PARTICLE MORPHOLOGY OF POLY(VINYL CHLORIDE)RESIN PREPARED BY SUSPENDED EMULSION POLYMERIZATION*

Your Location：

Home >

Browse articles >

PARTICLE MORPHOLOGY OF POLY(VINYL CHLORIDE)RESIN PREPARED BY SUSPENDED EMULSION POLYMERIZATION*

Papers | Updated：2021-06-21

- PARTICLE MORPHOLOGY OF POLY(VINYL CHLORIDE)RESIN PREPARED BY SUSPENDED EMULSION POLYMERIZATION*
- Vol. 21, Issue 4, Pages: 447-452(2003)
- Affiliations：
- Author bio：
- Funds：
- DOI：
  CLC：
- Published：20 August 2003
- Accepted：
Scan QR Code
PARTICLE MORPHOLOGY OF POLY(VINYL CHLORIDE)RESIN PREPARED BY SUSPENDED EMULSION POLYMERIZATION*[J]. 2003, 21(4): 447-452.
DOI：

PARTICLE MORPHOLOGY OF POLY(VINYL CHLORIDE)RESIN PREPARED BY SUSPENDED EMULSION POLYMERIZATION*[J]. 2003, 21(4): 447-452. DOI：

摘要

Suspended emulsion polymerization was used to prepare poly(vinyl chloride) (PVC) resin. Fine PVC particleswere formed at low polymerization conversions. The amount of fine panicles decreases as conversion increases anddisappears at conversions greater than 30%. Scanning electron micrographs show that PVC grains are composed of looselycoalesced primary particles

especially for PVC resins prepared in the presence of poly(vinyl alcohol) dispersant. The size ofprimary particles increases and porosity decreases with the increase of conversion.In view of the particle features of PVC resin

a particle formation mechanism including the formation of primary particles and grains is proposed.The formation process of primary particles includes the formation of particle nuclei

coalescence of particle nuclei to form primary particles

and growth of primary particles.PVC grains are formed by the coagulation of primary particles.The loose coalescence of primary particles is caused by the colloidal stability of primary particles and the low swelling degree of vinyl chloride in the primary particles.

Abstract

a particle formation mechanism including the formation of primary particles and grains is proposed.The formation process of primary particles includes the formation of particle nuclei

coalescence of particle nuclei to form primary particles

关键词

Keywords

references

Views

Downloads

CSCD

Alert me when the article has been cited

Submit

Tools

Publicity Resources

Upgrading Commercially Available Polyethylene to High-value Materials with Strong Mechanical Performance and Hydrophilicity by Blending with Ethylene/meta-Methoxystyrene Copolymers

Enhancing Processability of Phenylethynyl-terminated Imide Oligomers and Properties of Cured Polyimides via ―CF3 Incorporation

A Paradigm for BF3 Co-initiated Cationic Polymerization with Low Dispersity: Introducing Acetonitrile and Lowering the Reaction Temperature

Alternating Poly(ether-alt-ester)s with High Glass Transition Temperature Enabled by Rotationally Constrained Biaryl Units

Topology-regulated Co-assembly of Single Chain Polymer Nanoparticles and Block Copolymers into Hierarchical Micelle@Vesicle Composite Structures

Related Author

No data

Related Institution

No data

⁰