SYNTHESIS, CHARACTERIZATION AND NANOPARTICLE FORMATION OF STAR-SHAPED POLY(L-LACTIDE) WITH SIX ARMS

Lu Wang; Chen Cai; Chang-Ming Dong

Your Location：

Home >

Browse articles >

SYNTHESIS, CHARACTERIZATION AND NANOPARTICLE FORMATION OF STAR-SHAPED POLY(L-LACTIDE) WITH SIX ARMS

Papers | Updated：2021-06-21

- SYNTHESIS, CHARACTERIZATION AND NANOPARTICLE FORMATION OF STAR-SHAPED POLY(L-LACTIDE) WITH SIX ARMS
- SYNTHESIS, CHARACTERIZATION AND NANOPARTICLE FORMATION OF STAR-SHAPED POLY(L-LACTIDE) WITH SIX ARMS
- 高分子科学（英文版） 2008年26卷第2期页码：161-169
- Affiliations：
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：2008-03-20
- Accepted：
Scan QR Code
Lu Wang, Chen Cai, Chang-Ming Dong. SYNTHESIS, CHARACTERIZATION AND NANOPARTICLE FORMATION OF STAR-SHAPED POLY(L-LACTIDE) WITH SIX ARMS[J]. 高分子科学（英文版）, 2008,26(2):161-169.

Lu Wang, Chen Cai, Chang-Ming Dong. SYNTHESIS, CHARACTERIZATION AND NANOPARTICLE FORMATION OF STAR-SHAPED POLY(L-LACTIDE) WITH SIX ARMS[J]. 2008, 26(2): 161-169.
Lu Wang, Chen Cai, Chang-Ming Dong. SYNTHESIS, CHARACTERIZATION AND NANOPARTICLE FORMATION OF STAR-SHAPED POLY(L-LACTIDE) WITH SIX ARMS[J]. 高分子科学（英文版）, 2008,26(2):161-169. DOI：

Lu Wang, Chen Cai, Chang-Ming Dong. SYNTHESIS, CHARACTERIZATION AND NANOPARTICLE FORMATION OF STAR-SHAPED POLY(L-LACTIDE) WITH SIX ARMS[J]. 2008, 26(2): 161-169. DOI：

摘要

Well-defined star-shaped poly(L-lactide) with six arms (sPLLA) was synthesized via the ring-opening polymerization of L-lactide using dipentaerythritol as initiator and stannous octoate as catalyst in bulk at 125°C. The effects of molar ratios of both monomer to initiator and monomer to catalyst on the molecular weights of as-synthesized sPLLA polymers were in detail investigated. The molecular weights of sPLLA polymers linearly increased with the molar ratio of monomer to initiator

and the molecular weight distribution was narrow (Mw/Mn = 1.04－1.12). However

the molar ratio of monomer to catalyst had no apparent influence on the polymer molecular weight. Moreover

the maximal melting point

the crystallization temperature

and the degree of crystallinity of sPLLA polymers increased with the increasing molecular weight

meanwhile they exhibited a spherulitic morphology. Furthermore

spherical nanoparticles (less than 100 nm) could be generated by direct injection of sPLLA solutions into distilled water

and the average size of nanoparticles could be adjusted through both the macromolecular architecture and the polymer molecular weight

respectively.

Abstract

and the molecular weight distribution was narrow (Mw/Mn = 1.04－1.12). However

the molar ratio of monomer to catalyst had no apparent influence on the polymer molecular weight. Moreover

the maximal melting point

the crystallization temperature

and the degree of crystallinity of sPLLA polymers increased with the increasing molecular weight

meanwhile they exhibited a spherulitic morphology. Furthermore

spherical nanoparticles (less than 100 nm) could be generated by direct injection of sPLLA solutions into distilled water

and the average size of nanoparticles could be adjusted through both the macromolecular architecture and the polymer molecular weight

respectively.

关键词

Keywords

references

浏览量

378

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Alternating Poly(ether-alt-ester)s with High Glass Transition Temperature Enabled by Rotationally Constrained Biaryl Units

Optically Active Helical Poly(phenyl isocyanide)s Bearing Achiral Benzanilide Pendants: from Controlled Synthesis to Enantioseparation Application

Two-way Shape Memory Effect of Polycaprolactone-based Polyurethane via Synergistic Role of Hydrogen Bonding and Crystallization Tuned by Malic Acid

End-to-End Neuron-inspired Signal Transduction Using Organic Electrochemical Transistors

Tunable Circularly Polarized Luminescence of Helical Poly(phenylacetylene)s via Side-chain-to-Backbone Förster Resonance Energy Transfer