Characteristic Assessment of Stabilized Polyacrylonitrile Nanowebs for the Production of Activated Carbon Nano-Sorbents

S. Rafiei; B. Noroozi; Sh. Arbab; A.K. Haghi

doi:10.1007/s10118-014-1410-4

Your Location：

Home >

Browse articles >

Characteristic Assessment of Stabilized Polyacrylonitrile Nanowebs for the Production of Activated Carbon Nano-Sorbents

Updated：2021-06-21

- Characteristic Assessment of Stabilized Polyacrylonitrile Nanowebs for the Production of Activated Carbon Nano-Sorbents
- Chinese Journal of Polymer Science Vol. 32, Issue 4, Pages: 449-457(2014)
- Affiliations：
  
  Department of Textile Engineering, University of Guilan, P.O. Box 41635-3756, Rasht, Iran
- Author bio：
  
  *B. Noroozi, E-mail: babaknoroozi@guilan.ac.ir
- Funds：
- DOI：10.1007/s10118-014-1410-4
  CLC：
- Received：04 July 2013，
  
  Revised：2013-09-02，
  
  Accepted：05 September 2013，
  
  Published：2014-04
- Accepted：
Scan QR Code
S. Rafiei, B. Noroozi, Sh. Arbab, et al. Characteristic Assessment of Stabilized Polyacrylonitrile Nanowebs for the Production of Activated Carbon Nano-Sorbents[J]. Chinese Journal of Polymer Science, 2014, 32(4): 449-457.
DOI：

S. Rafiei, B. Noroozi, Sh. Arbab, et al. Characteristic Assessment of Stabilized Polyacrylonitrile Nanowebs for the Production of Activated Carbon Nano-Sorbents[J]. Chinese Journal of Polymer Science, 2014, 32(4): 449-457. DOI： 10.1007/s10118-014-1410-4.

摘要

Abstract

Polyacrylonitrile (PAN) nanofibers with average diameter of 300 nm were produced by electro-spinning. The nanofibers were stabilized at different temperatures in the range of 180−270 ℃ in several duration times and heating rates. Fourier transforms infrared (FTIR) spectroscopy

differential scanning calorimetry (DSC) and X-ray diffraction (XRD) analyzing techniques were employed to measure the extent of stabilization reaction. By all procedures

the ranges of temperature and duration time recommended were about 250−270 ℃ and 1−2 h

respectively. Increasing the activation temperature from 800 ℃ to 1200 ℃ caused porosity and pore volume development up to 60% and 0.532 cm

respectively. Pore width of all samples was calculated to be about 0.7 nm confirming micro-pore structure of the produced PAN based activated carbon nanofibers. Comparing dye adsorption for different adsorbents including chitin and granular activated carbon (GAC) showed the highest efficiency for the produced activated carbon nanofibers (ACNFs).

关键词

Keywords

references

Views

375

Downloads

CSCD

Alert me when the article has been cited

Submit

Tools

Publicity Resources

EFFECTS OF DEFORMATION-INDUCED ORIENTATION ON CYCLIZATION AND OXIDATION OF POLYACRYLONITRILE FIBERS DURING STABILIZATION PROCESS

Boehmite/Polyacrylonitrile Composite Nanofiber Separator with Enhanced Ionic Conductivity and Thermal Stability for Lithium-Ion Batteries

High Strength Electrospun Single Copolyacrylonitrile (coPAN) Nanofibers with Improved Molecular Orientation by Drawing

Elimination of Surfactants and Small Dyes from Water with Silicasupported Dendritic Amphiphiles

Hierarchically Porous Carbon Membranes Derived from PAN and Their Selective Adsorption of Organic Dyes

Related Author

Jie-ying Liang

Zhao-kun Ma

Feng Lian

Jie Liu

Dávid István Kis

Wei Luo

Xiao-Peng Li

Xiao-Song Liu

Related Institution

Key Laboratory of Carbon Fiber and Functional Polymers, Ministry of Education, Beijing University of Chemical Technology

Department of Innovative Vehicles and Materials, GAMF Faculty of Engineering and Computer Science, John von Neumann University, Kecskemét

College of Materials Science and Engineering, Donghua University

Oxford Suzhou Centre for Advanced Research

School of Materials, Shanghai Dianji University

⁰