OBSERVATION OF ENERGY DISSIPATION PEAK IN POLYSTYRENE MELT ABOVE T<sub>g</sub>

Shu-ying Shang Xue-bang Wu Jia-peng Shui Zhen-gang Zhu~() Key Laboratory of Materials Physics; Institute of Solid State Physics; Chinese Academy of Sciences; P.O.Box 1129; Hefei 230031; China

Your Location：

Home >

Browse articles >

OBSERVATION OF ENERGY DISSIPATION PEAK IN POLYSTYRENE MELT ABOVE T_g

Updated：2021-06-21

- OBSERVATION OF ENERGY DISSIPATION PEAK IN POLYSTYRENE MELT ABOVE T_g
- OBSERVATION OF ENERGY DISSIPATION PEAK IN POLYSTYRENE MELT ABOVE T_g
- 高分子科学（英文版） 2007年第6期页码：629-633
- Affiliations：
- Author bio：
- Funds：
  
  This work was supported by the National Natural Science Foundation of China（No.10174089）();Innovation Project of Chinese Academy of Sciences（No.044N121507）.()
- DOI：
  中图分类号： TQ325.2
- 纸质出版：2007
- Accepted：
Scan QR Code
[1].OBSERVATION OF ENERGY DISSIPATION PEAK IN POLYSTYRENE MELT ABOVE T_g[J].Chinese Journal of Polymer Science,2007(06):629-633.

Shu-ying Shang Xue-bang Wu Jia-peng Shui Zhen-gang Zhu~() Key Laboratory of Materials Physics, Institute of Solid State Physics, Chinese Academy of Sciences, et al. OBSERVATION OF ENERGY DISSIPATION PEAK IN POLYSTYRENE MELT ABOVE T_g[J]. 2007, (6): 629-633.
[1].OBSERVATION OF ENERGY DISSIPATION PEAK IN POLYSTYRENE MELT ABOVE T_g[J].Chinese Journal of Polymer Science,2007(06):629-633. DOI：

Shu-ying Shang Xue-bang Wu Jia-peng Shui Zhen-gang Zhu~() Key Laboratory of Materials Physics, Institute of Solid State Physics, Chinese Academy of Sciences, et al. OBSERVATION OF ENERGY DISSIPATION PEAK IN POLYSTYRENE MELT ABOVE T_g[J]. 2007, (6): 629-633. DOI：

摘要

正

In this paper two different kinds of dynamic mechanical techniques（inversed torsion pendulum and energy dissipation apparatus）were used to study the dynamic behavior of atactic monodisperse polystyrene above glass transition. The plots of energy dissipation versus temperature were presented for two atactic polystyrene samples.An apparent energy dissipation peak occurred above T

in each plot measured by the inversed torsion pendulum

and simultaneously the sample was found to flow assuredly at the moment.To exclude the influence of the flow and demonstrate there was a peak indeed above T

the energy dissipation apparatus was used

in which the samples were put into a cup.An obvious peak appeared

and it was in agreement with the peak observed by the inversed torsion pendulum.On basis of the results measured by the two kinds of apparatus

a conclusion is drawn that a peak occurrs above T

which gives a manifestation for the existence of the liquid-liquid transition.

Abstract

in each plot measured by the inversed torsion pendulum

and simultaneously the sample was found to flow assuredly at the moment.To exclude the influence of the flow and demonstrate there was a peak indeed above T

the energy dissipation apparatus was used

in which the samples were put into a cup.An obvious peak appeared

and it was in agreement with the peak observed by the inversed torsion pendulum.On basis of the results measured by the two kinds of apparatus

a conclusion is drawn that a peak occurrs above T

which gives a manifestation for the existence of the liquid-liquid transition.

关键词

Keywords

references

浏览量

159

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Topology-regulated Co-assembly of Single Chain Polymer Nanoparticles and Block Copolymers into Hierarchical Micelle@Vesicle Composite Structures

Squaramide-directed Cooperative One-dimensional Assembly in Telechelic Polydimethylsiloxane for Hierarchical Network Formation

Special Topic: Chirality in Polymers

2026-9 Contents

End-group and Side-chain Dual-engineering of Selenium-fused Acceptors for 20.08% Efficiency Polymer Solar Cells with Low Energy Loss

OBSERVATION OF ENERGY DISSIPATION PEAK IN POLYSTYRENE MELT ABOVE Tg

OBSERVATION OF ENERGY DISSIPATION PEAK IN POLYSTYRENE MELT ABOVE Tg

DOI：

摘要

Abstract

关键词

Keywords

references

OBSERVATION OF ENERGY DISSIPATION PEAK IN POLYSTYRENE MELT ABOVE T_g

OBSERVATION OF ENERGY DISSIPATION PEAK IN POLYSTYRENE MELT ABOVE T_g