SYNTHESIS AND CHARACTERIZATION OF AN ACRYLATE POLYMER CONTAINING CHLORINE-1,3-DIOXALANE GROUPS IN SIDE CHAINS

Zulfiye İlter; Ferhat Alhanlı; Fatih Doğan; İsmet Kaya

doi:10.1007/s10118-012-1155-x

Your Location：

Home >

Browse articles >

SYNTHESIS AND CHARACTERIZATION OF AN ACRYLATE POLYMER CONTAINING CHLORINE-1,3-DIOXALANE GROUPS IN SIDE CHAINS

PAPER | Updated：2023-01-03

- SYNTHESIS AND CHARACTERIZATION OF AN ACRYLATE POLYMER CONTAINING CHLORINE-1,3-DIOXALANE GROUPS IN SIDE CHAINS
- Chinese Journal of Polymer Science Vol. 30, Issue 5, Pages: 642-651(2012)
- Affiliations：
  
  a.Fırat University, Faculty of Science and Arts, Department of Chemistry, Elazıg, Turkey
  b.Çanakkale Onsekiz Mart University, Faculty of Education, Secondary Science and Mathematics Education 17100, Çanakkale, Turkey
  c.Çanakkale Onsekiz Mart University, Department of Chemistry, 17020, Çanakkale, Turkey
- Author bio：
  
  *İsmet Kaya, E-mail: kayaismet@hotmail.com
- Funds：
- DOI：10.1007/s10118-012-1155-x
  CLC：
- Received：31 October 2011，
  
  Revised：2011-12-03，
  
  Accepted：06 December 2011，
  
  Published：2012-09
- Accepted：
Scan QR Code
Zulfiye İlter, Ferhat Alhanlı, Fatih Doğan, et al. SYNTHESIS AND CHARACTERIZATION OF AN ACRYLATE POLYMER CONTAINING CHLORINE-1,3-DIOXALANE GROUPS IN SIDE CHAINS[J]. Chinese Journal of Polymer Science, 2012, 30(5): 642-651.
DOI：

Zulfiye İlter, Ferhat Alhanlı, Fatih Doğan, et al. SYNTHESIS AND CHARACTERIZATION OF AN ACRYLATE POLYMER CONTAINING CHLORINE-1,3-DIOXALANE GROUPS IN SIDE CHAINS[J]. Chinese Journal of Polymer Science, 2012, 30(5): 642-651. DOI： 10.1007/s10118-012-1155-x.

摘要

Abstract

Poly[2-(4-chlorophenyl)-1

3-dioxolan-4-yl]methyl acrylate

poly(CPhDMA)

was synthesized with radical polymerization process using 2

2′-azobisisobutyronitrile as radical initiator in 1

4-dioxane at 60℃. The structure of poly(CPhDMA) was confirmed by means of UV-Vis

FT-IR

H-NMR

and

C-NMR spectral techniques. The molecular weight distribution values of the polymer were determined with gel permeation chromatography (GPC). The number-average molecular weight (

)

weight-average molecular weight (

) and polydispersity index (PDI) values of poly(CPhDMA) were determined to be 10300

21600 and 2.097

respectively. The thermal degradation kinetics of the polymer was investigated by using TG/DTG-DTA and DSC analyses at different heating rates in dynamic nitrogen atmosphere. The apparent activation energy values obtained by Flynn-Wall-Ozawa and Friedman methods were found to be 91.68 and 85.23 kJ mol

-1

respectively

for thermal decomposition of poly(CPhDMA). Also

the thermal degradation activation energy value of poly(CPhDMA) was calculated by using the Kissinger method based on the DTG

DTA and DSC data. Then the mechanism function of it was determined by master plots method. Finally

electrical and optical properties of poly(CPhDMA) were determined by four-point probe and UV-Vis techniques

respectively.

关键词

Keywords

references

Views

Downloads

CSCD

Alert me when the article has been cited

Submit

Tools

Publicity Resources

Preparation of Poly(phosphoric acid piperazine) and Its Application as an Effective Flame Retardant for Epoxy Resin

Synergistic Effects of Aluminum Hypophosphite on Intumescent Flame Retardant Polypropylene System

Thermal Degradation, Flame Retardance and Mechanical Properties of Thermoplastic Polyurethane Composites Based on Aluminum Hypophosphite

Sliding Dynamics of Ring Chain on a Rod-Coil Block Copolymer in Rotaxane

On-demand Peelable UV-curable Adhesives with Superior Bonding Strength: Rational Molecular Engineering of Cohesion-adhesion Synergy

Related Author

Miao-jun Xu

Si-Yu Xia

Chuan Liu

Bin Li

Jing Wang

Yue-hang Ding

Shou-song Xiao

Ming-jun Chen

Related Institution

Heilongjiang Key Laboratory of Molecular Design and Preparation of Flame Retarded Materials, College of Science, Northeast Forestry University

Center for Degradable and Flame-Retardant Polymeric Materials, National Engineering Laboratory of Eco-Friendly Polymeric Materials (Sichuan), College of Chemistry, Analytical and Testing Center, Sichuan University

⁰