PREPARATION OF COMPOSITE MAGNETIC MICROSPHERES BY REACTIVE BLENDING

PAPER | Updated：2021-06-21

- PREPARATION OF COMPOSITE MAGNETIC MICROSPHERES BY REACTIVE BLENDING
- PREPARATION OF COMPOSITE MAGNETIC MICROSPHERES BY REACTIVE BLENDING
- Chinese Journal of Polymer Science 2011年29卷第5期页码：580-585
- Affiliations：
  
  Shanghai Key Laboratory of Advanced Polymeric Materials, School of Materials Science & Engineering, East China University of Science & Technology, Shanghai 200237, China
- Author bio：
  
  **Guo-zhang Wu (吴国章), E-mail: wgz@ecust.edu.cn
- Funds：
  
  National Natural Science Foundation of China(50873033;20974033)
- DOI：10.1007/s10118-011-1061-7
  中图分类号：
- 收稿：2010-09-17，
  
  修回：2010-10-27，
  
  录用：2010-11-16，
  
  纸质出版：2011
- Accepted：
Scan QR Code
Xiao-xia Cai, Guo-zhang Wu. PREPARATION OF COMPOSITE MAGNETIC MICROSPHERES BY REACTIVE BLENDING[J]. Chinese Journal of Polymer Science, 2011,29(5):580-585.

Xiao-xia Cai, Guo-zhang Wu. PREPARATION OF COMPOSITE MAGNETIC MICROSPHERES BY REACTIVE BLENDING[J]. Chinese Journal of Polymer Science, 2011, 29(5): 580-585.
Xiao-xia Cai, Guo-zhang Wu. PREPARATION OF COMPOSITE MAGNETIC MICROSPHERES BY REACTIVE BLENDING[J]. Chinese Journal of Polymer Science, 2011,29(5):580-585. DOI： 10.1007/s10118-011-1061-7.

Xiao-xia Cai, Guo-zhang Wu. PREPARATION OF COMPOSITE MAGNETIC MICROSPHERES BY REACTIVE BLENDING[J]. Chinese Journal of Polymer Science, 2011, 29(5): 580-585. DOI： 10.1007/s10118-011-1061-7.

摘要

Abstract

A novel method for preparation of polymer-based magnetic microspheres was proposed by utilizing melt reactive blending

which was based on selective location of Fe

nanoparticles in PA6 domains of polystyrene (PS)/polyamide 6 (PA6) immiscible blends. The morphology of PA6/Fe

composite magnetic microspheres was studied by scanning electronic microscopy (SEM). The composite magnetic microspheres were spherical with a diameter range of 0.5-8 μm; the diameter was sharply decreased with a very narrow distribution by adding terminal maleic anhydride functionalized polystyrenes (FPS) for reactive blending. Transmission electron microscopy (TEM) and thermogravimetry analysis (TGA) results showed that most of Fe

was located in the PA6 microspheres. Magnetization data revealed the magnetite content of PA6/Fe

microspheres was about 32 wt% and the saturation magnetization could be up to 17.2 Am

/kg.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Overcoming the Trade-off between Toughness and Stiffness of Fully Polymer-based Alloys by Elastomeric Salami Particles through Reactive Blending

SYNTHESIS AND CHARACTERIZATION OF POLY(ε-CAPROLACTONE)/Fe3O4 NANOCOMPOSITES BY IN SITU POLYMERIZATION

pH-Responsive L-Cysteine-conjugated Polydopamine Nanocarriers for Controlled Release of Emamectin Benzoate against Pieris brassicae

Epoxy-functionalized Cyclohexane-based Ricinoleate Plasticizer: Synthesis, Performance Evaluation, and Plasticizing Mechanism

Durable Anti-fogging and Abrasion-resistant Coatings Based on Polyoxometalates-Hydrophilic Resin Composites with Enhanced Cohesion and Adhesion