The effect of pre-shear flow on the subsequent crystallization process of polymeric melt was investigated and a flow-induced crystallization (FIC) model based on the conformation tensor incorporating the pre-shear effect was proposed. The model is capable of predicting the overshoot phenomena of the stress and the flow-induced free energy change of the polymeric system at high pre-shear rates. Under the condition of flow

the increase in the activated nuclei number was contributed by the flow-induced free energy change

which showed an overwhelming effect on the nuclei formation during the pre-shear process at high shear rates. The half crystallization time (t1/2) of polypropylene (PP) as functions of pre-shear rate and pre-shear time at different crystallization temperatures was predicted and compared with the experiment data. Both numerical and experimental results showed that t1/2 of PP decreased dramatically when the flow started but leveled off at long times. It was found that two transformation stages in t1/2 existed within a wide range of shear rates. For the first stage where the melting polymer experienced a relatively weak shear flow

the acceleration of crystallization kinetics was mainly contributed by the steady value of free energy change while in the second stage for high shear rates

strong overshoot in flow-induced free energy change occurred and the crystallization kinetics was thus significantly enhanced. The overshoots in stress and flow-induced free energy change reflected an important role of flow on the primary nucleation especially when the flow was strong enough.