AN EVA/UNMODIFIED NANO-MAGNESIUM HYDROXIDE/SILICONE RUBBER NANOCOMPOSITE WITH SYNERGISTIC FLAME RETARDANCY

乔金樑

Your Location：

Home >

Browse articles >

AN EVA/UNMODIFIED NANO-MAGNESIUM HYDROXIDE/SILICONE RUBBER NANOCOMPOSITE WITH SYNERGISTIC FLAME RETARDANCY

Rapid Communication | Updated：2021-06-21

- AN EVA/UNMODIFIED NANO-MAGNESIUM HYDROXIDE/SILICONE RUBBER NANOCOMPOSITE WITH SYNERGISTIC FLAME RETARDANCY
- AN EVA/UNMODIFIED NANO-MAGNESIUM HYDROXIDE/SILICONE RUBBER NANOCOMPOSITE WITH SYNERGISTIC FLAME RETARDANCY
- 高分子科学（英文版） 2007年第5期页码：437-440
- Affiliations：
  
  1. SINOPEC Beijing Research Institute of Chemical Industry Beijing 100013
  2. China
- Author bio：
- Funds：
  
  This work was subsidized by the Special Funds for Major State Basic Research Projects（No.2005CB623800）.()
- DOI：
  中图分类号： TB383.1
- 纸质出版：2007
- Accepted：
Scan QR Code
[1]乔金樑.AN EVA/UNMODIFIED NANO-MAGNESIUM HYDROXIDE/SILICONE RUBBER NANOCOMPOSITE WITH SYNERGISTIC FLAME RETARDANCY[J].Chinese Journal of Polymer Science,2007(05):437-440.

AN EVA/UNMODIFIED NANO-MAGNESIUM HYDROXIDE/SILICONE RUBBER NANOCOMPOSITE WITH SYNERGISTIC FLAME RETARDANCY[J]. 2007, (5): 437-440.
[1]乔金樑.AN EVA/UNMODIFIED NANO-MAGNESIUM HYDROXIDE/SILICONE RUBBER NANOCOMPOSITE WITH SYNERGISTIC FLAME RETARDANCY[J].Chinese Journal of Polymer Science,2007(05):437-440. DOI：

AN EVA/UNMODIFIED NANO-MAGNESIUM HYDROXIDE/SILICONE RUBBER NANOCOMPOSITE WITH SYNERGISTIC FLAME RETARDANCY[J]. 2007, (5): 437-440. DOI：

摘要

<正>A novel EVA/unmodified nano-magnesium hydroxide（NMH）/silicone rubber ternary nanocomposite was prepared by using a special compound flame retardant of NMH and silicone rubber（CFR）.The flammability of the ternary composite was studied by cone calorimeter test（CCT）.Synergistic effect on flame retardancy was found between silicone rubber and NMH.EVA/CFR ternary nanocomposite showed the lowest peak heat release rate（PHRR）and mass loss rate （MLR）among the samples of virgin EVA

EVA composites.The synergistic flame retardancy of silicone rubber and NMH in EVA system is attributed to the enhanced char layers in the condensed phase that prevents the heat and mass transfer in the fire.

Abstract

A novel EVA/unmodified nano-magnesium hydroxide（NMH）/silicone rubber ternary nanocomposite was prepared by using a special compound flame retardant of NMH and silicone rubber（CFR）.The flammability of the ternary composite was studied by cone calorimeter test（CCT）.Synergistic effect on flame retardancy was found between silicone rubber and NMH.EVA/CFR ternary nanocomposite showed the lowest peak heat release rate（PHRR）and mass loss rate （MLR）among the samples of virgin EVA

关键词

Keywords

references

浏览量

145

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

A Paradigm for BF3 Co-initiated Cationic Polymerization with Low Dispersity: Introducing Acetonitrile and Lowering the Reaction Temperature

Tunable Circularly Polarized Luminescence of Helical Poly(phenylacetylene)s via Side-chain-to-Backbone Förster Resonance Energy Transfer

Experimental Investigation of Graphene and TiO2 Reinforced Poly(vinyl alcohol)-based Fiber Metal Laminates

From Molecular Defect to Macroscopic Performance: Manipulating Dichroism and Mechanics in Iodine-doped Poly(vinyl alcohol) via Ethylene Incorporation

Porous Organic Polymers for Photocatalytic Hydrogen Peroxide Production: Recent Advances and Future Perspectives