PREPARATION OF HIGHLY BRANCHED POLYETHYLENE WITH ACENAPHTHENEDHMINE NICKEL CHLORIDE/DIETHYLALUMINUM CHLORIDE CATALYST

Your Location：

Home >

Browse articles >

PREPARATION OF HIGHLY BRANCHED POLYETHYLENE WITH ACENAPHTHENEDHMINE NICKEL CHLORIDE/DIETHYLALUMINUM CHLORIDE CATALYST

Updated：2021-06-21

- PREPARATION OF HIGHLY BRANCHED POLYETHYLENE WITH ACENAPHTHENEDHMINE NICKEL CHLORIDE/DIETHYLALUMINUM CHLORIDE CATALYST
- Issue 5, Pages: 483-488(2006)
- Affiliations：
  
  Institute of Polymer Science Sun Yat-Sen University Guangzhou China ,510275
- Author bio：
- Funds：
  
  This work was supported by the Foundation of Guangdong Province （No. 31598）.()
- DOI：
  CLC： O631.5
- Published：2006
- Accepted：
Scan QR Code
[1]王海华.PREPARATION OF HIGHLY BRANCHED POLYETHYLENE WITH ACENAPHTHENEDHMINE NICKEL CHLORIDE/DIETHYLALUMINUM CHLORIDE CATALYST[J].Chinese Journal of Polymer Science,2006(05):483-488.

PREPARATION OF HIGHLY BRANCHED POLYETHYLENE WITH ACENAPHTHENEDHMINE NICKEL CHLORIDE/DIETHYLALUMINUM CHLORIDE CATALYST[J]. 2006, (5): 483-488.
[1]王海华.PREPARATION OF HIGHLY BRANCHED POLYETHYLENE WITH ACENAPHTHENEDHMINE NICKEL CHLORIDE/DIETHYLALUMINUM CHLORIDE CATALYST[J].Chinese Journal of Polymer Science,2006(05):483-488. DOI：

PREPARATION OF HIGHLY BRANCHED POLYETHYLENE WITH ACENAPHTHENEDHMINE NICKEL CHLORIDE/DIETHYLALUMINUM CHLORIDE CATALYST[J]. 2006, (5): 483-488. DOI：

摘要

<正>The homogeneous catalyst system [ArN = C（Nap） - C（Nap） = NAr]NiCl2 （Nap = 1

8-naphthdiyl

Ar = 2

6-diisopropylphenyl）/AlEt2Cl has been prepared and examined for ethylene polymerization. Polymerization conditions such as cocatalyst

Al/Ni molar ratio and polymerization temperature （Tp） have a great effect on catalytic activity and properties of polyethylenes （PE）. The activity of 5.1×105g PE/mol Ni·h was obtained by the catalyst

activated with AlEt2Cl at 120 of Al/Ni ratio and 30℃. Especially

Tp had a pronounced influence on branches and molecular weight of PE. Branching degree of PE increased with increasing temperature whereas their molecular weight decreased correspondingly. At Tp lower than about 70℃

the resultant PE was an elastic material. When Tp was higher than 70℃

the product was a viscous oil. The resultant PE was confirmed by 13C-NMR to contain significant amounts of not only methyl but also ethyl

propyl

butyl

amyl

and longer branches （longer than six carbons）. According to gel permeation chromatographic measurement

the weight average molecular weights of the polymers obtained ranged from 3.6×103 to 2.3×105.

Abstract

The homogeneous catalyst system [ArN = C（Nap） - C（Nap） = NAr]NiCl2 （Nap = 1

8-naphthdiyl

Ar = 2

6-diisopropylphenyl）/AlEt2Cl has been prepared and examined for ethylene polymerization. Polymerization conditions such as cocatalyst

activated with AlEt2Cl at 120 of Al/Ni ratio and 30℃. Especially

the resultant PE was an elastic material. When Tp was higher than 70℃

the product was a viscous oil. The resultant PE was confirmed by 13C-NMR to contain significant amounts of not only methyl but also ethyl

propyl

butyl

amyl

and longer branches （longer than six carbons）. According to gel permeation chromatographic measurement

the weight average molecular weights of the polymers obtained ranged from 3.6×103 to 2.3×105.

关键词

Keywords

references

Views

Downloads

CSCD

Alert me when the article has been cited

Submit

Tools

Publicity Resources

One-handed Helical Poly(m-terphenyl acetylene)s with Broad Optical Activity Range from Ultraviolet-Visible to Near-infrared Regions

Silk Sericin-inspired Poly-β-homoserine for Protein Protection

Tunable Circularly Polarized Luminescence of Helical Poly(phenylacetylene)s via Side-chain-to-Backbone Förster Resonance Energy Transfer

Experimental Investigation of Graphene and TiO2 Reinforced Poly(vinyl alcohol)-based Fiber Metal Laminates

Multiple-Responsive Chiral Hydrogels from Helical Dendronized Poly(phenylacetylene)s

Related Author

No data

Related Institution

No data

⁰