DISPERSION STABILITY AND RHEOLOGICAL BEHAVIOR OF SUSPENSIONS OF POLYSTYRENE COATED FUMED SILICA PARTICLES IN POLYSTYRENE SOLUTIONS

Xian-ze Yin; Ye-qiang Tan; Yi-hu Song; Qiang Zheng

doi:10.1007/s10118-012-1099-1

Your Location：

Home >

Browse articles >

DISPERSION STABILITY AND RHEOLOGICAL BEHAVIOR OF SUSPENSIONS OF POLYSTYRENE COATED FUMED SILICA PARTICLES IN POLYSTYRENE SOLUTIONS

Paper | Updated：2023-01-03

- DISPERSION STABILITY AND RHEOLOGICAL BEHAVIOR OF SUSPENSIONS OF POLYSTYRENE COATED FUMED SILICA PARTICLES IN POLYSTYRENE SOLUTIONS
- DISPERSION STABILITY AND RHEOLOGICAL BEHAVIOR OF SUSPENSIONS OF POLYSTYRENE COATED FUMED SILICA PARTICLES IN POLYSTYRENE SOLUTIONS
- Chinese Journal of Polymer Science 2012年30卷第1期页码：26-35
- Affiliations：
  
  a.Key Laboratory of Macromolecular Synthesis and Functionalization of Ministry of Education, Zhejiang University, Hangzhou 310027, China
  b.Department of Polymer Science and Engineering, Zhejiang University, Hangzhou 310027, China
- Author bio：
  
  **Yi-hu Song (宋义虎), E-mail: s_yh0411@zju.edu.cn
- Funds：
  
  National Natural Science Foundation of China(51073136);Fundamental Research Funds for the Central Universities of China(2010QNA4011)
- DOI：10.1007/s10118-012-1099-1
  中图分类号：
- 收稿：2011-01-18，
  
  修回：2011-03-02，
  
  录用：2011-03-28，
  
  纸质出版：2012-01
- Accepted：
Scan QR Code
Xian-ze Yin, Ye-qiang Tan, Yi-hu Song, 等. DISPERSION STABILITY AND RHEOLOGICAL BEHAVIOR OF SUSPENSIONS OF POLYSTYRENE COATED FUMED SILICA PARTICLES IN POLYSTYRENE SOLUTIONS[J]. Chinese Journal of Polymer Science, 2012,30(1):26-35.

Xian-ze Yin, Ye-qiang Tan, Yi-hu Song, et al. DISPERSION STABILITY AND RHEOLOGICAL BEHAVIOR OF SUSPENSIONS OF POLYSTYRENE COATED FUMED SILICA PARTICLES IN POLYSTYRENE SOLUTIONS[J]. Chinese Journal of Polymer Science, 2012, 30(1): 26-35.
Xian-ze Yin, Ye-qiang Tan, Yi-hu Song, 等. DISPERSION STABILITY AND RHEOLOGICAL BEHAVIOR OF SUSPENSIONS OF POLYSTYRENE COATED FUMED SILICA PARTICLES IN POLYSTYRENE SOLUTIONS[J]. Chinese Journal of Polymer Science, 2012,30(1):26-35. DOI： 10.1007/s10118-012-1099-1.

Xian-ze Yin, Ye-qiang Tan, Yi-hu Song, et al. DISPERSION STABILITY AND RHEOLOGICAL BEHAVIOR OF SUSPENSIONS OF POLYSTYRENE COATED FUMED SILICA PARTICLES IN POLYSTYRENE SOLUTIONS[J]. Chinese Journal of Polymer Science, 2012, 30(1): 26-35. DOI： 10.1007/s10118-012-1099-1.

摘要

Abstract

Polystyrene coated silica (SiO

@PS) core-shell composite particles with averaged diameter of about 290 nm were prepared by

in situ

emulsion polymerization of styrene on the surface of g-methacryloxypropyltrimethoxysilane grafted SiO

nanoparticles of 20-50 nm in diameter. Rheological behavior and dispersion stability of SiO

@PS suspension in 10 wt% PS solution were compared with suspensions of untreated SiO

and silane modified SiO

nanoparticles. Suspensions of the untreated and the silane modified SiO

exhibited obvious shear thinning. The SiO

@PS suspension exhibits shear viscosity considerably smaller than suspensions of untreated and silane modified SiO

at low shear rates. Transmission electron microscopy showed that the composite particles can uniformly and stably disperse in PS solution compared to other suspensions

implying that the PS shell can effectively enhance the particle compatibility with PS macromolecules in solution.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

One-step Preparation of Brush-type Polystyrene (PS)-SiO2-Poly(2-hydroxyethyl methacrylate) Janus Nanoparticle to Compatibilize PS/Poly(methyl methacrylate) Blends

A Potential Alternative to Polystyrene: Ring-opening Terpolymerization of Different Epoxides with Phthalic Anhydride Using Metal-free Dual Catalysts

Structural Changes and Electrodynamic Effects in Polymers under Fast Uniaxial Compression

Substituent Effects of Pyridyl-methylene Cyclopentadienyl Rare-earth Metal Complexes on Styrene Polymerization

End-group and Side-chain Dual-engineering of Selenium-fused Acceptors for 20.08% Efficiency Polymer Solar Cells with Low Energy Loss