MORPHOLOGY OF HEAD-TO-TAIL POLY（3-HEXYLTHIOPHENE） SINGLE CRYSTALS FROM SOLUTION CRYSTALLIZATION

Feature Article | Updated：2021-06-21

- MORPHOLOGY OF HEAD-TO-TAIL POLY（3-HEXYLTHIOPHENE） SINGLE CRYSTALS FROM SOLUTION CRYSTALLIZATION
- Issue 1, Pages: 43-46(2007)
- Affiliations：
  
  1.   State Key Laboratory of Polymer Physics and Chemistry Changchun Institute of Applied Chemistry Chinese Academy of Sciences
  2.   Graduate School of Chinese Academy of Sciences
  3.   Changchun China  ,130022
- Author bio：
- Funds：
  
  This work was financially supported by the Special Funds for Major State Basic Research Projects （No. 2002CB613400） by the National Natural Science Foundation of China （Nos. 90301008, 20474064, and 20521415）.()
- DOI：
  CLC： O633.5
- Published：2007
- Accepted：
Scan QR Code
[1]闫东航.MORPHOLOGY OF HEAD-TO-TAIL POLY(3-HEXYLTHIOPHENE) SINGLE CRYSTALS FROM SOLUTION CRYSTALLIZATION[J].Chinese Journal of Polymer Science,2007(01):43-46.

MORPHOLOGY OF HEAD-TO-TAIL POLY（3-HEXYLTHIOPHENE） SINGLE CRYSTALS FROM SOLUTION CRYSTALLIZATION[J]. 2007, (1): 43-46.
[1]闫东航.MORPHOLOGY OF HEAD-TO-TAIL POLY(3-HEXYLTHIOPHENE) SINGLE CRYSTALS FROM SOLUTION CRYSTALLIZATION[J].Chinese Journal of Polymer Science,2007(01):43-46. DOI：

MORPHOLOGY OF HEAD-TO-TAIL POLY（3-HEXYLTHIOPHENE） SINGLE CRYSTALS FROM SOLUTION CRYSTALLIZATION[J]. 2007, (1): 43-46. DOI：

摘要

<正>Single crystals of head-to-tail poly（3-hexylthiophene）s have been grown through the method of isothermal solution crystallization. Electron diffraction in combination with powder X-ray diffraction revealed the crystal structure

a = 1.52 nm

b = 3.36 nm

c= 1.56 nm andα=β=γ= 90°.

Abstract

Single crystals of head-to-tail poly（3-hexylthiophene）s have been grown through the method of isothermal solution crystallization. Electron diffraction in combination with powder X-ray diffraction revealed the crystal structure

a = 1.52 nm

b = 3.36 nm

c= 1.56 nm andα=β=γ= 90°.

关键词

Keywords

references

Views

144

Downloads

CSCD

Alert me when the article has been cited

Submit

Tools

Publicity Resources

Durable Anti-fogging and Abrasion-resistant Coatings Based on Polyoxometalates-Hydrophilic Resin Composites with Enhanced Cohesion and Adhesion

Pyrimidoisoindigo-based Polymers for Ambipolar Charge Transport

Silk Sericin-inspired Poly-β-homoserine for Protein Protection

Improvements of Hydrophobicity and Toughness of Epoxy Coatings Modified with Hydroxyl-terminated Fluororubber

Bioinspired Zinc-doped Nano Hydroxyapatite Reinforced Poly(lactic acid) Composites for Bone Repair

Related Author

No data

Related Institution

No data

⁰