ELECTRORHEOLOGY AND CREEP-RECOVERY BEHAVIOR OF CONDUCTING POLYTHIOPHENE/POLY(OXYMETHYLENE)-BLEND SUSPENSIONS

Ozlem Erol; H. Ibrahim Unal; Bekir Sari

doi:10.1007/s10118-012-1091-9

Your Location：

Home >

Browse articles >

ELECTRORHEOLOGY AND CREEP-RECOVERY BEHAVIOR OF CONDUCTING POLYTHIOPHENE/POLY(OXYMETHYLENE)-BLEND SUSPENSIONS

Paper | Updated：2023-01-03

- ELECTRORHEOLOGY AND CREEP-RECOVERY BEHAVIOR OF CONDUCTING POLYTHIOPHENE/POLY(OXYMETHYLENE)-BLEND SUSPENSIONS
- ELECTRORHEOLOGY AND CREEP-RECOVERY BEHAVIOR OF CONDUCTING POLYTHIOPHENE/POLY(OXYMETHYLENE)-BLEND SUSPENSIONS
- Chinese Journal of Polymer Science 2012年30卷第1期页码：16-25
- Affiliations：
  
  Smart Materials Research Lab, Chemistry Department, Gazi University, Ankara, Turkey
- Author bio：
  
  **H. Ibrahim Unal, E-mail: hiunal@gazi.edu.tr
- Funds：
  
  Turkish Scientific and Technological Research Council(107 T 711)
- DOI：10.1007/s10118-012-1091-9
  中图分类号：
- 收稿：2011-01-14，
  
  修回：2011-03-21，
  
  录用：2011-03-22，
  
  纸质出版：2012-01
- Accepted：
Scan QR Code
Ozlem Erol, H. Ibrahim Unal, Bekir Sari. ELECTRORHEOLOGY AND CREEP-RECOVERY BEHAVIOR OF CONDUCTING POLYTHIOPHENE/POLY(OXYMETHYLENE)-BLEND SUSPENSIONS[J]. Chinese Journal of Polymer Science, 2012,30(1):16-25.

Ozlem Erol, H. Ibrahim Unal, Bekir Sari. ELECTRORHEOLOGY AND CREEP-RECOVERY BEHAVIOR OF CONDUCTING POLYTHIOPHENE/POLY(OXYMETHYLENE)-BLEND SUSPENSIONS[J]. Chinese Journal of Polymer Science, 2012, 30(1): 16-25.
Ozlem Erol, H. Ibrahim Unal, Bekir Sari. ELECTRORHEOLOGY AND CREEP-RECOVERY BEHAVIOR OF CONDUCTING POLYTHIOPHENE/POLY(OXYMETHYLENE)-BLEND SUSPENSIONS[J]. Chinese Journal of Polymer Science, 2012,30(1):16-25. DOI： 10.1007/s10118-012-1091-9.

Ozlem Erol, H. Ibrahim Unal, Bekir Sari. ELECTRORHEOLOGY AND CREEP-RECOVERY BEHAVIOR OF CONDUCTING POLYTHIOPHENE/POLY(OXYMETHYLENE)-BLEND SUSPENSIONS[J]. Chinese Journal of Polymer Science, 2012, 30(1): 16-25. DOI： 10.1007/s10118-012-1091-9.

摘要

Abstract

Electrorheological properties and creep-recovery behavior of polythiophene/polyoxymethylene-blend having PT(50%)/POM(50%) composition were investigated. Particle size

conductivity and dielectric values were measured to be 24.77 μm

3.85 × 10

-5

S·m

-1

and 26.75

respectively. Sedimentation ratio was measured to be 64% at the end of 16 days. The effects of dispersed particle volume fraction

external electric field strength

shear rate

frequency and temperature on ER properties and storage modulus of PT/POM-blend/silicone oil (SO) suspensions were examined. Enhancement were observed in the electric field viscosities of the suspensions and thus they were classified as a smart material. Shear thinning non-Newtonian viscoelastic behavior was determined for PT/POM-blend/SO system. Further

time-dependent deformation was examined by creep-recovery tests and recoverable viscoelastic deformation established.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Dynamics of Poly(methyl methacrylate) in Ionic Liquids with Different Concentration and Cationic Structures

From Molecular Defect to Macroscopic Performance: Manipulating Dichroism and Mechanics in Iodine-doped Poly(vinyl alcohol) via Ethylene Incorporation

Bioinspired Zinc-doped Nano Hydroxyapatite Reinforced Poly(lactic acid) Composites for Bone Repair

Tunable Circularly Polarized Luminescence of Helical Poly(phenylacetylene)s via Side-chain-to-Backbone Förster Resonance Energy Transfer

Epoxy-functionalized Cyclohexane-based Ricinoleate Plasticizer: Synthesis, Performance Evaluation, and Plasticizing Mechanism