The Application of Highly Soluble Amine-terminated Aromatic Polyimides with Pendent Tert-butyl Groups as a Tougher for Epoxy Resin

Qing Zhao; Xing-yi Wang; Yan-hong Hu

doi:10.1007/s10118-015-1685-0

Your Location：

Home >

Browse articles >

The Application of Highly Soluble Amine-terminated Aromatic Polyimides with Pendent Tert-butyl Groups as a Tougher for Epoxy Resin

PAPER | Updated：2021-06-21

- The Application of Highly Soluble Amine-terminated Aromatic Polyimides with Pendent Tert-butyl Groups as a Tougher for Epoxy Resin
- The Application of Highly Soluble Amine-terminated Aromatic Polyimides with Pendent Tert-butyl Groups as a Tougher for Epoxy Resin
- Chinese Journal of Polymer Science 2015年33卷第10期页码：1359-1372
- Affiliations：
  
  a.Laboratory for Advanced Materials, Research Institute of Industrial Catalysis, East China University of Science and Technology, Shanghai 200237, China
  b.Key Laboratory for Specially Functional Polymers and Related Technology of Ministry of Education, School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237, China
- Author bio：
  
  **Xing-yi Wang (王幸宜), E-mail: wangxy@ecust.edu.cn
  Yan-hong Hu (扈艳红), E-mail: huyhxy@ecust.edu.cn
- Funds：
  
  Shanghai key R&D Program(DZ1100105)
- DOI：10.1007/s10118-015-1685-0
  中图分类号：
- 收稿：2015-03-04，
  
  修回：2015-04-30，
  
  录用：2015-05-02，
  
  纸质出版：2015-10
- Accepted：
Scan QR Code
Qing Zhao, Xing-yi Wang, Yan-hong Hu. The Application of Highly Soluble Amine-terminated Aromatic Polyimides with Pendent Tert-butyl Groups as a Tougher for Epoxy Resin[J]. Chinese Journal of Polymer Science, 2015,33(10):1359-1372.

Qing Zhao, Xing-yi Wang, Yan-hong Hu. The Application of Highly Soluble Amine-terminated Aromatic Polyimides with Pendent Tert-butyl Groups as a Tougher for Epoxy Resin[J]. Chinese Journal of Polymer Science, 2015, 33(10): 1359-1372. DOI: 10.1007/s10118-015-1685-0.
Qing Zhao, Xing-yi Wang, Yan-hong Hu. The Application of Highly Soluble Amine-terminated Aromatic Polyimides with Pendent Tert-butyl Groups as a Tougher for Epoxy Resin[J]. Chinese Journal of Polymer Science, 2015,33(10):1359-1372. DOI： 10.1007/s10118-015-1685-0.

Qing Zhao, Xing-yi Wang, Yan-hong Hu. The Application of Highly Soluble Amine-terminated Aromatic Polyimides with Pendent Tert-butyl Groups as a Tougher for Epoxy Resin[J]. Chinese Journal of Polymer Science, 2015, 33(10): 1359-1372. DOI: 10.1007/s10118-015-1685-0. DOI：

摘要

Abstract

Polyimides (PIs) with various molecular weights synthesized

via

the reaction of aromatic diamine monomer containing

tert

-butyl groups with aromatic dianhydride were highly soluble in common organic solvents and some epoxy resins at room temperature. These PIs can be incorporated in the absence of organic solvent into epoxy resin E51 with the loading below 2 wt% forming EP-PI composites. No phase separation is observed by SEM on cryogenically fractured surfaces of EP-PI composites. The PI can improve mechanical properties

especially impact strength. Adding 2 wt% PI-1.5W

the impact strength reaches to 55 kJ/m

with the increase in tensile and flexural strengths by 14% and 3%

respectively. SEM analyses for the fracture surface suggest that PI reduces the crosslink density

improves the plasticity of epoxy resin and changes the mode of fracture from fragile to ductile. Moreover

the glass transition temperature of EP-PI composites was found to increase to a significant extent.

关键词

Keywords

references

浏览量

503

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Soluble Polyimide-reinforced TGDDM and DGEBA Epoxy Composites

Fluorinated Polyimide/POSS Hybrid Polymers with High Solubility and Low Dielectric Constant

Improvements of Hydrophobicity and Toughness of Epoxy Coatings Modified with Hydroxyl-terminated Fluororubber

Molecularly Engineered Polyimide Films with Switchable Cavitation for Bidirectional Passive Thermal Regulation

High-performance Polyimide Cuff Tube with Tunable Mechanics and Long-term Biocompatibility for Microvascular Anastomosis