CHARACTERIZATION OF IMPACT POLYPROPYLENE COPOLYMERS BY SOLVENT FRACTIONATION

Xiao-ying Lu; Jian-jun Yi; Shang-tao Chen; Feng-hua Zu; Rong-bo Li

doi:10.1007/s10118-012-1097-3

Your Location：

Home >

Browse articles >

CHARACTERIZATION OF IMPACT POLYPROPYLENE COPOLYMERS BY SOLVENT FRACTIONATION

Paper | Updated：2023-01-03

- CHARACTERIZATION OF IMPACT POLYPROPYLENE COPOLYMERS BY SOLVENT FRACTIONATION
- Chinese Journal of Polymer Science Vol. 30, Issue 1, Pages: 122-129(2012)
- Affiliations：
  
  Petrochina Petrochemical Research Institute, Beijing 100195, China
- Author bio：
  
  **Jian-jun Yi (义建军), E-mail: yijianjun@petrochina.com.cn
- Funds：
- DOI：10.1007/s10118-012-1097-3
  CLC：
- Received：15 February 2011，
  
  Revised：2011-04-07，
  
  Accepted：18 April 2011，
  
  Published：2012-01
- Accepted：
Scan QR Code
Xiao-ying Lu, Jian-jun Yi, Shang-tao Chen, et al. CHARACTERIZATION OF IMPACT POLYPROPYLENE COPOLYMERS BY SOLVENT FRACTIONATION[J]. Chinese Journal of Polymer Science, 2012, 30(1): 122-129.
DOI：

Xiao-ying Lu, Jian-jun Yi, Shang-tao Chen, et al. CHARACTERIZATION OF IMPACT POLYPROPYLENE COPOLYMERS BY SOLVENT FRACTIONATION[J]. Chinese Journal of Polymer Science, 2012, 30(1): 122-129. DOI： 10.1007/s10118-012-1097-3.

摘要

Abstract

The compositional heterogeneity of two impact polypropylene copolymers (IPCs) was studied by a combinatory investigation of temperature rising elution fractionation (TREF) and solvent fractionation. The chain structures and composition of fractions obtained from solvent fractionation were examined in detail. The TREF results shows that there are much more E-P segmented copolymer and more uniform distribution of ethylene sequence in IPC-1

which is responsible for its better comprehensive mechanical performance. The fractions from hexane and heptane are ethylene-propylene rubber phase and E-P block copolymers respectively. The result of solvent fractionation method also shows that custom hexane or heptane extractions can not extract the E-P copolymer completely.

关键词

Keywords

references

Views

Downloads

CSCD

Alert me when the article has been cited

Submit

Tools

Publicity Resources

Organocatalytic Copolymerization of Mixed Type Monomers

Comparison of Chain Structures between High-speed Extrusion Coating Polyethylene Resins by Preparative Temperature Rising Elution Fractionation and Cross-fractionation

Reconstruction of Core-Shell Dispersed Particles in Impact Polypropylene Copolymer during Extrusion

Multiple-Responsive Chiral Hydrogels from Helical Dendronized Poly(phenylacetylene)s

Topology-regulated Co-assembly of Single Chain Polymer Nanoparticles and Block Copolymers into Hierarchical Micelle@Vesicle Composite Structures

Related Author

Qi-lei Song

Shuang-yan Hu

Jun-Peng Zhao

Guang-zhao Zhang

Yan-hu Xue

Shu-qin Bo

Xiang-ling Ji

Feng Chen

Related Institution

Faculty of Materials Science and Engineering, South China University of Technology

State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences

MOE Key Laboratory of Macromolecular Synthesis and Functionalization, Department of Polymer Science and Engineering, Zhejiang University

⁰