Preparation of Polystyrene/Triphenyl Phosphate Composites by Suspension Polymerization and Melt Extrusion Method——A Comparative Study

Zhang Cun-wei; Yang Rong-jie; Li Xiang-mei; Yi De-qi

doi:10.1007/s10118-016-1791-7

Your Location：

Home >

Browse articles >

Preparation of Polystyrene/Triphenyl Phosphate Composites by Suspension Polymerization and Melt Extrusion Method——A Comparative Study

Papers | Updated：2022-02-21

- Preparation of Polystyrene/Triphenyl Phosphate Composites by Suspension Polymerization and Melt Extrusion Method——A Comparative Study
- Preparation of Polystyrene/Triphenyl Phosphate Composites by Suspension Polymerization and Melt Extrusion Method——A Comparative Study
- 高分子科学（英文版） 2016年34卷第6期页码：688-696
- Affiliations：
  
  a.National Engineering Research Center of Flame Retardant Materials, School of Materials, Beijing Institute of Technology, Beijing 100081, China
  b.Fire Command Department, Chinese People's Armed Police Forces Academy, Langfang 065000, China
- Author bio：
  
  Xiang-mei Li (李向梅), E-mail: bjlglxm@bit.edu.cn
- Funds：
- DOI：10.1007/s10118-016-1791-7
  中图分类号：
- 收稿：2015-11-26，
  
  修回：2016-1-28，
  
  录用：2016-2-18，
  
  纸质出版：2016-06
- Accepted：
Scan QR Code
Zhang Cun-wei, Yang Rong-jie, Li Xiang-mei, 等. Preparation of Polystyrene/Triphenyl Phosphate Composites by Suspension Polymerization and Melt Extrusion Method——A Comparative Study[J]. 高分子科学（英文版）, 2016,34(6):688-696.

Preparation of Polystyrene/Triphenyl Phosphate Composites by Suspension Polymerization and Melt Extrusion Method——A Comparative Study[J]. 2016, 34(6): 688-696.
Zhang Cun-wei, Yang Rong-jie, Li Xiang-mei, 等. Preparation of Polystyrene/Triphenyl Phosphate Composites by Suspension Polymerization and Melt Extrusion Method——A Comparative Study[J]. 高分子科学（英文版）, 2016,34(6):688-696. DOI： 10.1007/s10118-016-1791-7.

Preparation of Polystyrene/Triphenyl Phosphate Composites by Suspension Polymerization and Melt Extrusion Method——A Comparative Study[J]. 2016, 34(6): 688-696. DOI： 10.1007/s10118-016-1791-7.

摘要

Abstract

Polystyrene (PS)/triphenyl phosphate (TPP) composites were prepared by both suspension polymerization and melt extrusion

and a comparative study of the flame retardance and mechanical properties was carried out. The results showed that suspension polymerization was a better technique than melt extrusion for obtaining good dispersity of the PS/TPP composite. The TPP nanoparticles

which were approximately 50 nm in size

were homogenously and uniformly dispersed in the PS matrix by suspension polymerization in one-step. However

the PS/TPP composite was partially agglomerated

exhibiting irregularly shaped micron-scale particles as a result of melt extrusion. In contrast to the melt extrusion

the limited oxygen index (LOI) of the PS/TPP nanocomposite by suspension polymerization increased to 22.6% from 21.8%

and time to ignition (TTI) increased by 12.3%

the peak heat release rate (PHRR) decreased by 8.5%

and the total heat release (THR) decreased by 11.0%. The mechanical properties of the PS/TPP nanocomposite by suspension polymerization also increased. The tensile strength

elongation at break

and flexural strength increased by 36.4%

8.5%

and 108%

respectively.

关键词

Keywords

references

S.V Levchik, , E.D. Weil, . Polym. Int. , 2008 . 57 431 .

Q.L. Tai, , L.J. Chen, , L. Song, , S.B. Nie, , Y. Hu, , R.K.K. Yuen, . Polym. Degrad. Stab. , 2010 . 95 830 .

L. Utevski, , M. Scheinker, , P Georlette, , S. Lach, . J. Fire Sci. , 1997 . 15 375 .

L Chen, , Y.Z. Wang, . Polym. Adv. Technol. , 2010 . 21 1 .

Y.Y. Liu, , S.J. Wang, , M Xiao, , Y.Z. Meng. . Res J Chem Environ , 2007 . 11 84 .

S Bourbigot, , S. Duquesne, . J. Mater. Chem. , 2007 . 17 2283 .

K.Q. Zhou, , Q.J. Zhang, , J.J. Liu, , B. Wang, , S.H. Jiang, , Y.Q. Shi, , Y Hu, , Z. Gui, . RSC Adv. , 2014 . 4 13205 .

J.C. Liu, , Z.L. Yu, , H.B. Chang, , Y.B. Zhang, , Y.Z. Shi, , J. Luo, , B.L Pan, , C. Lu, . Polym. Degrad. Stab. , 2014 . 103 83 .

Y.W. Yan, , L. Chen, , R.K. Jian, , S Kong, , Y.Z. Wang, . Polym. Degrad. Stab. , 2012 . 97 1423 .

U Braun, , B. Schartel, . Macromol. Chem. Phys. , 2004 . 205 2185 .

Z Czégény, , M. Blazso, . J. Anal. Appl. Pyrolysis , 2008 . 81 218 .

W.G. Cui, , F Guo, , J.F. Chen, . Fire Safety J. , 2007 . 42 232 .

Y.W. Yan, , J.Q Huang, , Y.H. Guan, , K. Shang, , R.K Jian, , Y.Z. Wang, . Polym. Degrad. Stab. , 2014 . 99 35 .

B.Y. Li, , Y.P. Wang, , X.B Niu, , Z.M. Liu, . Chinese J. Polym. Sci. , 2014 . 32 ( 2 ): 123 .

B. W. Brooks, . Chem. Eng. Technol. , 2010 . 33 1737 .

K.Q. Zhou, , J.J. Liu, , Y.Q. Shi, , S.H. Jiang, , D. Wang, , Y Hu, , Z. Gui, . ACS Appl. Mater. Inter. , 2015 . 7 6070 .

M. Raheel, , K. Yao, , J. Gong, , X.C. Chen, , D.T. Liu, , Y.C. Lin, , D.M. Cui, , M Siddiq, , T. Tang, . Chinese J. Polym. Sci. , 2015 . 33 ( 2 ): 329 .

A.M. Alansi, , W.Z. Alkayali, , M.H. Al-qunaibit, , T.F Qahtan, , T.A. Saleh, . RSC Adv. , 2015 . 5 71441 .

X.L. Xie, , Q.X. Liu, , R.K.Y. Li, , X.P. Zhou, , Q.X. Zhang, , Z.Z Yu, , Y.W. Mai, . Polymer , 2004 . 45 6665 .

D.Y. Yang, , Q.X. Liu, , X.L Xie, , F.D. Zeng, . J. Therm. Anal. Calorim. , 2006 . 84 355 .

C. Liu, , Y.F. Luo, , Z.X. Jia, , S.Q. Li, , D Huang, , D.M. Jia, . Polym. Compos. , 2014 . 35 856 .

Y.Z. Bao, , Z.M Huang, , Z.X. Weng, . J. Appl. Polym. Sci. , 2006 . 102 1471 .

Z.H. Zheng, , W.J. Li, , H.M. Sun, , A.Q. Cheng, , J.T. Yan, , H.W Wang, , X.J. Cui, . Polym. Compos. , 2013 . 34 1110 .

J.T. Yan, , X.J. Miao, , Q.Y. Zhang, , X.J. Cui, , J.F Li, , H.Y. Wang, . Polym. Eng. Sci. , 2011 . 51 294 .

J.M. Hwu, , T.H. Ko, , W.T. Yang, , J.C. Lin, , G.J. Jiang, , W Xie, , W.P. Pan, . J. Appl. Polym. Sci. , 2004 . 91 101 .

W. Xie, , J.M. Hwu, , G.J. Jiang, , T.M Buthelezi, , W.P. Pan, . Polym. Eng. Sci. , 2003 . 43 214 .

W.P Wang, , C.Y. Pan, . Polymer , 2004 . 45 3987 .

K. Lee, , K. Yoon, , J. Kima, , J. Bae, , J Yang, , S. Hong, . Polym. Degrad. Stab. , 2003 . 81 173 .

Q.F Wang, , W.F. Shi, . Polym. Degrad. Stab. , 2006 . 91 1289 .

Z.G Huang, , W.F. Shi, . Eur. Polym. J. , 2006 . 42 1506 .

N. Muller, , P.C Lauterbur, , J. Goldenson, . J. Am. Chem. Soc. , 1956 . 78 3557 .

K.M Armstrong, , P. Kilian, . Eur. J. Inorg. Chem. , 2011 . 13 2138 .

Chimanowsky , J.P. Jr. , R.P.C Neto, , M.I.B. Tavares, . Polym. Degrad. Stab. , 2015 . 118 178 .

G. Sanchez-Olivares, , A. Sanchez-Solis1, , G Camino, , O. Manero, . Express Polym. Lett. , 2008 . 2 569 .

Y. Wang, , J. Jow , K Su, , J. Zhang, . J. Fire Sci. , 2012 . 30 477 .

V Babrauskas, , R.D. Peacock, . Fire Safety J. , 1992 . 18 255 .

K.Q. Zhou, , S.H. Jiang, , Y.Q. Shi, , J.J. Liu, , B. Wang, , Y Hu, , Z. Gui, . RSC Adv. , 2014 . 4 40170 .

H Ishida, , D.J. Allen, . Polymer , 1996 . 37 4487 .

S. Rimdusit, , N. Thamprasom, , N. Suppakarn, , C. Jubsilp, , T Takeichi, , S. Tiptipakorn, . J. Appl. Polym. Sci. , 2013 . 130 1074 .

N. Herrera, , A.P Mathew, , K. Oksman, . Compos. Sci. Technol. , 2015 . 106 149 .

H. Zou, , J. Sun, , X.Y. Gu, , P. Jiang, , X.S Liu, , S. Zhang, . Chinese J. Polym. Sci. , 2015 . 33 ( 4 ): 554 .

P. Russo, , D. Acierno, , R. Rosa, , C. Leonelli, , A Corradi, , A. Rizzuti, . Surf. Coat. Tech. , 2014 . 243 65 .

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

One-step Preparation of Brush-type Polystyrene (PS)-SiO2-Poly(2-hydroxyethyl methacrylate) Janus Nanoparticle to Compatibilize PS/Poly(methyl methacrylate) Blends

A Potential Alternative to Polystyrene: Ring-opening Terpolymerization of Different Epoxides with Phthalic Anhydride Using Metal-free Dual Catalysts

Structural Changes and Electrodynamic Effects in Polymers under Fast Uniaxial Compression

Substituent Effects of Pyridyl-methylene Cyclopentadienyl Rare-earth Metal Complexes on Styrene Polymerization

Molecularly Engineered Polyimide Films with Switchable Cavitation for Bidirectional Passive Thermal Regulation