OSCILLATORY SHEAR-ACCELERATED EXFOLIATION OF GRAPHITE IN POLYPROPYLENE MELT DURING INJECTION MOLDING

Nan Li; Wei Cheng; Kun Ren; Feng Luo; Ke Wang; Qiang Fu

doi:10.1007/s10118-013-1204-0

Your Location：

Home >

Browse articles >

OSCILLATORY SHEAR-ACCELERATED EXFOLIATION OF GRAPHITE IN POLYPROPYLENE MELT DURING INJECTION MOLDING

PAPER | Updated：2023-01-03

- OSCILLATORY SHEAR-ACCELERATED EXFOLIATION OF GRAPHITE IN POLYPROPYLENE MELT DURING INJECTION MOLDING
- OSCILLATORY SHEAR-ACCELERATED EXFOLIATION OF GRAPHITE IN POLYPROPYLENE MELT DURING INJECTION MOLDING
- Chinese Journal of Polymer Science 2013年31卷第1期页码：98-109
- Affiliations：
  
  College of Polymer Science and Engineering, State Key Laboratory of Polymer Materials Engineering, Sichuan University, Chengdu 610065, China
- Author bio：
  
  **Ke Wang (王柯), wkestar@scu.edu.cn
  Qiang Fu (傅强), E-mail: qiangfu@scu.edu.cn
- Funds：
  
  National Natural Science Foundation of China(21074075);program for the new century excellent talents of ministry of education of China(NCET-11-0348)
- DOI：10.1007/s10118-013-1204-0
  中图分类号：
- 收稿：2012-05-09，
  
  修回：2012-07-09，
  
  录用：2012-07-25，
  
  纸质出版：2013-01
- Accepted：
Scan QR Code
Nan Li, Wei Cheng, Kun Ren, 等. OSCILLATORY SHEAR-ACCELERATED EXFOLIATION OF GRAPHITE IN POLYPROPYLENE MELT DURING INJECTION MOLDING[J]. Chinese Journal of Polymer Science, 2013,31(1):98-109.

Nan Li, Wei Cheng, Kun Ren, et al. OSCILLATORY SHEAR-ACCELERATED EXFOLIATION OF GRAPHITE IN POLYPROPYLENE MELT DURING INJECTION MOLDING[J]. Chinese Journal of Polymer Science, 2013, 31(1): 98-109.
Nan Li, Wei Cheng, Kun Ren, 等. OSCILLATORY SHEAR-ACCELERATED EXFOLIATION OF GRAPHITE IN POLYPROPYLENE MELT DURING INJECTION MOLDING[J]. Chinese Journal of Polymer Science, 2013,31(1):98-109. DOI： 10.1007/s10118-013-1204-0.

Nan Li, Wei Cheng, Kun Ren, et al. OSCILLATORY SHEAR-ACCELERATED EXFOLIATION OF GRAPHITE IN POLYPROPYLENE MELT DURING INJECTION MOLDING[J]. Chinese Journal of Polymer Science, 2013, 31(1): 98-109. DOI： 10.1007/s10118-013-1204-0.

摘要

Abstract

In this study

good dispersion status of graphite in a nonpolar

intractable polymer

i.e.

polypropylene (PP)

was realized in melt processing by using a specific dynamic packing injection molding (DPIM) technique. The exfoliation extent of graphite increased remarkably from the skin zone to the core zone of the molded part

as confirmed by combination of WAXD

SEM and TEM analyses

indicating an accelerated exfoliation occurred during the DPIM processing. This phenomenon is due to decreased melt flow c

hannel and increased melt viscosity as the solidification takes place from the wall into the center

which leads to greatly increased shear force. The good dispersion of graphite results in obvious reinforcements of both tensile strength and impact strength by adding moderate amount of graphite. The present study proposes a promising route for realizing the large-scale fabrication of structural parts of polymer/exfoliated-graphite nanocomposites with excellent mechanical properties.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Data-Driven Exploration of Polymer Processing Effects on the Mechanical Properties in Carbon Black-Reinforced Rubber Composites

Improvements of Hydrophobicity and Toughness of Epoxy Coatings Modified with Hydroxyl-terminated Fluororubber

Effects of Different Nucleating Agents, Annealing and Pre-stretching Process on the Crystallinity and Mechanical Properties of Poly(butylene carbonate)

Combining Matrix Flexibility and Synthesis Approaches as a Design Strategy for Tailored Polyimide Nanocomposites with Fe2O3 and Al2O3

Squaramide-directed Cooperative One-dimensional Assembly in Telechelic Polydimethylsiloxane for Hierarchical Network Formation