CONTROLLED RELEASE FROM PDMAEMA GELS PREPARED BY GAMMA RADIATION*

Papers | Updated：2021-06-21

- CONTROLLED RELEASE FROM PDMAEMA GELS PREPARED BY GAMMA RADIATION*
- CONTROLLED RELEASE FROM PDMAEMA GELS PREPARED BY GAMMA RADIATION*
- 高分子科学（英文版） 2002年20卷第5期页码：409-412
- Affiliations：
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：2002-10-20
- Accepted：
Scan QR Code
CONTROLLED RELEASE FROM PDMAEMA GELS PREPARED BY GAMMA RADIATION*[J]. 高分子科学（英文版）, 2002,20(5):409-412.

CONTROLLED RELEASE FROM PDMAEMA GELS PREPARED BY GAMMA RADIATION*[J]. 2002, 20(5): 409-412.
CONTROLLED RELEASE FROM PDMAEMA GELS PREPARED BY GAMMA RADIATION*[J]. 高分子科学（英文版）, 2002,20(5):409-412. DOI：

CONTROLLED RELEASE FROM PDMAEMA GELS PREPARED BY GAMMA RADIATION*[J]. 2002, 20(5): 409-412. DOI：

摘要

Poly(N

N-dimethylaminoethyl methacrylate) (polyDMAEMA) hydrogels prepared by γ-irradiation showed obvioustemperature-sensitivity in a temperature range of 38-40℃ and pH-sensitivity at pH = 2.5. They also showed clectric responsebehavior although it was not typical. The hydrogels were used in controlled release at different pH

temperature

and electricvoltage. The release rates of methylene blue (MB) from the gels at 52℃ and pH = 1.24 were fatter than those at 20℃ and pH= 10.56

respectively. In addition

the release rate at a field voltage of 5.0 was also faster than that without electric field.

Abstract

Poly(N

temperature

and electricvoltage. The release rates of methylene blue (MB) from the gels at 52℃ and pH = 1.24 were fatter than those at 20℃ and pH= 10.56

respectively. In addition

the release rate at a field voltage of 5.0 was also faster than that without electric field.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

From Molecular Defect to Macroscopic Performance: Manipulating Dichroism and Mechanics in Iodine-doped Poly(vinyl alcohol) via Ethylene Incorporation

End-group and Side-chain Dual-engineering of Selenium-fused Acceptors for 20.08% Efficiency Polymer Solar Cells with Low Energy Loss

Silk Sericin-inspired Poly-β-homoserine for Protein Protection

Improvements of Hydrophobicity and Toughness of Epoxy Coatings Modified with Hydroxyl-terminated Fluororubber

Durable Anti-fogging and Abrasion-resistant Coatings Based on Polyoxometalates-Hydrophilic Resin Composites with Enhanced Cohesion and Adhesion