EFFECT OF STRESS-INDUCED REACTIONS ON MORPHOLOGICAL STRUCTURE AND PROCESSABILITY OF PVC DURING PAN-MILLING

Hua-wei Zou; Wen Xu; Qing-fen  Feng; Xi Xu

Your Location：

Home >

Browse articles >

EFFECT OF STRESS-INDUCED REACTIONS ON MORPHOLOGICAL STRUCTURE AND PROCESSABILITY OF PVC DURING PAN-MILLING

Papers | Updated：2021-06-21

- EFFECT OF STRESS-INDUCED REACTIONS ON MORPHOLOGICAL STRUCTURE AND PROCESSABILITY OF PVC DURING PAN-MILLING
- EFFECT OF STRESS-INDUCED REACTIONS ON MORPHOLOGICAL STRUCTURE AND PROCESSABILITY OF PVC DURING PAN-MILLING
- 高分子科学（英文版） 2005年23卷第2期页码：227-234
- Affiliations：
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：2005-03-20
- Accepted：
Scan QR Code
Hua-wei Zou, Wen Xu, Qing-fen Feng, 等. EFFECT OF STRESS-INDUCED REACTIONS ON MORPHOLOGICAL STRUCTURE AND PROCESSABILITY OF PVC DURING PAN-MILLING[J]. 高分子科学（英文版）, 2005,23(2):227-234.

Hua-wei Zou, Wen Xu, Qing-fen Feng, et al. EFFECT OF STRESS-INDUCED REACTIONS ON MORPHOLOGICAL STRUCTURE AND PROCESSABILITY OF PVC DURING PAN-MILLING[J]. 2005, 23(2): 227-234.
Hua-wei Zou, Wen Xu, Qing-fen Feng, 等. EFFECT OF STRESS-INDUCED REACTIONS ON MORPHOLOGICAL STRUCTURE AND PROCESSABILITY OF PVC DURING PAN-MILLING[J]. 高分子科学（英文版）, 2005,23(2):227-234. DOI：

Hua-wei Zou, Wen Xu, Qing-fen Feng, et al. EFFECT OF STRESS-INDUCED REACTIONS ON MORPHOLOGICAL STRUCTURE AND PROCESSABILITY OF PVC DURING PAN-MILLING[J]. 2005, 23(2): 227-234. DOI：

摘要

The effect of pan-milling on morphological structure

processability and properties of PVC was studied through SEM

FTIR

granulometer

GPC and mechanical properties test in the hope of gaining ease in operation

needless of plasticizers

a clean and efficient route for improving the processability of PVC through stress-induced reactions

fulfilling the idea of “plasticizing PVC by itself”. The experimental results show that during pan-milling at ambient temperature

within 2-3 min

the microcrystalline structure of PVC becomes indistinct

the grain size of PVC is reduced from 130-160 mm to 1-50 mm

the molecular weight of PVC is slightly decreased

the variation of molecular weight distribution is indistinct

the plasticizing time and torque at balance drop a great deal from 71-132 s to 31-33 s and from 18.2-22.1 Nm to 14.7-18.4 Nm

respectively

the processability of PVC is markedly improved

and the mechanical properties get enhanced too.

Abstract

The effect of pan-milling on morphological structure

processability and properties of PVC was studied through SEM

FTIR

granulometer

GPC and mechanical properties test in the hope of gaining ease in operation

needless of plasticizers

a clean and efficient route for improving the processability of PVC through stress-induced reactions

fulfilling the idea of “plasticizing PVC by itself”. The experimental results show that during pan-milling at ambient temperature

within 2-3 min

the microcrystalline structure of PVC becomes indistinct

the grain size of PVC is reduced from 130-160 mm to 1-50 mm

the molecular weight of PVC is slightly decreased

the variation of molecular weight distribution is indistinct

the plasticizing time and torque at balance drop a great deal from 71-132 s to 31-33 s and from 18.2-22.1 Nm to 14.7-18.4 Nm

respectively

the processability of PVC is markedly improved

and the mechanical properties get enhanced too.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

End-group and Side-chain Dual-engineering of Selenium-fused Acceptors for 20.08% Efficiency Polymer Solar Cells with Low Energy Loss

Epoxy-functionalized Cyclohexane-based Ricinoleate Plasticizer: Synthesis, Performance Evaluation, and Plasticizing Mechanism

Manipulating Hierarchical Aggregation Structure via Film-forming Kinetics Enables Organic Photovoltaics over 20% Efficiency

Enhanced Segment Mobility Promotes Stereocomplex Crystallization in Polymer Blends via Elevated Segmental Miscibility

Optically Active Helical Poly(phenyl isocyanide)s Bearing Achiral Benzanilide Pendants: from Controlled Synthesis to Enantioseparation Application