INFLUENCES OF ACID POST-TREATMENT ON THE MORPHOLOGY OF SOAP-FREE P(MMA-EA-MAA) PARTICLES PREPARED BY SEEDED EMULSION POLYMERIZATION

Kai Kang; Cheng-you Kan; Yi Du; De-shan Liu

Your Location：

Home >

Browse articles >

INFLUENCES OF ACID POST-TREATMENT ON THE MORPHOLOGY OF SOAP-FREE P(MMA-EA-MAA) PARTICLES PREPARED BY SEEDED EMULSION POLYMERIZATION

Papers | Updated：2021-06-21

- INFLUENCES OF ACID POST-TREATMENT ON THE MORPHOLOGY OF SOAP-FREE P(MMA-EA-MAA) PARTICLES PREPARED BY SEEDED EMULSION POLYMERIZATION
- INFLUENCES OF ACID POST-TREATMENT ON THE MORPHOLOGY OF SOAP-FREE P(MMA-EA-MAA) PARTICLES PREPARED BY SEEDED EMULSION POLYMERIZATION
- 高分子科学（英文版） 2005年23卷第5期页码：479-485
- Affiliations：
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：2005-09-20
- Accepted：
Scan QR Code
Kai Kang, Cheng-you Kan, Yi Du, 等. INFLUENCES OF ACID POST-TREATMENT ON THE MORPHOLOGY OF SOAP-FREE P(MMA-EA-MAA) PARTICLES PREPARED BY SEEDED EMULSION POLYMERIZATION[J]. 高分子科学（英文版）, 2005,23(5):479-485.

Kai Kang, Cheng-you Kan, Yi Du, et al. INFLUENCES OF ACID POST-TREATMENT ON THE MORPHOLOGY OF SOAP-FREE P(MMA-EA-MAA) PARTICLES PREPARED BY SEEDED EMULSION POLYMERIZATION[J]. 2005, 23(5): 479-485.
Kai Kang, Cheng-you Kan, Yi Du, 等. INFLUENCES OF ACID POST-TREATMENT ON THE MORPHOLOGY OF SOAP-FREE P(MMA-EA-MAA) PARTICLES PREPARED BY SEEDED EMULSION POLYMERIZATION[J]. 高分子科学（英文版）, 2005,23(5):479-485. DOI：

Kai Kang, Cheng-you Kan, Yi Du, et al. INFLUENCES OF ACID POST-TREATMENT ON THE MORPHOLOGY OF SOAP-FREE P(MMA-EA-MAA) PARTICLES PREPARED BY SEEDED EMULSION POLYMERIZATION[J]. 2005, 23(5): 479-485. DOI：

摘要

Soap-free poly(methyl methacrylate-ethyl acrylate-methacrylic acid) latex particles with narrow size distribution were synthesized by seeded emulsion polymerization

and the porous particles were created by a stepwise alkali/acid treatment method. Effects of acid treatment conditions on the particle morphology were investigated. Results show that one to three pores were formed inside most of particles after post-treatment. At pH 7.0

when the treatment temperature was lower than 70℃

the size of particles and the volume of pores remained almost unchanged

and these two values increased significantly when the temperature was higher than 70℃. Both the particle size and the pore volume decreased with the increase in initial pH value and treatment time in the acid treatment. As the pH was below 4.0 and the treatment time was longer than 180 min

the particles shrunk in size.

Abstract

Soap-free poly(methyl methacrylate-ethyl acrylate-methacrylic acid) latex particles with narrow size distribution were synthesized by seeded emulsion polymerization

when the treatment temperature was lower than 70℃

the size of particles and the volume of pores remained almost unchanged

the particles shrunk in size.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Epoxy-functionalized Cyclohexane-based Ricinoleate Plasticizer: Synthesis, Performance Evaluation, and Plasticizing Mechanism

Circularly Polarized Luminescence Based on Helical Polymers: Structure-Property Relationships and Regulation Mechanisms

Squaramide-directed Cooperative One-dimensional Assembly in Telechelic Polydimethylsiloxane for Hierarchical Network Formation

Alternating Poly(ether-alt-ester)s with High Glass Transition Temperature Enabled by Rotationally Constrained Biaryl Units

Multiple-Responsive Chiral Hydrogels from Helical Dendronized Poly(phenylacetylene)s