SYNTHESIS OF GRAFT COPOLYMERS WITH POLYISOBUTYLENE BRANCH CHAINS

Qing-yuan Li; Yi-xian Wu; Wen-yan Ma; Ri-wei Xu; Guan-ying Wu; Wan-tai Yang

doi:10.1007/s10118-010-9092-z

Your Location：

Home >

Browse articles >

SYNTHESIS OF GRAFT COPOLYMERS WITH POLYISOBUTYLENE BRANCH CHAINS

Papers | Updated：2021-06-21

- SYNTHESIS OF GRAFT COPOLYMERS WITH POLYISOBUTYLENE BRANCH CHAINS
- SYNTHESIS OF GRAFT COPOLYMERS WITH POLYISOBUTYLENE BRANCH CHAINS
- 高分子科学（英文版） 2010年28卷第3期页码：449-456
- Affiliations：
- Author bio：
- Funds：
- DOI：10.1007/s10118-010-9092-z
  中图分类号：
- 纸质出版：2010-05-20
- Accepted：
Scan QR Code
Qing-yuan Li, Yi-xian Wu, Wen-yan Ma, 等. SYNTHESIS OF GRAFT COPOLYMERS WITH POLYISOBUTYLENE BRANCH CHAINS[J]. 高分子科学（英文版）, 2010,28(3):449-456.

Qing-yuan Li, Yi-xian Wu, Wen-yan Ma, et al. SYNTHESIS OF GRAFT COPOLYMERS WITH POLYISOBUTYLENE BRANCH CHAINS[J]. 2010, 28(3): 449-456.
Qing-yuan Li, Yi-xian Wu, Wen-yan Ma, 等. SYNTHESIS OF GRAFT COPOLYMERS WITH POLYISOBUTYLENE BRANCH CHAINS[J]. 高分子科学（英文版）, 2010,28(3):449-456. DOI： 10.1007/s10118-010-9092-z.

Qing-yuan Li, Yi-xian Wu, Wen-yan Ma, et al. SYNTHESIS OF GRAFT COPOLYMERS WITH POLYISOBUTYLENE BRANCH CHAINS[J]. 2010, 28(3): 449-456. DOI： 10.1007/s10118-010-9092-z.

摘要

The copolymerization of 4-vinylbenzyl chloride (VBC) and vinyl acetate (VAC) was carried out in toluene at 75C via radical polymerization using 2

2-azo-bis-(isobutyronitrile) (AIBN) as an initiator. The random copolymers of poly(4-vinylbenzyl chloride-co-vinyl acetate) (P(VBC-co-VAC)) with number average molecular weight (Mn) from 2000 to 6900

relatively narrow molecular weight distribution (MWD

Mw/Mn ca. 2.0) and with different copolymer composition of 4-vinylbenzyl chloride (VBC) from 17 mol% to 62 mol% could be obtained. The P(VBC-co-VAC) copolymers with an average number of 7 to 13 initiating sites of benzyl chloride per macromolecule could be used for the cationic polymerization of isobutylene (IB). The cationic polymerizations of IB were further conducted by using P(VBC-co-VAC) copolymers as macroinitiators in conjunction with TiCl4 at-40C in CH2Cl2. The effects of VBC/TiCl4 (molar ratio) on monomer conversion

Mn and MWD of the resultant copolymers were investigated under 3 sets of conditions. It is found that P(VBC-co-VAC)-g-PIB copolymers with relatively narrow MWD (Mw/Mn ca. 2.0) and with terminal tert-chlorine functional groups in branched PIB chains could be successfully synthesized when VBC/TiCl4 (molar ratio) was set in the range from 0.10 to 1.12. The unimodal GPC curve of the P(VBC-co-VAC)-g-PIB copolymers by RI detector was almost in harmony with the GPC curve by UV detector. The TEM image of the P(VBC-co-VAC)-g-PIB copolymer stained by RuO indicated that the copolymer formed a two-phase morphology with P(VBC-co-VAC)-rich domains of 20-100 nm in size tethered by PIB branch segments.

Abstract

The copolymerization of 4-vinylbenzyl chloride (VBC) and vinyl acetate (VAC) was carried out in toluene at 75C via radical polymerization using 2

2-azo-bis-(isobutyronitrile) (AIBN) as an initiator. The random copolymers of poly(4-vinylbenzyl chloride-co-vinyl acetate) (P(VBC-co-VAC)) with number average molecular weight (Mn) from 2000 to 6900

relatively narrow molecular weight distribution (MWD

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Optically Active Helical Poly(phenyl isocyanide)s Bearing Achiral Benzanilide Pendants: from Controlled Synthesis to Enantioseparation Application

Preparation and Chiral Recognition Ability of Crystalline Cellulose Phenylcarbamate

Advances in Polymer-based Circularly Polarized Luminescent Materials

One-handed Helical Poly(m-terphenyl acetylene)s with Broad Optical Activity Range from Ultraviolet-Visible to Near-infrared Regions

Multiple-Responsive Chiral Hydrogels from Helical Dendronized Poly(phenylacetylene)s