MECHANICAL BEHAVIORS OF POLYURETHANE-UREA ELASTOMERIC FIBERS UNDER STATIC STRETCHING DEFORMATION

WANG Dexi; R. E. Lyon; R. J. Farris

Your Location：

Home >

Browse articles >

MECHANICAL BEHAVIORS OF POLYURETHANE-UREA ELASTOMERIC FIBERS UNDER STATIC STRETCHING DEFORMATION

Papers | Updated：2021-06-21

- MECHANICAL BEHAVIORS OF POLYURETHANE-UREA ELASTOMERIC FIBERS UNDER STATIC STRETCHING DEFORMATION
- MECHANICAL BEHAVIORS OF POLYURETHANE-UREA ELASTOMERIC FIBERS UNDER STATIC STRETCHING DEFORMATION
- 高分子科学（英文版） 1986年4卷第3期页码：262-273
- Affiliations：
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：1986-09-20
- Accepted：
Scan QR Code
WANG Dexi, R. E. Lyon, R. J. Farris. MECHANICAL BEHAVIORS OF POLYURETHANE-UREA ELASTOMERIC FIBERS UNDER STATIC STRETCHING DEFORMATION[J]. 高分子科学（英文版）, 1986,4(3):262-273.

WANG Dexi, R. E. Lyon, R. J. Farris. MECHANICAL BEHAVIORS OF POLYURETHANE-UREA ELASTOMERIC FIBERS UNDER STATIC STRETCHING DEFORMATION[J]. 1986, 4(3): 262-273.
WANG Dexi, R. E. Lyon, R. J. Farris. MECHANICAL BEHAVIORS OF POLYURETHANE-UREA ELASTOMERIC FIBERS UNDER STATIC STRETCHING DEFORMATION[J]. 高分子科学（英文版）, 1986,4(3):262-273. DOI：

WANG Dexi, R. E. Lyon, R. J. Farris. MECHANICAL BEHAVIORS OF POLYURETHANE-UREA ELASTOMERIC FIBERS UNDER STATIC STRETCHING DEFORMATION[J]. 1986, 4(3): 262-273. DOI：

摘要

The mechanical behaviors of polyether (ET) and polyester (ES) soft segment urethane-ureaelastomeric fibers constrained at different levels of elongation have been investigated by means ofdynamic mechanical tests and force-temperature measurements. The dynamjc mechanical re-sponse of the ET urethane-urea showed some difference from that of the ES as a function of exten-sion ratio. For force-temperature measuring the existence of a low temperature transition corre-sponding to the glass transition (Tg's) of the ester or ether soft segments

stree-softening temperature(Ts) and initial melting temperature(Tmh) of hard segment crystallites was observed.The result of cyclic testing of a constrained sample as a function of temperature indicated that the irreversible decrease in stress implied a permanent change in sample microstructure.

Abstract

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Sliding Dynamics of Ring Chain on a Rod-Coil Block Copolymer in Rotaxane

Manipulating Hierarchical Aggregation Structure via Film-forming Kinetics Enables Organic Photovoltaics over 20% Efficiency

2026-9 Contents

Sequence-encoded Conformation Pathways in Viscoelastic Microphase Separation of Multiblock Copolymers

From Molecular Defect to Macroscopic Performance: Manipulating Dichroism and Mechanics in Iodine-doped Poly(vinyl alcohol) via Ethylene Incorporation