Thermal, Mechanical and Rheological Properties of Biodegradable Poly(propylene carbonate) and Poly(butylene carbonate) Blends

Dan-dan Wu; Wu Li; Yan Zhao; Yun-jiao Deng; Hui-liang Zhang; Hui-xuan Zhang; Li-song Dong

doi:10.1007/s10118-015-1597-z

Your Location：

Home >

Browse articles >

Thermal, Mechanical and Rheological Properties of Biodegradable Poly(propylene carbonate) and Poly(butylene carbonate) Blends

PAPER | Updated：2021-06-21

- Thermal, Mechanical and Rheological Properties of Biodegradable Poly(propylene carbonate) and Poly(butylene carbonate) Blends
- Thermal, Mechanical and Rheological Properties of Biodegradable Poly(propylene carbonate) and Poly(butylene carbonate) Blends
- Chinese Journal of Polymer Science 2015年33卷第3期页码：444-455
- Affiliations：
  
  a.Changchun University of Technology, Changchun 130012, China
  b.Laboratory of Polymer Ecomaterials, Chinese Academy of Sciences, Changchun Institute of Applied Chemistry, Changchun 130022, China
- Author bio：
  
  **Hui-liang Zhang (张会良), E-mail: hlzhang@ciac.jl.cn
- Funds：
  
  Science & Technology Bureau of Jilin Province of China(20126023);National High Technology Research and Development Program of China (863 Program)(2012AA062904);National Natural Science Foundation of China(51021003)
- DOI：10.1007/s10118-015-1597-z
  中图分类号：
- 收稿：2014-06-04，
  
  修回：2014-06-27，
  
  录用：2014-07-29，
  
  纸质出版：2015-03
- Accepted：
Scan QR Code
Dan-dan Wu, Wu Li, Yan Zhao, 等. Thermal, Mechanical and Rheological Properties of Biodegradable Poly(propylene carbonate) and Poly(butylene carbonate) Blends[J]. Chinese Journal of Polymer Science, 2015,33(3):444-455.

Dan-dan Wu, Wu Li, Yan Zhao, et al. Thermal, Mechanical and Rheological Properties of Biodegradable Poly(propylene carbonate) and Poly(butylene carbonate) Blends[J]. Chinese Journal of Polymer Science, 2015, 33(3): 444-455.
Dan-dan Wu, Wu Li, Yan Zhao, 等. Thermal, Mechanical and Rheological Properties of Biodegradable Poly(propylene carbonate) and Poly(butylene carbonate) Blends[J]. Chinese Journal of Polymer Science, 2015,33(3):444-455. DOI： 10.1007/s10118-015-1597-z.

Dan-dan Wu, Wu Li, Yan Zhao, et al. Thermal, Mechanical and Rheological Properties of Biodegradable Poly(propylene carbonate) and Poly(butylene carbonate) Blends[J]. Chinese Journal of Polymer Science, 2015, 33(3): 444-455. DOI： 10.1007/s10118-015-1597-z.

摘要

Abstract

Poly(propylene carbonate) (PPC) was melt blended in a batch mixer with poly(butylene carbonate) (PBC) in an effort to improve the toughness of the PPC without compromising its biodegradability and biocompatibility. DMA results showed that the PPC/PBC blends were an immiscible two-phase system. With the increase in PBC content

the PPC/PBC blends showed decreased tensile strength

however

the elongation at break was increased to 230% for the 50/50 PPC/PBC blend. From the tensile strength experiments

the Pukanszky model gave credit to the modest interfacial adhesion between PPC and PBC

although PPC/PBC was immscible. The impact strength increased significantly which indicated the toughening effects of the PBC on PPC. SEM examination showed that cavitation and shear yielding were the major toughening mechanisms in the blends subjected the impact tests. TGA measurements showed that the thermal stability of PPC decreased with the incorporation of PBC. Rheological investigation demonstrated that the addition of PBC reduced the value of storage modulus

loss modulus and complex viscosity of the PPC/PBC blends to some extent. Moreover

the addition of PBC was found to increase the processability of PPC in extrusion. The introduction of PBC provided an efficient and novel toughened method to extend the application area of PPC.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Thermal, Mechanical and Rheological Properties of Eco-friendly Poly(propylene carbonate)/Poly(1,2-propylene succinate) Blends

Effects of Different Nucleating Agents, Annealing and Pre-stretching Process on the Crystallinity and Mechanical Properties of Poly(butylene carbonate)

Synthesis and Properties of Poly(ethylene succinate)-b-poly(butylene carbonate) Multiblock Copolymers

Unidirectional Pre-stretching and Isothermal Annealing Reinforced Poly(butylene carbonate) Sheets at Room Temperature

Durable Anti-fogging and Abrasion-resistant Coatings Based on Polyoxometalates-Hydrophilic Resin Composites with Enhanced Cohesion and Adhesion