ICAR ATRP OF ACRYLONITRILE UTILIZING A MODERATE TEMPERATURE RADICAL INITIATOR

Fei-jun Zhang; Xiao-hui Liu

doi:10.1007/s10118-013-1348-y

Your Location：

Home >

Browse articles >

ICAR ATRP OF ACRYLONITRILE UTILIZING A MODERATE TEMPERATURE RADICAL INITIATOR

PAPER | Updated：2023-01-03

- ICAR ATRP OF ACRYLONITRILE UTILIZING A MODERATE TEMPERATURE RADICAL INITIATOR
- ICAR ATRP OF ACRYLONITRILE UTILIZING A MODERATE TEMPERATURE RADICAL INITIATOR
- Chinese Journal of Polymer Science 2013年31卷第12期页码：1613-1622
- Affiliations：
  
  School of Materials Science and Engineering, Key Lab of Hollow Fiber Membrane Material and Processes of Ministry of Education, Tianjin Polytechnic University, Tianjin 300387, China
- Author bio：
  
  **Xiao-hui Liu (刘晓辉), E-mail: liuxiaohui@tjpu.edu.cn
- Funds：
  
  National Natural Science Foundation of China(21074127;20804044);Key Project of Chinese Ministry of Education(212003)
- DOI：10.1007/s10118-013-1348-y
  中图分类号：
- 收稿：2012-12-18，
  
  修回：2013-01-16，
  
  录用：2013-01-21，
  
  纸质出版：2013-12
- Accepted：
Scan QR Code
Fei-jun Zhang, Xiao-hui Liu. ICAR ATRP OF ACRYLONITRILE UTILIZING A MODERATE TEMPERATURE RADICAL INITIATOR[J]. Chinese Journal of Polymer Science, 2013,31(12):1613-1622.

Fei-jun Zhang, Xiao-hui Liu. ICAR ATRP OF ACRYLONITRILE UTILIZING A MODERATE TEMPERATURE RADICAL INITIATOR[J]. Chinese Journal of Polymer Science, 2013, 31(12): 1613-1622.
Fei-jun Zhang, Xiao-hui Liu. ICAR ATRP OF ACRYLONITRILE UTILIZING A MODERATE TEMPERATURE RADICAL INITIATOR[J]. Chinese Journal of Polymer Science, 2013,31(12):1613-1622. DOI： 10.1007/s10118-013-1348-y.

Fei-jun Zhang, Xiao-hui Liu. ICAR ATRP OF ACRYLONITRILE UTILIZING A MODERATE TEMPERATURE RADICAL INITIATOR[J]. Chinese Journal of Polymer Science, 2013, 31(12): 1613-1622. DOI： 10.1007/s10118-013-1348-y.

摘要

Abstract

Initiators for continuous activator regeneration atom transfer radical polymerization (ICAR ATRP) of acrylonitrile was first conducted at various ambient temperatures (30−45 ℃). The key to success is ascribed to the usage of an appropriate low temperature radical initiator (2

2′-azobis(2

4-dimethylvaleronitrile)) and a high reactivity catalytic system (CuBr

/Me

TREN). The molar ratio of Cu catalyst to AN as low as 1:20000 was used to prepare well-defined polyacrylonitrile with controlled molecular weight and a narrow polydispersity index range of 1.08−1.30

while the monomer conversion was up to

ca.

98%. The apparent activation energy of the polymerization was calculated to be 128.45 kJ/mol

suggesting that the polymerization strongly depended on reaction temperature. The very high chain-end functionality of the resultant polymer was confirmed by

H-NMR and GPC analyses as well as chain extension reaction.

关键词

Keywords

references

浏览量

664

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Optically Active Helical Poly(phenyl isocyanide)s Bearing Achiral Benzanilide Pendants: from Controlled Synthesis to Enantioseparation Application

Polyacrylonitrile (PAN)-derived Carbon Modification of Polysilazane Composite SiCNO/C as a High-performance Anode Material for Lithium-ion Batteries

Enantiomer-selective Living Polymerization of rac-Phenyl Isocyanide Using Chiral Palladium Catalyst

Polythiophene-block-poly(phenyl isocyanide) Copolymers:One-pot Synthesis, Properties and Applications

Experimental Investigation of Graphene and TiO2 Reinforced Poly(vinyl alcohol)-based Fiber Metal Laminates