Poly(lactic acid) Nanocomposites with Improved Flame Retardancy and Impact Strength by Combining of Phosphinates and Organoclay

Ye Lei; Ren Jie; Cai Shen-yang; Wang Zhi-gang; Li Jian-bo

doi:10.1007/s10118-016-1799-z

Your Location：

Home >

Browse articles >

Poly(lactic acid) Nanocomposites with Improved Flame Retardancy and Impact Strength by Combining of Phosphinates and Organoclay

Papers | Updated：2022-02-21

- Poly(lactic acid) Nanocomposites with Improved Flame Retardancy and Impact Strength by Combining of Phosphinates and Organoclay
- Poly(lactic acid) Nanocomposites with Improved Flame Retardancy and Impact Strength by Combining of Phosphinates and Organoclay
- 高分子科学（英文版） 2016年34卷第6期页码：785-796
- Affiliations：
  
  a.Key Laboratory of Advanced Civil Engineering Materials of Ministry of Education, School of Materials Science and Engineering, Tongji University, Shanghai 200092, China
  b.Institute of Nano and Bio-Polymeric Materials, School of Material Science and Engineering, Tongji University, Shanghai 201804, China
- Author bio：
  
  Jie Ren (任杰), E-mail: renjie6598@163.com
  Jian-bo Li (李建波), E-mail: lijianbo@tongji.edu.cn
- Funds：
  
  the National Natural Science Foundation of China;the Shanghai Automotive Industry Science and Technology Development Foundation
- DOI：10.1007/s10118-016-1799-z
  中图分类号：
- 收稿：2015-12-27，
  
  修回：2016-;2-16，
  
  纸质出版：2016-06
- Accepted：
Scan QR Code
Ye Lei, Ren Jie, Cai Shen-yang, 等. Poly(lactic acid) Nanocomposites with Improved Flame Retardancy and Impact Strength by Combining of Phosphinates and Organoclay[J]. 高分子科学（英文版）, 2016,34(6):785-796.

Ye Lei, Ren Jie, Cai Shen-yang, et al. Poly(lactic acid) Nanocomposites with Improved Flame Retardancy and Impact Strength by Combining of Phosphinates and Organoclay[J]. 2016, 34(6): 785-796.
Ye Lei, Ren Jie, Cai Shen-yang, 等. Poly(lactic acid) Nanocomposites with Improved Flame Retardancy and Impact Strength by Combining of Phosphinates and Organoclay[J]. 高分子科学（英文版）, 2016,34(6):785-796. DOI： 10.1007/s10118-016-1799-z.

Ye Lei, Ren Jie, Cai Shen-yang, et al. Poly(lactic acid) Nanocomposites with Improved Flame Retardancy and Impact Strength by Combining of Phosphinates and Organoclay[J]. 2016, 34(6): 785-796. DOI： 10.1007/s10118-016-1799-z.

摘要

Abstract

To minimize the loading level of the char-forming phosphorus based flame retardants in the poly(lactic acid) (PLA) with reduced flammability

we have developed the flame-retarded PLA nanocomposites by melt blending method incorporating organically modified montmorillonite (OMMT) and aluminium diethylphosphinate (AlPi) additives. The influence of AlPi and OMMT on flame retardancy and thermal stability of PLA was thoroughly investigated by means of the limiting oxygen index (LOI)

UL94 test

cone calorimeter

X-ray diffraction (XRD)

thermogravimetric analysis and scanning electronic microscopy (SEM). The experimental results show that the PLA/AlPi/OMMT system has excellent fire retardancy. The LOI value increases from 19% for pristine PLA to 28% for the flame-retarded PLA. Cone calorimeter analysis of the PLA/AlPi/OMMT exhibits a reduction in the peak heat release rate values by 26.2%. Thermogravimetric analysis and SEM of cone calorimeter residues indicate that OMMT significantly enhances the thermal stability

promotes char-forming and suppresses the melt dripping. The research of this study implies that the combining of the flame retardant and organoclay results in a synergistic effect. In addition

the flame-retarded PLA nanocomposite also exhibits notable increase in the impact strength and the elongation at break.

关键词

Keywords

references

K. Fukushima, , M. Murariu, , G Camino, , P. Dubois, . Polym. Degrad. Stab. , 2010 . 95 ( 6 ): 1063 .

J. Ren, , Z.H. Zhang, , Y. Feng, , J.B Li, , W.Z. Yuan, . J. Appl. Polym. Sci. , 2010 . 118 ( 5 ): 2650 .

Ren, J., "Biodegradable Poly(lactic acid): Synthesis, Modification, Processing and Applications", Springer Berlin Heidelberg, Berlin, 2010, p.54

P. Ding, , B. Kang, , J. Zhang, , J.W. Yang, , N. Song, , S.F Tang, , L.Y. Shi, . J. Colloid Interf. Sci. , 2015 . 440 46 .

D.M. Fox, , M. Novy, , K. Brown, , M. Zammarano, , R.H. Jr. Harris, , M. Murariu, , E.D. McCarthy, , J.E Seppala, , J.W. Gilman, . Polym. Degrad. Stab. , 2014 . 106 54 .

Q.F Wang, , W.F. Shi, . Polym. Degrad. Stab. , 2006 . 91 ( 6 ): 1289 .

H.J. Lin, , L.J. Han, , X.M. Wang, , Y.J Bian, , Y.S. Li, . Polym. Adv. Technol. , 2013 . 24 ( 6 ): 576 .

J. Deng, , S.W Zhu, , W.F. Shi, . J. Appl. Polym. Sci. , 2004 . 94 ( 5 ): 2065 .

X. Chen, , J Zhuo, , C. Jiao, . Polym. Degrad. Stab. , 2012 . 97 ( 11 ): 2143 .

X. Chen, , C. Jiao, , S Li, , J. Sun, . J. Polym. Res. , 2011 . 18 ( 6 ): 2229 .

D. Chen, , J Li, , J. Ren, . Polym. Int. , 2011 . 60 ( 4 ): 599 .

G. Tang, , X. Wang, , R. Zhang, , B.B. Wang, , N.N. Hong, , Y. Hu, , L Song, , X.L. Gong, . Ind. Eng. Chem. Res. , 2013 . 52 ( 22 ): 7362 .

G. Tang, , X. Wang, , W.Y. Xing, , P. Zhang, , B.B. Wang, , N.N. Hong, , W. Yang, , Y Hu, , L. Song, . Ind. Eng. Chem. Res. , 2012 . 51 ( 37 ): 12009 .

G. Tang, , X.J. Huang, , H.C. Ding, , X. Wang, , S.D. Jiang, , K.Q. Zhou, , B.B. Wang, , W Yang, , Y. Hu, . RSC Advances , 2014 . 4 ( 18 ): 8985 .

A. Lorenzetti, , S. Besco, , D. Hrelja, , M. Roso, , E. Gallo, , B Schartel, , M. Modesti, . Polym. Degrad. Stab. , 2013 . 98 ( 11 ): 2366 .

J.B. Dahiya, , N Kumar, , H. Bockhorn, . Fire. Mater. , 2014 . 38 ( 1 ): 1 .

E. Gallo, , U. Braun, , B. Schartel, , P Russo, , D. Acierno, . Polym. Degrad. Stab. , 2009 . 94 ( 8 ): 1245 .

U Braun, , B. Schartel, . Macromol. Mater. Eng. , 2008 . 293 ( 3 ): 206 .

A Ramani, , A.E. Dahoe, . Polym. Degrad. Stab. , 2014 . 105 1 .

S. Bourbigot, , F. Samyn, , T Turf, , S. Duquesne, . Polym. Degrad. Stab. , 2010 . 95 ( 3 ): 320 .

F Samyn, , S. Bourbigot, . Polym. Degrad. Stab. , 2012 . 97 ( 11 ): 2217 .

A. Vannier, , S. Duquesne, , S Bourbigot, , J. Alongi, . Thermochim. Acta , 2009 . 495 ( 1-2 ): 155 .

J. Alongi, . Fiber. Polym. , 2011 . 12 ( 2 ): 166 .

T.D Hapuarachchi, , T. Peijs, . Compos. Part. A-Appl. S. , 2010 . 41 ( 8 ): 954 .

M.F. Chiang, , M.Z Chu, , T.M. Wu, . Polym. Degrad. Stab. , 2011 . 96 ( 1 ): 60 .

P. Wei, , S Bocchini, , G. Camino, . Eur. Polym. J. , 2013 . 49 ( 4 ): 932 .

M. Murariu, , A.L. Dechief, , L. Bonnaud, , Y. Paint, , A. Gallos, , G. Fontaine, , S Bourbigot, , P. Dubois, . Polym. Degrad. Stab. , 2010 . 95 ( 5 ): 889 .

S. Solarski, , F. Mahjoubi, , M. Ferreira, , E. Devaux, , P. Bachelet, , S. Bourbigot, , R. Delobel, , P. Coszach, , M. Murariu, , A.D. Ferreira, , M. Alexandre, , P Degee, , P. Dubois, . J. Mater. Sci. , 2007 . 42 ( 13 ): 5105 .

K.C. Cheng, , C.B. Yu, , W.J. Guo, , S.F. Wang, . Carbo. Polym. , 2012 . 87 ( 2 ): 1119 .

X. Wang, , Y.A. Hu, , L. Song, , S.Y. Xuan, , W.Y. Xing, , Z.M Bai, , H.D. Lu, . Ind. Eng. Chem. Res , 2011 . 50 ( 2 ): 713 .

M. Zanetti, , G Camino, , R. Mulhaupt, . Polym. Degrad. Stab. , 2001 . 74 ( 3 ): 413 .

J.W. Gilman, . Appl. Clay. Sci. , 1999 . 15 ( 1-2 ): 31 .

A.B. Morgan, . Polym. Adv. Technol. , 2006 . 17 ( 4 ): 206 .

P Kiliaris, , C.D. Papaspyrides, . Prog. Polym. Sci. , 2010 . 35 ( 7 ): 902 .

A. Fina, , F Cuttica, , G. Camino, . Polym. Degrad. Stab. , 2012 . 97 ( 12 ): 2619 .

M., J. Polym. Sci. Pluta, . Part B: Polym. Phys. , 2006 . 44 ( 23 ): 3392 .

F.D. Kopinke, , M. Remmler, , K Mackenzie, , M. Moder, . Polym. Degrad. Stab. , 1996 . 53 ( 3 ): 329 .

H.L. Qin, , S.M. Zhang, , C.G. Zhao, , G.J Hu, , M.S. Yang, . Polymer , 2005 . 46 ( 19 ): 8386 .

B.M. Alexander, . Polym. Adv. Technol. , 2006 . 17 ( 10 ): 206 .

U. Braun, , H. Bahr, , H Sturm, , B. Schartel, . Polym. Adv. Technol. , 2008 . 19 ( 6 ): 680 .

U. Braun, , B. Schartel, , M.A Fichera, , C. Jaeger, . Polym. Degrad. Stab. , 2007 . 92 ( 8 ): 1528 .

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

DISPERSION OF GRAPHENE OXIDE AND ITS FLAME RETARDANCY EFFECT ON EPOXY NANOCOMPOSITES

Construction of Zinc Ion-reinforced Melamine Phosphate Flame Retardant for Synergistic Enhancement of Flame Retardancy and Energy Absorption in Ethylene-Vinyl Acetate Foams

Ingenious Engineering of Phosphorus and Nitrogen-enriched Nickel/Iron Bimetallic Phyllosilicates: Forging Multifunctional Epoxy Composites with Excellent Toughness, Self-lubrication, Wear Resistance and Flame Retardancy

Transparent UV-cured Phosphorus/Nitrogen Hybrid Coating for Simultaneously Enhancing Flame Retardancy and Surface Hardness of Polycarbonate

Manipulating Hierarchical Aggregation Structure via Film-forming Kinetics Enables Organic Photovoltaics over 20% Efficiency