Microstructure Characterization of Short-chain Branching Polyethylene with Differential Scanning Calorimetry and Successive Self-nucleation/Annealing Thermal Fractionation

Yan-hu Xue; Yan-hui Wang; Yan-di Fan; He-ran Yang; Tao Tang; Shu-qin Bo; Xiang-ling Ji

doi:10.1007/s10118-014-1444-7

Your Location：

Home >

Browse articles >

Microstructure Characterization of Short-chain Branching Polyethylene with Differential Scanning Calorimetry and Successive Self-nucleation/Annealing Thermal Fractionation

Updated：2021-06-21

- Microstructure Characterization of Short-chain Branching Polyethylene with Differential Scanning Calorimetry and Successive Self-nucleation/Annealing Thermal Fractionation
- Microstructure Characterization of Short-chain Branching Polyethylene with Differential Scanning Calorimetry and Successive Selfnucleation/Annealing Thermal Fractionation
- Chinese Journal of Polymer Science 2014年32卷第6期页码：751-757
- Affiliations：
  
  a.State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China
  b.University of Chinese Academy of Sciences, Changchun 130022, China
- Author bio：
  
  **Xiang-ling Ji (姬相玲), E-mail: xlji@ciac.ac.cn
- Funds：
  
  National Natural Science Foundation of China(20734006;50921062)
- DOI：10.1007/s10118-014-1444-7
  中图分类号：
- 收稿：2013-09-09，
  
  修回：2013-10-29，
  
  录用：2013-11-19，
  
  纸质出版：2014-06
- Accepted：
Scan QR Code
Yan-hu Xue, Yan-hui Wang, Yan-di Fan, 等. Microstructure Characterization of Short-chain Branching Polyethylene with Differential Scanning Calorimetry and Successive Self-nucleation/Annealing Thermal Fractionation[J]. Chinese Journal of Polymer Science, 2014,32(6):751-757.

Yan-hu Xue, Yan-hui Wang, Yan-di Fan, et al. Microstructure Characterization of Short-chain Branching Polyethylene with Differential Scanning Calorimetry and Successive Selfnucleation/Annealing Thermal Fractionation[J]. Chinese Journal of Polymer Science, 2014, 32(6): 751-757.
Yan-hu Xue, Yan-hui Wang, Yan-di Fan, 等. Microstructure Characterization of Short-chain Branching Polyethylene with Differential Scanning Calorimetry and Successive Self-nucleation/Annealing Thermal Fractionation[J]. Chinese Journal of Polymer Science, 2014,32(6):751-757. DOI： 10.1007/s10118-014-1444-7.

Yan-hu Xue, Yan-hui Wang, Yan-di Fan, et al. Microstructure Characterization of Short-chain Branching Polyethylene with Differential Scanning Calorimetry and Successive Selfnucleation/Annealing Thermal Fractionation[J]. Chinese Journal of Polymer Science, 2014, 32(6): 751-757. DOI： 10.1007/s10118-014-1444-7.

摘要

Abstract

A series of the copolymers of ethylene with 1-hexene (M1–M9) synthesized by metallocene catalyst Et[Ind]

ZrCl

/MAO was studied by differential scanning calorimetry and successive self-nucleation and annealing (SSA) thermal fractionation. The distribution of methylene sequence length (MSL) in the different copolymers was determined using the SSA method. The comonomer contents of samples M4 and M5 are 2.04 mol% and 2.78 mol%

respectively. Both M4 and M5 have low comonomer content and their MSL distribution profiles exhibit a monotonous increase trend with their MSL. The longest MSL of M5 is 167

and its corresponding molar percent is 43.95%

which is higher than that of M4. Moreover

the melting temperature (

) of M5 is also higher than that of M4. The comonomer contents of samples M7

and M9 are 8.73 mol%

14.18 mol% and 15.05 mol%

respectively. M7

and M9 have high comonomer contents

and their MSL distribution profiles display unimodality. M7 has a lower peak value of 33 and a narrow MSL distribution

resulting in a

lower than that of M8 and M9. The MSL and its distribution are also key points that influence the melting behavior of copolymers. Sometimes

MSL and its distribution of copolymers have a greater impact on it than the total comonomer contents

which is different from traditional views.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Microstructure Characterization of a Complex Branched Low-density Polyethylene

Upgrading Commercially Available Polyethylene to High-value Materials with Strong Mechanical Performance and Hydrophilicity by Blending with Ethylene/meta-Methoxystyrene Copolymers

Modulating Molecular Weight of Polyethylenes from Oligomer to Polymer Using Highly Thermal Stable Cationic α-Diimine Palladium Complexes

Molecularly Engineered Polyimide Films with Switchable Cavitation for Bidirectional Passive Thermal Regulation

pH-Responsive L-Cysteine-conjugated Polydopamine Nanocarriers for Controlled Release of Emamectin Benzoate against Pieris brassicae