A NEW PEAK (T4) IN THE 13C-NMR SPECTRUM OF POLYBUTADIENE

Your Location：

Home >

Browse articles >

Papers | Updated：2021-06-21

- A NEW PEAK (T4) IN THE 13C-NMR SPECTRUM OF POLYBUTADIENE
- A NEW PEAK (T4) IN THE 13C-NMR SPECTRUM OF POLYBUTADIENE
- 高分子科学（英文版） 1983年1卷第1期页码：80-82
- Affiliations：
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：1983-07-20
- Accepted：
Scan QR Code
ZHOU Zinan, XIE Demin, ZHANG Jianguo, 等. A NEW PEAK (T4) IN THE 13C-NMR SPECTRUM OF POLYBUTADIENE[J]. 高分子科学（英文版）, 1983,1(1):80-82.

ZHOU Zinan, XIE Demin, ZHANG Jianguo, et al. A NEW PEAK (T4) IN THE 13C-NMR SPECTRUM OF POLYBUTADIENE[J]. 1983, 1(1): 80-82.
ZHOU Zinan, XIE Demin, ZHANG Jianguo, 等. A NEW PEAK (T4) IN THE 13C-NMR SPECTRUM OF POLYBUTADIENE[J]. 高分子科学（英文版）, 1983,1(1):80-82. DOI：

ZHOU Zinan, XIE Demin, ZHANG Jianguo, et al. A NEW PEAK (T4) IN THE 13C-NMR SPECTRUM OF POLYBUTADIENE[J]. 1983, 1(1): 80-82. DOI：

A new peak at 39.0 ppm in the 13C-NMR spectrum of polybutadiene (PBD) was discovered. This peak is assigned to the fourth peak (T4) of trans-1

4-sequence marked with an asterisk as shown in Fig. 3 in the text.The occurrence of T4 carbon nuclei is strongly affected by their neighboring 1

2-units. So long as both contents of trans-1

4- and 1

2-units attain their proper amounts the peak (T4) with appear in the 13C-NMR spectrum of PBD.

A new peak at 39.0 ppm in the 13C-NMR spectrum of polybutadiene (PBD) was discovered. This peak is assigned to the fourth peak (T4) of trans-1

4-sequence marked with an asterisk as shown in Fig. 3 in the text.The occurrence of T4 carbon nuclei is strongly affected by their neighboring 1

2-units. So long as both contents of trans-1

4- and 1

2-units attain their proper amounts the peak (T4) with appear in the 13C-NMR spectrum of PBD.

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Improvements of Hydrophobicity and Toughness of Epoxy Coatings Modified with Hydroxyl-terminated Fluororubber

On-demand Peelable UV-curable Adhesives with Superior Bonding Strength: Rational Molecular Engineering of Cohesion-adhesion Synergy

One-handed Helical Poly(m-terphenyl acetylene)s with Broad Optical Activity Range from Ultraviolet-Visible to Near-infrared Regions

Epoxy-functionalized Cyclohexane-based Ricinoleate Plasticizer: Synthesis, Performance Evaluation, and Plasticizing Mechanism

Advances in Polymer-based Circularly Polarized Luminescent Materials