NOVEL HYPERBRANCHED POLY（AMINE-ESTER） FILMS: PREPARATION, CHARACTERIZATION AND PROPERTIES

Xiu-zhen Wei; Bao-ku Zhu; Ling Xiao and You-yi Xu Institute of Polymer Science; Zhejiang University; Hangzhou 310027; China

Your Location：

Home >

Browse articles >

NOVEL HYPERBRANCHED POLY（AMINE-ESTER） FILMS: PREPARATION, CHARACTERIZATION AND PROPERTIES

Updated：2021-06-21

- NOVEL HYPERBRANCHED POLY（AMINE-ESTER） FILMS: PREPARATION, CHARACTERIZATION AND PROPERTIES
- NOVEL HYPERBRANCHED POLY（AMINE-ESTER） FILMS: PREPARATION, CHARACTERIZATION AND PROPERTIES
- 高分子科学（英文版） 2006年第3期页码：291-297
- Affiliations：
- Author bio：
- Funds：
  
  This work was supported by the National Natural Science Foundation of China （No. 50103010）the "973" Program （No. 2003. CB615705）()
- DOI：
  中图分类号： TQ320.721
- 纸质出版：2006
- Accepted：
Scan QR Code
[1].NOVEL HYPERBRANCHED POLY(AMINE-ESTER) FILMS: PREPARATION, CHARACTERIZATION AND PROPERTIES[J].Chinese Journal of Polymer Science,2006(03):291-297.

Xiu-zhen Wei, Bao-ku Zhu, Ling Xiao and You-yi Xu Institute of Polymer Science, et al. NOVEL HYPERBRANCHED POLY（AMINE-ESTER） FILMS: PREPARATION, CHARACTERIZATION AND PROPERTIES[J]. 2006, (3): 291-297.
[1].NOVEL HYPERBRANCHED POLY(AMINE-ESTER) FILMS: PREPARATION, CHARACTERIZATION AND PROPERTIES[J].Chinese Journal of Polymer Science,2006(03):291-297. DOI：

Xiu-zhen Wei, Bao-ku Zhu, Ling Xiao and You-yi Xu Institute of Polymer Science, et al. NOVEL HYPERBRANCHED POLY（AMINE-ESTER） FILMS: PREPARATION, CHARACTERIZATION AND PROPERTIES[J]. 2006, (3): 291-297. DOI：

摘要

<正>Crosslinked film of hyperbranched poly（amine-ester）（HPAE） was prepared by crosslinking its terminal hydroxyl groups with glutaraldehyde （GA）. Atom force microscope （AFM） and scanning electron microscope （SEM） reveals that they have smooth surfaces

dense and homogenous matrices. It was found that the water static contact angle is smaller than 41.7°

the tensile strength is higher than 8.9 MPa

the elongation at break is higher than 5.1%

the swelling degree is higher than 42% in water

and the Bovine hemoglobin （Hb） adsorption is relatively low. These results indicate that the crosslinked HPAE films might have some potential applications in many areas.

Abstract

Crosslinked film of hyperbranched poly（amine-ester）（HPAE） was prepared by crosslinking its terminal hydroxyl groups with glutaraldehyde （GA）. Atom force microscope （AFM） and scanning electron microscope （SEM） reveals that they have smooth surfaces

dense and homogenous matrices. It was found that the water static contact angle is smaller than 41.7°

the tensile strength is higher than 8.9 MPa

the elongation at break is higher than 5.1%

the swelling degree is higher than 42% in water

and the Bovine hemoglobin （Hb） adsorption is relatively low. These results indicate that the crosslinked HPAE films might have some potential applications in many areas.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

One-handed Helical Poly(m-terphenyl acetylene)s with Broad Optical Activity Range from Ultraviolet-Visible to Near-infrared Regions

Enhancing Processability of Phenylethynyl-terminated Imide Oligomers and Properties of Cured Polyimides via ―CF3 Incorporation

Advances in Polymer-based Circularly Polarized Luminescent Materials

Sequence-encoded Conformation Pathways in Viscoelastic Microphase Separation of Multiblock Copolymers

Improvements of Hydrophobicity and Toughness of Epoxy Coatings Modified with Hydroxyl-terminated Fluororubber