SYNTHESIS, STRUCTURE AND ELECTRICAL PROPERTIES OF POLY(PHENYLENE VINYLENE) FILM DOPED WITH FERRIC CHLORIDE*

LI Wenguang; WAN Meixiang

Your Location：

Home >

Browse articles >

SYNTHESIS, STRUCTURE AND ELECTRICAL PROPERTIES OF POLY(PHENYLENE VINYLENE) FILM DOPED WITH FERRIC CHLORIDE*

Papers | Updated：2021-06-21

- SYNTHESIS, STRUCTURE AND ELECTRICAL PROPERTIES OF POLY(PHENYLENE VINYLENE) FILM DOPED WITH FERRIC CHLORIDE*
- SYNTHESIS, STRUCTURE AND ELECTRICAL PROPERTIES OF POLY(PHENYLENE VINYLENE) FILM DOPED WITH FERRIC CHLORIDE*
- 高分子科学（英文版） 1997年15卷第2期页码：129-138
- Affiliations：
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：1997-06-20
- Accepted：
Scan QR Code
LI Wenguang, WAN Meixiang. SYNTHESIS, STRUCTURE AND ELECTRICAL PROPERTIES OF POLY(PHENYLENE VINYLENE) FILM DOPED WITH FERRIC CHLORIDE*[J]. 高分子科学（英文版）, 1997,15(2):129-138.

LI Wenguang, WAN Meixiang. SYNTHESIS, STRUCTURE AND ELECTRICAL PROPERTIES OF POLY(PHENYLENE VINYLENE) FILM DOPED WITH FERRIC CHLORIDE*[J]. 1997, 15(2): 129-138.
LI Wenguang, WAN Meixiang. SYNTHESIS, STRUCTURE AND ELECTRICAL PROPERTIES OF POLY(PHENYLENE VINYLENE) FILM DOPED WITH FERRIC CHLORIDE*[J]. 高分子科学（英文版）, 1997,15(2):129-138. DOI：

LI Wenguang, WAN Meixiang. SYNTHESIS, STRUCTURE AND ELECTRICAL PROPERTIES OF POLY(PHENYLENE VINYLENE) FILM DOPED WITH FERRIC CHLORIDE*[J]. 1997, 15(2): 129-138. DOI：

摘要

Poly(phenylene vinylene) (PPV) film was synthesized via a soluble precursor poly-mer. Strong fluorescence at 500-600nm was observed in both precursor and PPV film.Room-temperature conductivity of PPV film doped with FeCl3 depends on the eliminationtemperature

the concentration of FeCl3 and doping time. The maximum conductivity ofdoped PPV at room-temperature can reach about 40 S·cm-1. The temperature depen-dence of conductivity was controlled by 1D-VRH (1 Dimension Variable Range Hopping)model with To value of 3.9×103K.Non-Ohmic conductivity resulting from Schottky effect was observed and the value of converted voltage from Ohmic region into non-Ohmic region at the current-voltage characteristic was found to be dependent upon the work function of electrodes.

Abstract

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

End-group and Side-chain Dual-engineering of Selenium-fused Acceptors for 20.08% Efficiency Polymer Solar Cells with Low Energy Loss

Two-way Shape Memory Effect of Polycaprolactone-based Polyurethane via Synergistic Role of Hydrogen Bonding and Crystallization Tuned by Malic Acid

Porous Organic Polymers for Photocatalytic Hydrogen Peroxide Production: Recent Advances and Future Perspectives

Advances in Polymer-based Circularly Polarized Luminescent Materials

Optically Active Helical Poly(phenyl isocyanide)s Bearing Achiral Benzanilide Pendants: from Controlled Synthesis to Enantioseparation Application