J.Sub-Tgcross-linkingofapolyimidemembraneforenhancedCO2plasticizationresistancefornaturalgasseparation.Macromolecules2011,44,6046−6056..

Zhang,C.;Li,P.;Cao,B.DecarboxylationcrosslinkingofpolyimideswithhighCO2/CH4separationperformanceandplasticizationresistance.J. Membr. Sci.2017,528,206−216..

Du,N.;Dal-Cin,M.M.;Robertson,G.P.;Guiver,M.D.Decarboxylation-inducedcross-linkingofpolymersofintrinsicmicroporosity(PIMs)formembranegasseparation.Macromolecules2012,45,5134−5139..

Cheng,Z.;Liu,Y.;Meng,C.B.;Dai,Y.;Luo,L.B.;Liu,X.Y.Constructingaweavingstructureforaramidfiberbycarbonnanotube-basednetworktosimultaneouslyimprovecompositesinterfacialpropertiesandcompressiveproperties.Compos. Sci. Technol.2019,182,107721−107729..

Zheng,S.S.;Dong,J.;Zhou,X.Y.;Li,X.T.;Zhao,X.;Zhang,Q.H.High-strengthandhigh-moduluspolyimidefiberswithexcellentUVandozoneresistance.ACS Appl. Polym.2022,4,4558−4567..

Xu,Y.;Zhang,Q.Two-dimensionalFouriertransforminfrared(FT-IR)correlationspectroscopystudyoftheimidizationreactionfrompolyamicacidtopolyimide.Appl. Spectrosc.2014,68,657−662..

Xu,S.;Wang,Y.Novelthermallycross-linkedpolyimidemembranesforethanoldehydrationviapervaporation.J. Membr. Sci.2015,496,142−155..

Xu,Y.M.;Le,N.L.;Zuo,J.;Chung,T.S.Aromaticpolyimideandcrosslinkedthermallyrearrangedpoly(benzoxazole-co-imide)membranesforisopropanoldehydrationviapervaporation.J. Membr. Sci.2016,499,317−325..

Fang,Y.T.;Gan,F.;Dong,J.;Zhao,X.;Li,X.T.;Zhang,Q.H.Preparationofhigh-performancepolyimidefiberswithwhollyrigidstructurescontainingbenzobisoxazolemoieties.Chinese J. Polym. Sci.2022,40,280−289..

Wang,J.;Zhang,H.;Miao,Y.;Qiao,L.;Wang,X.;Wang,F.UV-curablewaterbornepolyurethanefromCO2-polyolwithhighhydrolysisresistance.Polymer2016,100,219−226..

Fu,H.;Gong,L.B.;Gong,S.L.Anewapproachutilizingaza-michaeladditionforhydrolysis-resistancenon-ionicwaterbornepolyester.Polymers2022,14,2655−2671..

Yu,W.;Ko,T.M.Surfacecharacterizationsofpotassium-hydroxide-modifiedUpilex-S®polyimideatanelevatedtemperature.Eur. Polym. J.2001,37,1791−1799..

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Thermally Conductive Polyimide/Boron Nitride Composite Films with Improved Interfacial Compatibility Based on Modified Fillers by Polyimide Brushes

A Facile Strategy for Intrinsic Low-D_k and Low-D_f Polyimides Enabled by Spirobifluorene Groups