EFFECT OF ULTRASONIC WAVE ON THE ELECTROPOLYMERIZATION OF PYRROLE*

YANG Jing; LI Yongfang

Your Location：

Home >

Browse articles >

EFFECT OF ULTRASONIC WAVE ON THE ELECTROPOLYMERIZATION OF PYRROLE*

Papers | Updated：2021-06-21

- EFFECT OF ULTRASONIC WAVE ON THE ELECTROPOLYMERIZATION OF PYRROLE*
- EFFECT OF ULTRASONIC WAVE ON THE ELECTROPOLYMERIZATION OF PYRROLE*
- 高分子科学（英文版） 1996年14卷第3期页码：270-276
- Affiliations：
  
  1.   Laboratory of Organic Solids
  2.   Institute of Chemistry
  3.   Academia Sinica
  4.   Beijing 100080
- Author bio：
- Funds：
- DOI：
  中图分类号： TQ316.3
- 纸质出版：1996-09-20
- Accepted：
Scan QR Code
[1]杨静,李永舫.EFFECT OF ULTRASONIC WAVE ON THE ELECTROPOLYMERIZATION OF PYRROLE[J].Chinese Journal of Polymer Science,1996,{4}(03):270-276.

YANG Jing, LI Yongfang. EFFECT OF ULTRASONIC WAVE ON THE ELECTROPOLYMERIZATION OF PYRROLE*[J]. 1996, 14(3): 270-276.
[1]杨静,李永舫.EFFECT OF ULTRASONIC WAVE ON THE ELECTROPOLYMERIZATION OF PYRROLE[J].Chinese Journal of Polymer Science,1996,{4}(03):270-276. DOI：

YANG Jing, LI Yongfang. EFFECT OF ULTRASONIC WAVE ON THE ELECTROPOLYMERIZATION OF PYRROLE*[J]. 1996, 14(3): 270-276. DOI：

摘要

<正> Electropolymerization of pyrrole under ultrasonic field at 20kHz was performed ina series of aqueous and propylene carbonate （PC） solutions. The ultrasonic wave withmoderate intensity at the power of 44W

which is the power threshold of the ultrasonicgenerator used in this work to produce cavitation effect

enhance the conductivity andtensile strength of the polypyrrole films as prepared. However

too high intensity of theultrasonic wave is harmful to the polymerization.

Abstract

Electropolymerization of pyrrole under ultrasonic field at 20kHz was performed ina series of aqueous and propylene carbonate （PC） solutions. The ultrasonic wave withmoderate intensity at the power of 44W

which is the power threshold of the ultrasonicgenerator used in this work to produce cavitation effect

enhance the conductivity andtensile strength of the polypyrrole films as prepared. However

too high intensity of theultrasonic wave is harmful to the polymerization.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Experimental Investigation of Graphene and TiO2 Reinforced Poly(vinyl alcohol)-based Fiber Metal Laminates

pH-Responsive L-Cysteine-conjugated Polydopamine Nanocarriers for Controlled Release of Emamectin Benzoate against Pieris brassicae

One-handed Helical Poly(m-terphenyl acetylene)s with Broad Optical Activity Range from Ultraviolet-Visible to Near-infrared Regions

Advances in Polymer-based Circularly Polarized Luminescent Materials

Multiple-Responsive Chiral Hydrogels from Helical Dendronized Poly(phenylacetylene)s