CHARACTERIZATION OF A MODIFIED SILICON-CONTAINING ARYLACETYLENE RESIN WITH POSS FUNCTIONALITY

Zhen-yu Jiang; Yan Zhou; Fa-rong Huang; Lei Du

doi:10.1007/s10118-011-1086-y

Your Location：

Home >

Browse articles >

CHARACTERIZATION OF A MODIFIED SILICON-CONTAINING ARYLACETYLENE RESIN WITH POSS FUNCTIONALITY

Updated：2021-06-21

- CHARACTERIZATION OF A MODIFIED SILICON-CONTAINING ARYLACETYLENE RESIN WITH POSS FUNCTIONALITY
- CHARACTERIZATION OF A MODIFIED SILICON-CONTAINING ARYLACETYLENE RESIN WITH POSS FUNCTIONALITY
- Chinese Journal of Polymer Science 2011年29卷第6期页码：726-731
- Affiliations：
  
  1.Key Laboratory of Specially Functional Polymeric Materials of Ministry of Education, School of Material Science and Engineering, East China University of Science and Techology, Shanghai 200237, China
- Author bio：
  
  *Fa-rong Huang (黄发荣), E-mail: fhuanglab@ecust.edu.cn
- Funds：
- DOI：10.1007/s10118-011-1086-y
  中图分类号：
Scan for full text
Zhen-yu Jiang, Yan Zhou, Fa-rong Huang, 等. CHARACTERIZATION OF A MODIFIED SILICON-CONTAINING ARYLACETYLENE RESIN WITH POSS FUNCTIONALITY[J]. Chinese Journal of Polymer Science, 2011,29(6):726-731.

Zhen-yu Jiang, Yan Zhou, Fa-rong Huang, et al. CHARACTERIZATION OF A MODIFIED SILICON-CONTAINING ARYLACETYLENE RESIN WITH POSS FUNCTIONALITY[J]. Chinese Journal of Polymer Science, 2011,29(6):726-731.
Zhen-yu Jiang, Yan Zhou, Fa-rong Huang, 等. CHARACTERIZATION OF A MODIFIED SILICON-CONTAINING ARYLACETYLENE RESIN WITH POSS FUNCTIONALITY[J]. Chinese Journal of Polymer Science, 2011,29(6):726-731. DOI： 10.1007/s10118-011-1086-y.

Zhen-yu Jiang, Yan Zhou, Fa-rong Huang, et al. CHARACTERIZATION OF A MODIFIED SILICON-CONTAINING ARYLACETYLENE RESIN WITH POSS FUNCTIONALITY[J]. Chinese Journal of Polymer Science, 2011,29(6):726-731. DOI： 10.1007/s10118-011-1086-y.

摘要

Abstract

A modified silicon-containing arylacetylene resin with a well-defined organic-inorganic POSS functionality was successfully synthesized by Huisgen azide-alkyne 1,3-dipolar cycloaddition. The POSS hybridized resin exhibits excellent thermal properties which were characterized by differential scanning calorimetry (DSC) and thermogravimetric analyses (TGA). Scanning electron microscope (SEM) was used to characterize fracture surface of the hybridized polymer. The results show that phase separation occurs. The POSS moieties are aggregated each other in the polymer to form 200-400 nm domains.

关键词

Keywords

Silicon-containing arylacetylene resin13-Dipolar cycloadditionPOSS-hybridized resinHigh performance resinModification by click chemistry