Solution Blowing of Poly(dimethylsiloxane)/Nylon 6 Nanofiber Mats for Protective Applications

Lei Shi; Xu-pin Zhuang; Bo-wen Cheng; Xiao-xiao Tao; Wei-min Kang

doi:10.1007/s10118-014-1452-7

Your Location：

Home >

Browse articles >

Solution Blowing of Poly(dimethylsiloxane)/Nylon 6 Nanofiber Mats for Protective Applications

Updated：2021-06-21

- Solution Blowing of Poly(dimethylsiloxane)/Nylon 6 Nanofiber Mats for Protective Applications
- Solution Blowing of Poly(dimethylsiloxane)/Nylon 6 Nanofiber Mats for Protective Applications
- Chinese Journal of Polymer Science 2014年32卷第6期页码：786-792
- Affiliations：
  
  a.School of Textiles, Tianjin Polytechnic University, Tianjin 300387, China
  b.Key Laboratory of Advanced Textile Composite Materials of Ministry of Education, Tianjin Polytechnic University, Tianjin 300387, China
- Author bio：
  
  **Bo-wen Cheng (程博闻), E-mail: bowen15@tjpu.edu.cn
- Funds：
  
  National Natural Science Foundation of China(51103104;51173131);ianjin Natural Science Foundation(13JCZDJC32600)
- DOI：10.1007/s10118-014-1452-7
  中图分类号：
- 收稿：2013-09-25，
  
  修回：2013-11-26，
  
  录用：2013-12-11，
  
  纸质出版：2014-06
- Accepted：
Scan QR Code
Lei Shi, Xu-pin Zhuang, Bo-wen Cheng, 等. Solution Blowing of Poly(dimethylsiloxane)/Nylon 6 Nanofiber Mats for Protective Applications[J]. Chinese Journal of Polymer Science, 2014,32(6):786-792.

Lei Shi, Xu-pin Zhuang, Bo-wen Cheng, et al. Solution Blowing of Poly(dimethylsiloxane)/Nylon 6 Nanofiber Mats for Protective Applications[J]. Chinese Journal of Polymer Science, 2014, 32(6): 786-792.
Lei Shi, Xu-pin Zhuang, Bo-wen Cheng, 等. Solution Blowing of Poly(dimethylsiloxane)/Nylon 6 Nanofiber Mats for Protective Applications[J]. Chinese Journal of Polymer Science, 2014,32(6):786-792. DOI： 10.1007/s10118-014-1452-7.

Lei Shi, Xu-pin Zhuang, Bo-wen Cheng, et al. Solution Blowing of Poly(dimethylsiloxane)/Nylon 6 Nanofiber Mats for Protective Applications[J]. Chinese Journal of Polymer Science, 2014, 32(6): 786-792. DOI： 10.1007/s10118-014-1452-7.

摘要

Abstract

A new strategy was developed to fabricate superhydrophobic nylon 6 nanofibers

in which the blend solutions of poly(dimethylsiloxane) (PDMS) prepolymer and nylon 6 was spun using an innovative solution blowing process

and then the PDMS prepolymer contianning nanofibers were cured to obtain PDMS/nylon 6 nanofiber mats. Morphology

surface composition

non-wetting property and protective performance were investigated. The results showed that the addition of PDMS prepolymer improved the spinnability of the spinning solutions

and the PDMS/nylon 6 nanofibers had smooth surfaces and diameters from 100 nm to 350 nm. The presence of PDMS effectively enhanced the hydrophobicity of the nanofiber mats

showing water contact angles of 132° to 161° for PDMS contents of 1 wt% to 3 wt%. The PDMS/nylon 6 mats also possessed excellent protective and transport properties. The results indicated the potential application of the novel nanofiber mats in protective clothing.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Improvements of Hydrophobicity and Toughness of Epoxy Coatings Modified with Hydroxyl-terminated Fluororubber

Development of Organic-Inorganic High Thermal Performance Composites Reinforced with Nanofibers for 3D Printing

Preparation of Polypropylene Nanofibers as a Function of the Thermal Exposure Time of the Polymer in a Melt Electrospinning/Melt Blown Hybrid System

Molecularly Engineered Polyimide Films with Switchable Cavitation for Bidirectional Passive Thermal Regulation

Topology-regulated Co-assembly of Single Chain Polymer Nanoparticles and Block Copolymers into Hierarchical Micelle@Vesicle Composite Structures