ALTERNATING COPOLYMERIZATION OF CYCLOHEXENE OXIDE AND CARBON DIOXIDE UNDER COBALT PORPHYRIN CATALYST

Yu-sheng Qin; Li-jie Chen; Xian-hong Wang; Xiao-jiang Zhao; Fo-song Wang

doi:10.1007/s10118-011-1073-3

Your Location：

Home >

Browse articles >

ALTERNATING COPOLYMERIZATION OF CYCLOHEXENE OXIDE AND CARBON DIOXIDE UNDER COBALT PORPHYRIN CATALYST

PAPER | Updated：2021-06-21

- ALTERNATING COPOLYMERIZATION OF CYCLOHEXENE OXIDE AND CARBON DIOXIDE UNDER COBALT PORPHYRIN CATALYST
- ALTERNATING COPOLYMERIZATION OF CYCLOHEXENE OXIDE AND CARBON DIOXIDE UNDER COBALT PORPHYRIN CATALYST
- Chinese Journal of Polymer Science 2011年29卷第5期页码：602-608
- Affiliations：
  
  Key Laboratory of Polymer Ecomaterials, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China
- Author bio：
  
  **Xian-hong Wang (王献红), E-mail: xhwang@ciac.jl.cn
- Funds：
  
  National Natural Science Foundation of China(20634040;50903084)
- DOI：10.1007/s10118-011-1073-3
  中图分类号：
- 收稿：2010-10-09，
  
  修回：2010-12-01，
  
  录用：2010-12-07，
  
  纸质出版：2011
- Accepted：
Scan QR Code
Yu-sheng Qin, Li-jie Chen, Xian-hong Wang, 等. ALTERNATING COPOLYMERIZATION OF CYCLOHEXENE OXIDE AND CARBON DIOXIDE UNDER COBALT PORPHYRIN CATALYST[J]. Chinese Journal of Polymer Science, 2011,29(5):602-608.

Yu-sheng Qin, Li-jie Chen, Xian-hong Wang, et al. ALTERNATING COPOLYMERIZATION OF CYCLOHEXENE OXIDE AND CARBON DIOXIDE UNDER COBALT PORPHYRIN CATALYST[J]. Chinese Journal of Polymer Science, 2011, 29(5): 602-608.
Yu-sheng Qin, Li-jie Chen, Xian-hong Wang, 等. ALTERNATING COPOLYMERIZATION OF CYCLOHEXENE OXIDE AND CARBON DIOXIDE UNDER COBALT PORPHYRIN CATALYST[J]. Chinese Journal of Polymer Science, 2011,29(5):602-608. DOI： 10.1007/s10118-011-1073-3.

Yu-sheng Qin, Li-jie Chen, Xian-hong Wang, et al. ALTERNATING COPOLYMERIZATION OF CYCLOHEXENE OXIDE AND CARBON DIOXIDE UNDER COBALT PORPHYRIN CATALYST[J]. Chinese Journal of Polymer Science, 2011, 29(5): 602-608. DOI： 10.1007/s10118-011-1073-3.

摘要

Abstract

Cobalt porphyrin complexes (TPPCo

III

X) (TPP = 5

20-tetraphenyl-porphyrin; X = halide) in combination with bis(triphenylphosphine) iminium chloride (PPNCl) were used for the copolymerization of cyclohexene oxide and CO

. The highest turnover frequency of 67.2 h

-1

was achieved after 13 h at 20℃

and the obtained poly(1

2-cyclohexylene carbonate) (PCHC) showed number average molecular weight (

) of 10 × 10

. Though the obtained PCHC showed atactic structure

the

-centered tetrads content reached 58.1% at CO

pressure of 1.0 MPa

and decreased to 51.9% at CO

pressure of 6.0 MPa

indicating that it was inclined to form atactic polymer at high CO

pressure.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

The Effect of Oxygen to Salen-Co Complexes for the Copolymerization of PO/CO2

HCAⅡ-inspired Catalysts for Making Carbon Dioxide-based Copolymers: The Role of Metal-hydroxide Bond

SYNTHESIS AND CHARACTERIZATION OF HIGH MOLECULAR WEIGHT POLY(1,2-PROPYLENE CARBONATE-co-1,2-CYCLOHEXYLENE CARBONATE) USING ZINC COMPLEX CATALYST

Chemoselective Ring-opening Copolymerization of CO2-based Lactones towards Functional Polyesters

Super-high Active, Homogeneous Vanadium(V) Complexes Bearing Bidentate Phenoxy-Phosphine Ligands for Diverse Olefins (Co)polymerization