Effect of Functionalized Magnetite Nanoparticles and Diaminoxanthone on the Curing, Thermal Degradation Kinetic and Corrosion Property of Diglycidyl Ether of Bisphenol A-Based Epoxy Resin

Moslem Mansour Lakouraj; Ghasem Rahpaima; Ehsan Nazarzadeh Zare

doi:10.1007/s10118-014-1535-5

Your Location：

Home >

Browse articles >

Effect of Functionalized Magnetite Nanoparticles and Diaminoxanthone on the Curing, Thermal Degradation Kinetic and Corrosion Property of Diglycidyl Ether of Bisphenol A-Based Epoxy Resin

Updated：2021-06-21

- Effect of Functionalized Magnetite Nanoparticles and Diaminoxanthone on the Curing, Thermal Degradation Kinetic and Corrosion Property of Diglycidyl Ether of Bisphenol A-Based Epoxy Resin
- Effect of Functionalized Magnetite Nanoparticles and Diaminoxanthone on the Curing, Thermal Degradation Kinetic and Corrosion Property of Diglycidyl Ether of Bisphenol A-Based Epoxy Resin
- Chinese Journal of Polymer Science 2014年32卷第11期页码：1489-1499
- Affiliations：
  
  Department of Polymer Chemistry, Faculty of Chemistry, University of Mazandaran, Babolsar, Iran
- Author bio：
  
  *Moslem Mansour Lakouraj, E-mail: lakouraj@umz.ac.ir
- Funds：
- DOI：10.1007/s10118-014-1535-5
  中图分类号：
- 收稿：2014-01-09，
  
  修回：2014-02-19，
  
  录用：2014-02-27，
  
  纸质出版：2014-11
- Accepted：
Scan QR Code
Moslem Mansour Lakouraj, Ghasem Rahpaima, Ehsan Nazarzadeh Zare. Effect of Functionalized Magnetite Nanoparticles and Diaminoxanthone on the Curing, Thermal Degradation Kinetic and Corrosion Property of Diglycidyl Ether of Bisphenol A-Based Epoxy Resin[J]. Chinese Journal of Polymer Science, 2014,32(11):1489-1499.

Moslem Mansour Lakouraj, Ghasem Rahpaima, Ehsan Nazarzadeh Zare. Effect of Functionalized Magnetite Nanoparticles and Diaminoxanthone on the Curing, Thermal Degradation Kinetic and Corrosion Property of Diglycidyl Ether of Bisphenol A-Based Epoxy Resin[J]. Chinese Journal of Polymer Science, 2014, 32(11): 1489-1499.
Moslem Mansour Lakouraj, Ghasem Rahpaima, Ehsan Nazarzadeh Zare. Effect of Functionalized Magnetite Nanoparticles and Diaminoxanthone on the Curing, Thermal Degradation Kinetic and Corrosion Property of Diglycidyl Ether of Bisphenol A-Based Epoxy Resin[J]. Chinese Journal of Polymer Science, 2014,32(11):1489-1499. DOI： 10.1007/s10118-014-1535-5.

Moslem Mansour Lakouraj, Ghasem Rahpaima, Ehsan Nazarzadeh Zare. Effect of Functionalized Magnetite Nanoparticles and Diaminoxanthone on the Curing, Thermal Degradation Kinetic and Corrosion Property of Diglycidyl Ether of Bisphenol A-Based Epoxy Resin[J]. Chinese Journal of Polymer Science, 2014, 32(11): 1489-1499. DOI： 10.1007/s10118-014-1535-5.

摘要

Abstract

To prepare a high-performance epoxy resin with excellent thermal

chemical and corrosion stability

diaminoxanthone (DAX) was used to cure diglycidylether of bisphenol-A (DGEBA)-based epoxy resin and blend of DGEBA with functionalized Fe

nanoparticles. Kinetic parameters of curing and thermal degradation of epoxy resin systems were estimated by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA)

respectively. The 10% weight loss temperature has been increased from 340 ℃ to 366 ℃ and there was an increase in the char yield from 32.6% to 45.3% for the above systems. The corrosion performance of epoxy coated carbon steel was examined by potentiodynamic polarization

along with immersion test in 1.0 mol/L HCl solution. The results showed that epoxy resins cured with DAX had low tendency to corrosion. In addition

the cured epoxy resin containing 10% Fe

had higher anticorrosion activity than bare DGEBA system. The results showed that functionalized Fe

nanoparticles enhanced char formation and improved the thermal stability as well as anticorrosion activity of the resin.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Improvements of Hydrophobicity and Toughness of Epoxy Coatings Modified with Hydroxyl-terminated Fluororubber

In situ Loaded Nanoscale Red Phosphorus on Mesoporous Silica for Simultaneously Improved Flame Retardancy and Toughness of Epoxy Composites

Application of Polysulfone Cardo Copolymer in Epoxy Resin Binders for the Production of Carbon Fiber Reinforced Plastics

Enhancing Processability of Phenylethynyl-terminated Imide Oligomers and Properties of Cured Polyimides via ―CF3 Incorporation

Tunable Circularly Polarized Luminescence of Helical Poly(phenylacetylene)s via Side-chain-to-Backbone Förster Resonance Energy Transfer