POLYMERIZATION OF 1-OCTENE AND DETERMINATION OF MARK-HOUWINK CONSTANTS OF POLY(1-OCTENE)

Xin-hua Yan; Yan Shi; Lin Wang; Zhi-feng Fu

doi:10.1007/s10118-011-1069-z

Your Location：

Home >

Browse articles >

POLYMERIZATION OF 1-OCTENE AND DETERMINATION OF MARK-HOUWINK CONSTANTS OF POLY(1-OCTENE)

PAPER | Updated：2021-06-21

- POLYMERIZATION OF 1-OCTENE AND DETERMINATION OF MARK-HOUWINK CONSTANTS OF POLY(1-OCTENE)
- POLYMERIZATION OF 1-OCTENE AND DETERMINATION OF MARK-HOUWINK CONSTANTS OF POLY(1-OCTENE)
- Chinese Journal of Polymer Science 2011年29卷第5期页码：560-568
- Affiliations：
  
  a.State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology, Beijing 100029, China
  b.School of Chemistry and Biotechnology, Yunnan Nationalities University, Kunming 650031, China
- Author bio：
  
  **Zhi-feng Fu (付志峰), E-mail: fuzf@mail.buct.edu.cn
- Funds：
  
  program for new century excellent talents in Chinese universities and Beijing Municipal Education Commission
- DOI：10.1007/s10118-011-1069-z
  中图分类号：
- 收稿：2010-08-28，
  
  修回：2010-11-03，
  
  录用：2010-11-05，
  
  纸质出版：2011
- Accepted：
Scan QR Code
Xin-hua Yan, Yan Shi, Lin Wang, 等. POLYMERIZATION OF 1-OCTENE AND DETERMINATION OF MARK-HOUWINK CONSTANTS OF POLY(1-OCTENE)[J]. Chinese Journal of Polymer Science, 2011,29(5):560-568.

Xin-hua Yan, Yan Shi, Lin Wang, et al. POLYMERIZATION OF 1-OCTENE AND DETERMINATION OF MARK-HOUWINK CONSTANTS OF POLY(1-OCTENE)[J]. Chinese Journal of Polymer Science, 2011, 29(5): 560-568.
Xin-hua Yan, Yan Shi, Lin Wang, 等. POLYMERIZATION OF 1-OCTENE AND DETERMINATION OF MARK-HOUWINK CONSTANTS OF POLY(1-OCTENE)[J]. Chinese Journal of Polymer Science, 2011,29(5):560-568. DOI： 10.1007/s10118-011-1069-z.

Xin-hua Yan, Yan Shi, Lin Wang, et al. POLYMERIZATION OF 1-OCTENE AND DETERMINATION OF MARK-HOUWINK CONSTANTS OF POLY(1-OCTENE)[J]. Chinese Journal of Polymer Science, 2011, 29(5): 560-568. DOI： 10.1007/s10118-011-1069-z.

摘要

Abstract

The polymerization of 1-octene initiated by methylalumoxane (MAO)-activated Ni(II)-based-

-diimine complexes [(2

-Pr)

-DAB(An)]NiBr

was investigated. Using this catalyst

poly(1-octene)s with molecular weight between 100 × 10

and 400 × 10

and polydispersity (

) between 1.3 and 1.5 were synthesized successfully by varying reaction time at room temperature. The poly(1-octene)s were amorphous polymers and could be well soluble in tetrahydrofuran (THF). After fractional precipitation

poly(1-octene)s with narrow molecular weight distributions (

≤ 1.12) were obtained. Their weight-average molecular weights were measured by gel permeation chromatography (GPC) in conjunction with online model BI-MwA multiangle laser light scattering (MALLS)

and their intrinsic viscosities were measured by Maron’s single-point method. The

and

values in Mark-Houwink equation [

] =

in THF at 40℃ were 0.089 mL/g and 0.61 respectively.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Manipulating Hierarchical Aggregation Structure via Film-forming Kinetics Enables Organic Photovoltaics over 20% Efficiency

Upgrading Commercially Available Polyethylene to High-value Materials with Strong Mechanical Performance and Hydrophilicity by Blending with Ethylene/meta-Methoxystyrene Copolymers

Alternating Poly(ether-alt-ester)s with High Glass Transition Temperature Enabled by Rotationally Constrained Biaryl Units

Molecularly Engineered Polyimide Films with Switchable Cavitation for Bidirectional Passive Thermal Regulation

Improvements of Hydrophobicity and Toughness of Epoxy Coatings Modified with Hydroxyl-terminated Fluororubber