Synthesis, Characterization of Phosphorus Containing Diamide-diimide-tetraamines Based on L-Tryptophan Amino Acid and Their Effect on Flame Retardancy of Epoxy Resins

Seema Agrawal; Anudeep Kumar Narula

doi:10.1007/s10118-014-1392-2

Your Location：

Home >

Browse articles >

Synthesis, Characterization of Phosphorus Containing Diamide-diimide-tetraamines Based on L-Tryptophan Amino Acid and Their Effect on Flame Retardancy of Epoxy Resins

Updated：2021-06-21

- Synthesis, Characterization of Phosphorus Containing Diamide-diimide-tetraamines Based on L-Tryptophan Amino Acid and Their Effect on Flame Retardancy of Epoxy Resins
- Synthesis, Characterization of Phosphorus Containing Diamide-diimidetetraamines Based on L-Tryptophan Amino Acid and Their Effect on Flame Retardancy of Epoxy Resins
- Chinese Journal of Polymer Science 2014年32卷第2期页码：197-208
- Affiliations：
  
  GGS Indraprastha University, Sector-16C Dwarka, Delhi 110078, India
- Author bio：
  
  *Anudeep Kumar Narula, E-mail: researchchemlab58@gmail.com
- Funds：
- DOI：10.1007/s10118-014-1392-2
  中图分类号：
- 收稿：2013-04-23，
  
  修回：2013-06-26，
  
  录用：2013-07-08，
  
  纸质出版：2014-02
- Accepted：
Scan QR Code
Seema Agrawal, Anudeep Kumar Narula. Synthesis, Characterization of Phosphorus Containing Diamide-diimide-tetraamines Based on L-Tryptophan Amino Acid and Their Effect on Flame Retardancy of Epoxy Resins[J]. Chinese Journal of Polymer Science, 2014,32(2):197-208.

Seema Agrawal, Anudeep Kumar Narula. Synthesis, Characterization of Phosphorus Containing Diamide-diimidetetraamines Based on L-Tryptophan Amino Acid and Their Effect on Flame Retardancy of Epoxy Resins[J]. Chinese Journal of Polymer Science, 2014, 32(2): 197-208.
Seema Agrawal, Anudeep Kumar Narula. Synthesis, Characterization of Phosphorus Containing Diamide-diimide-tetraamines Based on L-Tryptophan Amino Acid and Their Effect on Flame Retardancy of Epoxy Resins[J]. Chinese Journal of Polymer Science, 2014,32(2):197-208. DOI： 10.1007/s10118-014-1392-2.

Seema Agrawal, Anudeep Kumar Narula. Synthesis, Characterization of Phosphorus Containing Diamide-diimidetetraamines Based on L-Tryptophan Amino Acid and Their Effect on Flame Retardancy of Epoxy Resins[J]. Chinese Journal of Polymer Science, 2014, 32(2): 197-208. DOI： 10.1007/s10118-014-1392-2.

摘要

Abstract

The curing behavior of diglycidyl ether of bisphenol-A (DGEBA) with different phosphorus containing diamidediimide- tetraamines (DADITAs) was studied by DSC. Eight DADITAs of varying structures were synthesized by reacting 1 mole of pyromellitic anhydride (PMDA)/3

3′-benzophenone tetracarboxylic dianhydride (BTDA)/1

8-naphthalene tetracarboxylic dianhydride (NTDA)/4

4′-oxydiphthalic anhydride (ODPA) with 2 mole of L-tryptophan (T) in a mixture of acetic acid and pyridine (3:2

V/V

) followed by activaton with thionyl chloride and then condensation with excess of phosphorus containing triamines tris(3-aminophenyl) phosphine (TAP) and tris(3-aminophenyl) phosphine oxide (TAPO). DADITAs obtained by reacting PMDA/BTDA/NTDA/ODPA with L-tryptophan followed by condensation with TAP/TAPO were designated as PTAP

PTAPO

BTAP

BTAPO

NTAP

NTAPO

OTAP and OTAPO respectively. The structural characterization of synthesized DADITAs was done by FTIR

H-NMR

C-NMR

P-NMR spectroscopic techniques and elemental analysis. Thermal stability of the isothermally cured epoxy was investigated using dynamic thermogravimetry analysis. The glass transition temperature (

) was highest in DGEBA cured using PTAP. All epoxy thermosets exhibited excellent flame retardancy

moderate changes in

and thermal stability. Due to presence of phosphorus in curing agents

all epoxy resin systems met the UL-94 V-0 classification and the limiting oxygen index (LOI) reached up to 38.5

probably because of the nitrogen-phosphorus synergistic effect.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Dry-spun Polyimide Fibers with Excellent Thermal Stability, Intrinsic Flame Retardancy and Ultralow Smoke Release

Construction of Zinc Ion-reinforced Melamine Phosphate Flame Retardant for Synergistic Enhancement of Flame Retardancy and Energy Absorption in Ethylene-Vinyl Acetate Foams

Ingenious Engineering of Phosphorus and Nitrogen-enriched Nickel/Iron Bimetallic Phyllosilicates: Forging Multifunctional Epoxy Composites with Excellent Toughness, Self-lubrication, Wear Resistance and Flame Retardancy

Transparent UV-cured Phosphorus/Nitrogen Hybrid Coating for Simultaneously Enhancing Flame Retardancy and Surface Hardness of Polycarbonate

Improvements of Hydrophobicity and Toughness of Epoxy Coatings Modified with Hydroxyl-terminated Fluororubber