SYNTHESIS OF HYBRID MESOPOROUS POLYSTYRENE-SILICA MATERIALS WITH NON-SURFACTANT CITRIC ACID AS TEMPLATE VIA SOL-GEL PROCESS*

Your Location：

Home >

Browse articles >

SYNTHESIS OF HYBRID MESOPOROUS POLYSTYRENE-SILICA MATERIALS WITH NON-SURFACTANT CITRIC ACID AS TEMPLATE VIA SOL-GEL PROCESS*

Papers | Updated：2021-06-21

- SYNTHESIS OF HYBRID MESOPOROUS POLYSTYRENE-SILICA MATERIALS WITH NON-SURFACTANT CITRIC ACID AS TEMPLATE VIA SOL-GEL PROCESS*
- SYNTHESIS OF HYBRID MESOPOROUS POLYSTYRENE-SILICA MATERIALS WITH NON-SURFACTANT CITRIC ACID AS TEMPLATE VIA SOL-GEL PROCESS*
- 高分子科学（英文版） 2002年20卷第6期页码：565-572
- Affiliations：
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：2002-12-20
- Accepted：
Scan QR Code
SYNTHESIS OF HYBRID MESOPOROUS POLYSTYRENE-SILICA MATERIALS WITH NON-SURFACTANT CITRIC ACID AS TEMPLATE VIA SOL-GEL PROCESS*[J]. 高分子科学（英文版）, 2002,20(6):565-572.

SYNTHESIS OF HYBRID MESOPOROUS POLYSTYRENE-SILICA MATERIALS WITH NON-SURFACTANT CITRIC ACID AS TEMPLATE VIA SOL-GEL PROCESS*[J]. 2002, 20(6): 565-572.
SYNTHESIS OF HYBRID MESOPOROUS POLYSTYRENE-SILICA MATERIALS WITH NON-SURFACTANT CITRIC ACID AS TEMPLATE VIA SOL-GEL PROCESS*[J]. 高分子科学（英文版）, 2002,20(6):565-572. DOI：

SYNTHESIS OF HYBRID MESOPOROUS POLYSTYRENE-SILICA MATERIALS WITH NON-SURFACTANT CITRIC ACID AS TEMPLATE VIA SOL-GEL PROCESS*[J]. 2002, 20(6): 565-572. DOI：

摘要

Hybrid mesoporous polystyrene-silica materials were successfully prepared through HCl-catalyzed sol-gelreactions of tetraethyl orthosilicate (TEOS) and triethoxysilyl-functionalized polystyrene obtained via atom transfer radicalpolymerization (ATRP) of styrene

in the presence of citric acid (CA) as non-surfactant template or pore-forming agent andfollowed by ethanol extraction to remove template molecules. The materials were characterized by infrared spectroscopy (IR)

N2 adsorption-desorption measurements

powder X-ray diffraction (XRD)

thermogravimetric analysis (TGA) and transmission electron microscopy (TEM).The results indicate that the materials prepared with 50 wt%-60 wt% template contents have average pore sized of 2-3 nm and large surface areas(ca.886 m2/g) as well as high pore volumes (ca.0.53 cm3/g) The mesoporosity arises from interconnected channels and pores with disordered arrangements.The pore diameters and pore volumes increase as the template content is increased.The pore diameters show a little change upon heating at 200℃ overnight.However

the materials do not have good hydrothermal stability.

Abstract

N2 adsorption-desorption measurements

powder X-ray diffraction (XRD)

the materials do not have good hydrothermal stability.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Alternating Poly(ether-alt-ester)s with High Glass Transition Temperature Enabled by Rotationally Constrained Biaryl Units

On-demand Peelable UV-curable Adhesives with Superior Bonding Strength: Rational Molecular Engineering of Cohesion-adhesion Synergy

Advances in Polymer-based Circularly Polarized Luminescent Materials

End-to-End Neuron-inspired Signal Transduction Using Organic Electrochemical Transistors

Tunable Circularly Polarized Luminescence of Helical Poly(phenylacetylene)s via Side-chain-to-Backbone Förster Resonance Energy Transfer