MODIFICATION OF EPOXY RESIN WITH POLYSILOXANE BEARING PENDANT QUATERNARY AMMONIUM GROUPS

Your Location：

Home >

Browse articles >

MODIFICATION OF EPOXY RESIN WITH POLYSILOXANE BEARING PENDANT QUATERNARY AMMONIUM GROUPS

Papers | Updated：2021-06-21

- MODIFICATION OF EPOXY RESIN WITH POLYSILOXANE BEARING PENDANT QUATERNARY AMMONIUM GROUPS
- Vol. 20, Issue 6, Pages: 537-541(2002)
- Affiliations：
- Author bio：
- Funds：
- DOI：
  CLC：
- Published：20 December 2002
- Accepted：
Scan QR Code
MODIFICATION OF EPOXY RESIN WITH POLYSILOXANE BEARING PENDANT QUATERNARY AMMONIUM GROUPS[J]. 2002, 20(6): 537-541.
DOI：

MODIFICATION OF EPOXY RESIN WITH POLYSILOXANE BEARING PENDANT QUATERNARY AMMONIUM GROUPS[J]. 2002, 20(6): 537-541. DOI：

摘要

Polysiloxane bearing pendant quaternary ammonium groups (PSI) was used to modify the surface properties ofepoxy resins. In the cured resin

PSI formed the dispersed phase. Remarkable enrichment and gradient distribution ofpolysiloxane on the surface region of the epoxy resins were demonstrated by XPS analysis. The composition and propertiesof the surface of PSI-modified epoxy resin

which is in contact with the mold

are dependent on the material of the mold.Through the incorporation of PSI

epoxy resins with low surface energy and low friction coefficient were obtained.Polysiloxane with lower ionic group content shows a higher degree of enrichment on the resin surface and leads to a higher contact angle against water

while the polysiloxane having optimum compatibility with the epoxy resin shows a greater effect in reducing the static friction coefficient of the resin against glass.

Abstract

Polysiloxane bearing pendant quaternary ammonium groups (PSI) was used to modify the surface properties ofepoxy resins. In the cured resin

which is in contact with the mold

are dependent on the material of the mold.Through the incorporation of PSI

while the polysiloxane having optimum compatibility with the epoxy resin shows a greater effect in reducing the static friction coefficient of the resin against glass.

关键词

Keywords

references

Views

Downloads

CSCD

Alert me when the article has been cited

Submit

Tools

Publicity Resources

Advances in Polymer-based Circularly Polarized Luminescent Materials

Two-way Shape Memory Effect of Polycaprolactone-based Polyurethane via Synergistic Role of Hydrogen Bonding and Crystallization Tuned by Malic Acid

A Paradigm for BF3 Co-initiated Cationic Polymerization with Low Dispersity: Introducing Acetonitrile and Lowering the Reaction Temperature

Upgrading Commercially Available Polyethylene to High-value Materials with Strong Mechanical Performance and Hydrophilicity by Blending with Ethylene/meta-Methoxystyrene Copolymers

Squaramide-directed Cooperative One-dimensional Assembly in Telechelic Polydimethylsiloxane for Hierarchical Network Formation

Related Author

No data

Related Institution

No data

⁰