- FREE STANDING FILM OF POLYANILINE
- FREE STANDING FILM OF POLYANILINE
- 高分子科学（英文版） 1991年9卷第3期页码：209-219
- Affiliations：
  
  1. Institute of Chemistry, Academia Sinica,Beijing
  2. Academia Sinica
  3. Beijing
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：1991-09-20
- Accepted：
Scan QR Code
[1]万梅香,曹镛,李军朝,周维侠,李素珍.FREE STANDING FILM OF POLYANILINE[J].Chinese Journal of Polymer Science,1991,{4}(03):209-219.

WAN Meixiang, CAO Yong, LI Junchao, et al. FREE STANDING FILM OF POLYANILINE[J]. 1991, 9(3): 209-219.
[1]万梅香,曹镛,李军朝,周维侠,李素珍.FREE STANDING FILM OF POLYANILINE[J].Chinese Journal of Polymer Science,1991,{4}(03):209-219. DOI：

WAN Meixiang, CAO Yong, LI Junchao, et al. FREE STANDING FILM OF POLYANILINE[J]. 1991, 9(3): 209-219. DOI：

摘要

<正> A free standing film of polyaniline as large as 18 cm×18cm×0.002 cm can be obtained by evaporation of a solution of the chemically synthesized base in NMP. Its structure was examined by the elemental analysis

U.V.-visible spectra

XPS

DSC

SEM and X-ray scattering and its conducting behavior as well as electrochemical properties were studied. Results show that the composition

structure of main chain

physical properties of the free standing film of polyanilme is similar to that of the powder. However

some differences in its electronic structure

conductivity at room temperature and potential of redox couple between the flee standing film and powder are observed

which may be due to cross-linking of the film of polyaniline.

Abstract

A free standing film of polyaniline as large as 18 cm×18cm×0.002 cm can be obtained by evaporation of a solution of the chemically synthesized base in NMP. Its structure was examined by the elemental analysis

U.V.-visible spectra

XPS

DSC

SEM and X-ray scattering and its conducting behavior as well as electrochemical properties were studied. Results show that the composition

structure of main chain

physical properties of the free standing film of polyanilme is similar to that of the powder. However

some differences in its electronic structure

conductivity at room temperature and potential of redox couple between the flee standing film and powder are observed

which may be due to cross-linking of the film of polyaniline.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Two-way Shape Memory Effect of Polycaprolactone-based Polyurethane via Synergistic Role of Hydrogen Bonding and Crystallization Tuned by Malic Acid

Durable Anti-fogging and Abrasion-resistant Coatings Based on Polyoxometalates-Hydrophilic Resin Composites with Enhanced Cohesion and Adhesion

Multiple-Responsive Chiral Hydrogels from Helical Dendronized Poly(phenylacetylene)s

Experimental Investigation of Graphene and TiO2 Reinforced Poly(vinyl alcohol)-based Fiber Metal Laminates

Molecularly Engineered Polyimide Films with Switchable Cavitation for Bidirectional Passive Thermal Regulation