SOLID-STATE VARIABLE-TEMPERATURE NMR STUDY ON THE PHASE SEPARATION OF POLYETHER POLYURETHANE ZWITTERIONOMERS*

YANG Guang; 陈群; CHEN Qun; WANG Yuanshen; YANG Changzheng; WU Xuewen

Your Location：

Home >

Browse articles >

SOLID-STATE VARIABLE-TEMPERATURE NMR STUDY ON THE PHASE SEPARATION OF POLYETHER POLYURETHANE ZWITTERIONOMERS*

Papers | Updated：2021-06-21

- SOLID-STATE VARIABLE-TEMPERATURE NMR STUDY ON THE PHASE SEPARATION OF POLYETHER POLYURETHANE ZWITTERIONOMERS*
- SOLID-STATE VARIABLE-TEMPERATURE NMR STUDY ON THE PHASE SEPARATION OF POLYETHER POLYURETHANE ZWITTERIONOMERS*
- 高分子科学（英文版） 1994年12卷第4期页码：302-308
- Affiliations：
  
  1.   Analytical Center
  2.   East China Normal University
  3.   Shanghai 200062
- Author bio：
- Funds：
- DOI：
  中图分类号： TQ317
- 纸质出版：1994-12-20
- Accepted：
Scan QR Code
[1]杨光,陈群,王源身,杨昌正,邬学文.SOLID-STATE VARIABLE-TEMPERATURE NMR STUDY ON THE PHASE SEPARATION OF POLYETHER POLYURETHANE ZWITTERIONOMERS[J].Chinese Journal of Polymer Science,1994,{4}(04):302-308.

YANG Guang, CHEN Qun, WANG Yuanshen, et al. SOLID-STATE VARIABLE-TEMPERATURE NMR STUDY ON THE PHASE SEPARATION OF POLYETHER POLYURETHANE ZWITTERIONOMERS*[J]. 1994, 12(4): 302-308.
[1]杨光,陈群,王源身,杨昌正,邬学文.SOLID-STATE VARIABLE-TEMPERATURE NMR STUDY ON THE PHASE SEPARATION OF POLYETHER POLYURETHANE ZWITTERIONOMERS[J].Chinese Journal of Polymer Science,1994,{4}(04):302-308. DOI：

YANG Guang, CHEN Qun, WANG Yuanshen, et al. SOLID-STATE VARIABLE-TEMPERATURE NMR STUDY ON THE PHASE SEPARATION OF POLYETHER POLYURETHANE ZWITTERIONOMERS*[J]. 1994, 12(4): 302-308. DOI：

摘要

正

Polyether-polyurethane zwitterionomers based on 4

4’-diphenylmethane diisocyanate（MDI）

methyl diethanolamine （MDEA）

and polytetramethylene oxide glycol （PTMO） werestudied with variable-temperature wide-line

H NMR. It is found that upon ionization

degree ofphase separation in the polymer system decreased at first due to the loss of hard segmentregularity

while further ionization increased the degree of phase separation through increasinghard phase cohesion and difference of polarity between hard and soft segments.

Abstract

Polyether-polyurethane zwitterionomers based on 4

4’-diphenylmethane diisocyanate（MDI）

methyl diethanolamine （MDEA）

and polytetramethylene oxide glycol （PTMO） werestudied with variable-temperature wide-line

H NMR. It is found that upon ionization

degree ofphase separation in the polymer system decreased at first due to the loss of hard segmentregularity

while further ionization increased the degree of phase separation through increasinghard phase cohesion and difference of polarity between hard and soft segments.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Durable Anti-fogging and Abrasion-resistant Coatings Based on Polyoxometalates-Hydrophilic Resin Composites with Enhanced Cohesion and Adhesion

On-demand Peelable UV-curable Adhesives with Superior Bonding Strength: Rational Molecular Engineering of Cohesion-adhesion Synergy

Multiple-Responsive Chiral Hydrogels from Helical Dendronized Poly(phenylacetylene)s

Optically Active Helical Poly(phenyl isocyanide)s Bearing Achiral Benzanilide Pendants: from Controlled Synthesis to Enantioseparation Application

Manipulating Hierarchical Aggregation Structure via Film-forming Kinetics Enables Organic Photovoltaics over 20% Efficiency