PREPARATION OF Au/SULFONATED POLYSTYRENE CATALYSTS FOR LOW-TEMPERATURE CO OXIDATION*

Your Location：

Home >

Browse articles >

PREPARATION OF Au/SULFONATED POLYSTYRENE CATALYSTS FOR LOW-TEMPERATURE CO OXIDATION*

Papers | Updated：2021-06-21

- PREPARATION OF Au/SULFONATED POLYSTYRENE CATALYSTS FOR LOW-TEMPERATURE CO OXIDATION*
- PREPARATION OF Au/SULFONATED POLYSTYRENE CATALYSTS FOR LOW-TEMPERATURE CO OXIDATION*
- 高分子科学（英文版） 2001年19卷第5期页码：503-507
- Affiliations：
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：2001-10-20
- Accepted：
Scan QR Code
PREPARATION OF Au/SULFONATED POLYSTYRENE CATALYSTS FOR LOW-TEMPERATURE CO OXIDATION*[J]. 高分子科学（英文版）, 2001,19(5):503-507.

PREPARATION OF Au/SULFONATED POLYSTYRENE CATALYSTS FOR LOW-TEMPERATURE CO OXIDATION*[J]. 2001, 19(5): 503-507.
PREPARATION OF Au/SULFONATED POLYSTYRENE CATALYSTS FOR LOW-TEMPERATURE CO OXIDATION*[J]. 高分子科学（英文版）, 2001,19(5):503-507. DOI：

PREPARATION OF Au/SULFONATED POLYSTYRENE CATALYSTS FOR LOW-TEMPERATURE CO OXIDATION*[J]. 2001, 19(5): 503-507. DOI：

摘要

Supported An catalysts for low-temperature CO oxidation were prepared by solvated motal atom impregnation(SMAI) and conventional impregnation (CI). X-ray photoelectron spectroscopy (XPS) investigations indicated that theelemental gold in all the samples was in the metallic state. XRD measurements showed that the mean diameters of Auparticles prepared by SMAI were smaller than those prepared by CI with the same gold content. Catalytic tests showed thatthe SMAI catalyst had higher CO oxidation activity than the CI catalyst with the same compositions.Both SMAI and CI catalysts exhibited high activity in low temperature CO oxidation.Full CO conversion was obtained at 323-383K.

Abstract

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Squaramide-directed Cooperative One-dimensional Assembly in Telechelic Polydimethylsiloxane for Hierarchical Network Formation

Enhanced Segment Mobility Promotes Stereocomplex Crystallization in Polymer Blends via Elevated Segmental Miscibility

Pyrimidoisoindigo-based Polymers for Ambipolar Charge Transport

Durable Anti-fogging and Abrasion-resistant Coatings Based on Polyoxometalates-Hydrophilic Resin Composites with Enhanced Cohesion and Adhesion

End-to-End Neuron-inspired Signal Transduction Using Organic Electrochemical Transistors