SYNTHESIS AND CHARACTERIZATION OF POLYMERS BEARING AZOBENZENE AND CARBAZOLE GROUPS VIA POST-AZO-COUPLING REACTION

Jun Shi; Zhi-wei Jiang; Li Zhang; Shao-kui Cao

Your Location：

Home >

Browse articles >

SYNTHESIS AND CHARACTERIZATION OF POLYMERS BEARING AZOBENZENE AND CARBAZOLE GROUPS VIA POST-AZO-COUPLING REACTION

Papers | Updated：2021-06-21

- SYNTHESIS AND CHARACTERIZATION OF POLYMERS BEARING AZOBENZENE AND CARBAZOLE GROUPS VIA POST-AZO-COUPLING REACTION
- SYNTHESIS AND CHARACTERIZATION OF POLYMERS BEARING AZOBENZENE AND CARBAZOLE GROUPS VIA POST-AZO-COUPLING REACTION
- 高分子科学（英文版） 2005年23卷第1期页码：5-9
- Affiliations：
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：2005-01-20
- Accepted：
Scan QR Code
Jun Shi, Zhi-wei Jiang, Li Zhang, 等. SYNTHESIS AND CHARACTERIZATION OF POLYMERS BEARING AZOBENZENE AND CARBAZOLE GROUPS VIA POST-AZO-COUPLING REACTION[J]. 高分子科学（英文版）, 2005,23(1):5-9.

Jun Shi, Zhi-wei Jiang, Li Zhang, et al. SYNTHESIS AND CHARACTERIZATION OF POLYMERS BEARING AZOBENZENE AND CARBAZOLE GROUPS VIA POST-AZO-COUPLING REACTION[J]. 2005, 23(1): 5-9.
Jun Shi, Zhi-wei Jiang, Li Zhang, 等. SYNTHESIS AND CHARACTERIZATION OF POLYMERS BEARING AZOBENZENE AND CARBAZOLE GROUPS VIA POST-AZO-COUPLING REACTION[J]. 高分子科学（英文版）, 2005,23(1):5-9. DOI：

Jun Shi, Zhi-wei Jiang, Li Zhang, et al. SYNTHESIS AND CHARACTERIZATION OF POLYMERS BEARING AZOBENZENE AND CARBAZOLE GROUPS VIA POST-AZO-COUPLING REACTION[J]. 2005, 23(1): 5-9. DOI：

摘要

A series of polymers bearing azobenzene and carbazole groups for photorefractive purpose were prepared via post-azo-coupling reaction. The successful reaction was identified by spectroscopic analysis and gel permeation chromatography. This approach is more facile compared with the direct polymerization of corresponding functional monomer. The polymers prepared have weight average molecular weight of higher than 1.5  104 and are easily soluble in common organic solvents like chloroform and tetrahydrofuran

polymer films with high optical quality could be easily fabricated through solution casting. Glass transition temperature (Tg) of the polymers ranges from 60℃ to 182℃

depending on the alkylene spacer length between the functional side group and the polymer backbone

and the polymers are relatively stable under 300℃.

Abstract

polymer films with high optical quality could be easily fabricated through solution casting. Glass transition temperature (Tg) of the polymers ranges from 60℃ to 182℃

depending on the alkylene spacer length between the functional side group and the polymer backbone

and the polymers are relatively stable under 300℃.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

End-group and Side-chain Dual-engineering of Selenium-fused Acceptors for 20.08% Efficiency Polymer Solar Cells with Low Energy Loss

Durable Anti-fogging and Abrasion-resistant Coatings Based on Polyoxometalates-Hydrophilic Resin Composites with Enhanced Cohesion and Adhesion

Circularly Polarized Luminescence Based on Helical Polymers: Structure-Property Relationships and Regulation Mechanisms

Silk Sericin-inspired Poly-β-homoserine for Protein Protection

Upgrading Commercially Available Polyethylene to High-value Materials with Strong Mechanical Performance and Hydrophilicity by Blending with Ethylene/meta-Methoxystyrene Copolymers