Effect of Conductive Fillers on the Cyclic Stress-Strain and Nano-Scale Free Volume Properties of Silicone Rubber

M.H. Abd-El Salam; S. El-Gamal; M. Mohsen; D.M. Abd El-Maqsoud

doi:10.1007/s10118-014-1428-7

Your Location：

Home >

Browse articles >

Effect of Conductive Fillers on the Cyclic Stress-Strain and Nano-Scale Free Volume Properties of Silicone Rubber

PAPER | Updated：2021-06-21

- Effect of Conductive Fillers on the Cyclic Stress-Strain and Nano-Scale Free Volume Properties of Silicone Rubber
- Effect of Conductive Fillers on the Cyclic Stress-Strain and Nano-Scale Free Volume Properties of Silicone Rubber
- Chinese Journal of Polymer Science 2014年32卷第5期页码：558-567
- Affiliations：
  
  Physics Department, Faculty of Education, Ain Shams University, Cairo, Egypt
  Physics Department, Faculty of Science, Ain Shams University, Cairo, Egypt
  Physics Department, Faculty of Education, Ain Shams University, Cairo, Egypt
- Author bio：
  
  *S. El-Gamal, E-mail: samyelgamal@gmail.com
- Funds：
- DOI：10.1007/s10118-014-1428-7
  中图分类号：
- 收稿：2013-07-11，
  
  修回：2013-10-06，
  
  录用：2013-10-09，
  
  纸质出版：2014-05
- Accepted：
Scan QR Code
M.H. Abd-El Salam, S. El-Gamal, M. Mohsen, 等. Effect of Conductive Fillers on the Cyclic Stress-Strain and Nano-Scale Free Volume Properties of Silicone Rubber[J]. Chinese Journal of Polymer Science, 2014,32(5):558-567.

M.H. Abd-El Salam, S. El-Gamal, M. Mohsen, et al. Effect of Conductive Fillers on the Cyclic Stress-Strain and Nano-Scale Free Volume Properties of Silicone Rubber[J]. Chinese Journal of Polymer Science, 2014, 32(5): 558-567.
M.H. Abd-El Salam, S. El-Gamal, M. Mohsen, 等. Effect of Conductive Fillers on the Cyclic Stress-Strain and Nano-Scale Free Volume Properties of Silicone Rubber[J]. Chinese Journal of Polymer Science, 2014,32(5):558-567. DOI： 10.1007/s10118-014-1428-7.

M.H. Abd-El Salam, S. El-Gamal, M. Mohsen, et al. Effect of Conductive Fillers on the Cyclic Stress-Strain and Nano-Scale Free Volume Properties of Silicone Rubber[J]. Chinese Journal of Polymer Science, 2014, 32(5): 558-567. DOI： 10.1007/s10118-014-1428-7.

摘要

Abstract

The effect of carbon black (CB) and graphite (G) powders on the macroscopic and nano-scale free volume properties of silicone rubber based on poly(di-methylsiloxane) (PDMS) was studied through thermal and cyclic mechanical measurements

as well as with positron annihilation lifetime spectroscopy (PALS). The melting temperature of the composites (

) and the endothermic enthalpy of melting (Δ

) were estimated by differential scanning calorimetry (DSC).

and the degree of crystallinity (

) of PDMS composites were found to decrease with increasing the CB content. This can be explained due to the increase in physical cross-linking which results in a decrease in the crystallite thickness. Besides

was found to be dependent on the filler type. Cyclic stress-strain behavior of PDMS loaded with different contents of filler has been studied. Mullins ratio (

) was found to be dependent on the filler type and content. It was found that

increases with increasing the filler content due to the increase in physical cross-linking which results in a decrease in the size of free volume

as observed through a decrease of the

-Ps lifetime

measured by PALS. Moreover

the hysteresis in PDMS-CB composites was more pronounced than in PDMS-G composites. Furthermore

a correlation was established between the free volume

and the mechanical properties of PDMS composites containing different fillers. A negative correlation was observed between

and

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Positron Spectroscopy of Free Volume in Poly(vinylidene fluoride) after Helium Ions Irradiation

Janus Particle Sizing Agent for Interfacial Enhancement of Basalt Fiber/Poly(vinyl chloride) Composites

Regulation of Mechanical Properties of Conductive Polymer Composites

A Thermodynamic Perspective on Polymer Glass Formation

Pyrimidoisoindigo-based Polymers for Ambipolar Charge Transport