SYNTHESIS AND CHARACTERIZATION OF PHTHALAZINONE POLY(ARYL ETHER SULFONE KETONE)WITH CARBONYL GROUP*

Papers | Updated：2021-06-21

- SYNTHESIS AND CHARACTERIZATION OF PHTHALAZINONE POLY(ARYL ETHER SULFONE KETONE)WITH CARBONYL GROUP*
- SYNTHESIS AND CHARACTERIZATION OF PHTHALAZINONE POLY(ARYL ETHER SULFONE KETONE)WITH CARBONYL GROUP*
- 高分子科学（英文版） 2002年20卷第3期页码：225-229
- Affiliations：
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：2002-06-20
- Accepted：
Scan QR Code
SYNTHESIS AND CHARACTERIZATION OF PHTHALAZINONE POLY(ARYL ETHER SULFONE KETONE)WITH CARBONYL GROUP*[J]. 高分子科学（英文版）, 2002,20(3):225-229.

SYNTHESIS AND CHARACTERIZATION OF PHTHALAZINONE POLY(ARYL ETHER SULFONE KETONE)WITH CARBONYL GROUP*[J]. 2002, 20(3): 225-229.
SYNTHESIS AND CHARACTERIZATION OF PHTHALAZINONE POLY(ARYL ETHER SULFONE KETONE)WITH CARBONYL GROUP*[J]. 高分子科学（英文版）, 2002,20(3):225-229. DOI：

SYNTHESIS AND CHARACTERIZATION OF PHTHALAZINONE POLY(ARYL ETHER SULFONE KETONE)WITH CARBONYL GROUP*[J]. 2002, 20(3): 225-229. DOI：

摘要

A kind of novel heat-resistant

high performance engineering thermoplastic phthalazinone poly(aryl ether sulfoneketone) (PPESK) containing a carboxyl group in its side chain was prepared by the nucleophilic displacement reaction of 4-(4-hydroxylphenyl)-1(2H)-phthalazinone with di(4-chlorophenyl) sulfone

4'-difluoro-benzophenone and phenolphthalin insulfolane in the presence of K2CO3 to produce high molecular weight polymers which can be dissolved in some polar solvents such as chloroform and nitrobenzene at room temperature and can be easily cast into flexible

yellowish and transparent films.PPESK is an amorphous polymer having a decomposition temperature above 400℃

which indicates that it has high thermal staility.At the same time

the thermal properties of PPESKs with dicyandiamide (DICY) as curing agent indicated that the heat-resistance properties of the PPESKs are improved after curing.The apparent activation energy(△E) of the cross-linking reaction and the reaction order(n) of PPESK/DICY were found to be 52.2 kJ/mol and ca.1.0

respectively.Therefore

the cross-linking reaction is approximately a first order reaction.

Abstract

A kind of novel heat-resistant

yellowish and transparent films.PPESK is an amorphous polymer having a decomposition temperature above 400℃

which indicates that it has high thermal staility.At the same time

respectively.Therefore

the cross-linking reaction is approximately a first order reaction.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Squaramide-directed Cooperative One-dimensional Assembly in Telechelic Polydimethylsiloxane for Hierarchical Network Formation

Manipulating Hierarchical Aggregation Structure via Film-forming Kinetics Enables Organic Photovoltaics over 20% Efficiency

2026-9 Contents

Improvements of Hydrophobicity and Toughness of Epoxy Coatings Modified with Hydroxyl-terminated Fluororubber

One-handed Helical Poly(m-terphenyl acetylene)s with Broad Optical Activity Range from Ultraviolet-Visible to Near-infrared Regions