EFFECT OF SILANE COUPLING AGENT ON THE MECHANICAL, THERMAL PROPERTIES AND MORPHOLOGY OF TREMOLITE/PA1010 COMPOSITES

Xiao-li Liu a; Ye Han a; b; Ge Gao a; Zhi-ying Li a

Your Location：

Home >

Browse articles >

EFFECT OF SILANE COUPLING AGENT ON THE MECHANICAL, THERMAL PROPERTIES AND MORPHOLOGY OF TREMOLITE/PA1010 COMPOSITES

Papers | Updated：2021-06-21

- EFFECT OF SILANE COUPLING AGENT ON THE MECHANICAL, THERMAL PROPERTIES AND MORPHOLOGY OF TREMOLITE/PA1010 COMPOSITES
- Vol. 26, Issue 3, Pages: 255-262(2008)
- Affiliations：
- Author bio：
- Funds：
- DOI：
  CLC：
- Published：20 May 2008
- Accepted：
Scan QR Code
Xiao-li Liu a, Ye Han a, b, et al. EFFECT OF SILANE COUPLING AGENT ON THE MECHANICAL, THERMAL PROPERTIES AND MORPHOLOGY OF TREMOLITE/PA1010 COMPOSITES[J]. 2008, 26(3): 255-262.
DOI：

Xiao-li Liu a, Ye Han a, b, et al. EFFECT OF SILANE COUPLING AGENT ON THE MECHANICAL, THERMAL PROPERTIES AND MORPHOLOGY OF TREMOLITE/PA1010 COMPOSITES[J]. 2008, 26(3): 255-262. DOI：

摘要

Tremolite

a kind of inorganic filler

was modified with a silane coupling agent γ-methacryloxypropyl trimethoxy silane (MPS) in ethanol/ammonia solution. The graft of MPS on tremolite was confirmed by X-ray photoelectron spectroscopy (XPS)

IR and thermogramitric analysis (TGA) measurements. In addition

contact angle analysis showed that particle surface property was changed from hydrophilicity to hydrophobicity after the modification. Modified tremolite and pure tremolite were blended respectively with PA1010 (polydecamethylene esbacamide) and the mechanical properties of the composites were studied. Results revealed that MPS had a remarkable influence on the mechanical properties of the composites due to the improvement of interfacial adhesion between filler and matrix. Tensile strength and notched Izod impact strength of MPS-modified tremolite composites were improved simultaneously compared to those with pure tremolite. Composites with MPS modified tremolite exhibited a much higher thermal stability than the samples with pure tremolite confirmed by TGA. The morphologies of the composites were also investigated using scanning electron microscopy (SEM). Results showed that better dispersion of MPS modified tremolite in matrix was obtained.

Abstract

Tremolite

a kind of inorganic filler

IR and thermogramitric analysis (TGA) measurements. In addition

关键词

Keywords

references

Views

Downloads

CSCD

Alert me when the article has been cited

Submit

Tools

Publicity Resources

Upgrading Commercially Available Polyethylene to High-value Materials with Strong Mechanical Performance and Hydrophilicity by Blending with Ethylene/meta-Methoxystyrene Copolymers

Two-way Shape Memory Effect of Polycaprolactone-based Polyurethane via Synergistic Role of Hydrogen Bonding and Crystallization Tuned by Malic Acid

Alternating Poly(ether-alt-ester)s with High Glass Transition Temperature Enabled by Rotationally Constrained Biaryl Units

Sequence-encoded Conformation Pathways in Viscoelastic Microphase Separation of Multiblock Copolymers

Energy Storage Performance of Supercapacitors with Polyelectrolyte Surface Coatings: Effects of Dielectric Contrast

Related Author

No data

Related Institution

No data

⁰