PHOTOINITIATED INVERSE EMULSION POLYMERIZATION OF

Lian-ying Liu; Zhi-xing Zhang; Wan-tai Yang

Your Location：

Home >

Browse articles >

PHOTOINITIATED INVERSE EMULSION POLYMERIZATION OF

Papers | Updated：2021-06-21

- PHOTOINITIATED INVERSE EMULSION POLYMERIZATION OF
- PHOTOINITIATED INVERSE EMULSION POLYMERIZATION OF
- 高分子科学（英文版） 2005年23卷第2期页码：219-225
- Affiliations：
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：2005-03-20
- Accepted：
Scan QR Code
Lian-ying Liu, Zhi-xing Zhang, Wan-tai Yang. PHOTOINITIATED INVERSE EMULSION POLYMERIZATION OF[J]. 高分子科学（英文版）, 2005,23(2):219-225.

Lian-ying Liu, Zhi-xing Zhang, Wan-tai Yang. PHOTOINITIATED INVERSE EMULSION POLYMERIZATION OF[J]. 2005, 23(2): 219-225.
Lian-ying Liu, Zhi-xing Zhang, Wan-tai Yang. PHOTOINITIATED INVERSE EMULSION POLYMERIZATION OF[J]. 高分子科学（英文版）, 2005,23(2):219-225. DOI：

Lian-ying Liu, Zhi-xing Zhang, Wan-tai Yang. PHOTOINITIATED INVERSE EMULSION POLYMERIZATION OF[J]. 2005, 23(2): 219-225. DOI：

摘要

Photoinitiated inverse emulsion polymerization of sodium acrylate (AANa) in kerosene was carried out at room or lower temperature

using 2

2-dimethoxy-2-phenylacetophenone (DMPA) as the initiator. Kinetic investigations indicated that the polymerization could be completed in about 30 min and produce polymer with high molecular weight (106~107). It was found that monomer droplets are the main sites for the polymerization (nucleation). With the increase of DMPA concentration

polymerization rate (Rp) reaches a maximum value while molecular weight of the produced polymer has an adverse result

but the dependence of Rp on incident light intensity is similar. Influences of other parameters such as monomer concentration

emulsifier content and reaction temperature

etc. were also studied. At lower pH values of water phase

Rp depends strongly on the pH due to the electrostatic interaction between the ionized radicals and the monomers. At higher pH

Rp shows a slight dependence on pH.

Abstract

Photoinitiated inverse emulsion polymerization of sodium acrylate (AANa) in kerosene was carried out at room or lower temperature

using 2

polymerization rate (Rp) reaches a maximum value while molecular weight of the produced polymer has an adverse result

but the dependence of Rp on incident light intensity is similar. Influences of other parameters such as monomer concentration

emulsifier content and reaction temperature

etc. were also studied. At lower pH values of water phase

Rp depends strongly on the pH due to the electrostatic interaction between the ionized radicals and the monomers. At higher pH

Rp shows a slight dependence on pH.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Tunable Circularly Polarized Luminescence of Helical Poly(phenylacetylene)s via Side-chain-to-Backbone Förster Resonance Energy Transfer

A Paradigm for BF3 Co-initiated Cationic Polymerization with Low Dispersity: Introducing Acetonitrile and Lowering the Reaction Temperature

Circularly Polarized Luminescence Based on Helical Polymers: Structure-Property Relationships and Regulation Mechanisms

pH-Responsive L-Cysteine-conjugated Polydopamine Nanocarriers for Controlled Release of Emamectin Benzoate against Pieris brassicae

Preparation and Chiral Recognition Ability of Crystalline Cellulose Phenylcarbamate