Effect of the Shell Crosslinking Level and Core/Shell Ratio on the Morphology of Latex Particles in the Preparation of Hollow Latexes

Yi-ming Jiang; Bo-tian Li; Wei-jia Wang; Min Xu; Cheng-you Kan

doi:10.1007/s10118-014-1387-z

Your Location：

Home >

Browse articles >

Effect of the Shell Crosslinking Level and Core/Shell Ratio on the Morphology of Latex Particles in the Preparation of Hollow Latexes

Updated：2021-06-21

- Effect of the Shell Crosslinking Level and Core/Shell Ratio on the Morphology of Latex Particles in the Preparation of Hollow Latexes
- Effect of the Shell Crosslinking Level and Core/Shell Ratio on the Morphology of Latex Particles in the Preparation of Hollow Latexes
- Chinese Journal of Polymer Science 2014年32卷第2期页码：177-186
- Affiliations：
  
  Department of Chemical Engineering and Key Laboratory of Advanced Materials of Ministry of Education of China, Tsinghua University, Beijing 100084, China
- Author bio：
  
  *Cheng-you Kan (阚成友), E-mail: kancy@tsinghua.edu.cn
- Funds：
- DOI：10.1007/s10118-014-1387-z
  中图分类号：
- 收稿：2013-04-09，
  
  修回：2013-05-06，
  
  录用：2013-05-07，
  
  纸质出版：2014-02
- Accepted：
Scan QR Code
Yi-ming Jiang, Bo-tian Li, Wei-jia Wang, 等. Effect of the Shell Crosslinking Level and Core/Shell Ratio on the Morphology of Latex Particles in the Preparation of Hollow Latexes[J]. Chinese Journal of Polymer Science, 2014,32(2):177-186.

Yi-ming Jiang, Bo-tian Li, Wei-jia Wang, et al. Effect of the Shell Crosslinking Level and Core/Shell Ratio on the Morphology of Latex Particles in the Preparation of Hollow Latexes[J]. Chinese Journal of Polymer Science, 2014, 32(2): 177-186.
Yi-ming Jiang, Bo-tian Li, Wei-jia Wang, 等. Effect of the Shell Crosslinking Level and Core/Shell Ratio on the Morphology of Latex Particles in the Preparation of Hollow Latexes[J]. Chinese Journal of Polymer Science, 2014,32(2):177-186. DOI： 10.1007/s10118-014-1387-z.

Yi-ming Jiang, Bo-tian Li, Wei-jia Wang, et al. Effect of the Shell Crosslinking Level and Core/Shell Ratio on the Morphology of Latex Particles in the Preparation of Hollow Latexes[J]. Chinese Journal of Polymer Science, 2014, 32(2): 177-186. DOI： 10.1007/s10118-014-1387-z.

摘要

Abstract

Three-layer core/shell latex particles with various shell crosslinking level and shell thickness were prepared by multistep emulsion polymerization

and the hollow latex particles with different morphologies were then obtained after alkali post-treatment. Influences of divinyl benzene (DVB) content and the core/shell mass ratio on emulsion polymerization and particle morphology were investigated. Results showed that with the increase of DVB content

the percentage of total amount of —COOH on the particle surface and free in aqueous phase (P

) decreased

and the morphology of the post-treated particles underwent evolution from cracked

intact hollow to deficient swelling structure. Decreasing the core/shell mass ratio could not only make more carboxyl groups encapsulated by the shell

but also increase the shell resistance to the swelling of the core. The uniform hollow latex particles with intact morphology were obtained when the DVB content was 3.54 wt% and the core/shell mass ratio was 1/6.

关键词

Keywords

references

浏览量

461

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Effect of Monomer Feeding Mode on the Preparation of Hollow Latexes with High MAA Content in the Core Latex Preparation

Environment-friendly Emulsion Copolymerization of Chlorotrifluoroethylene and Vinyl Ethers

Photoenzymatic RAFT Emulsion Polymerization with Oxygen Tolerance

Polyphosphoester-modified Cellulose Nanocrystals for Stabilizing Pickering Emulsion Polymerization of Styrene

A Comparative Study on Emulsion Polymerization Processes of Styrene Initiated by Water-soluble and Oil-soluble Initiators