STUDIES ON TUNG OIL COATED REGENERATED CELLULOSE FILMS WITH WATERRESISTANCE

ZHANG Lina; YAN Shanhong

Your Location：

Home >

Browse articles >

STUDIES ON TUNG OIL COATED REGENERATED CELLULOSE FILMS WITH WATERRESISTANCE

Papers | Updated：2021-06-21

- STUDIES ON TUNG OIL COATED REGENERATED CELLULOSE FILMS WITH WATERRESISTANCE
- Vol. 13, Issue 1, Pages: 78-83(1995)
- Affiliations：
  
  1.   Department of Chemistry
  2.   Wuhan University
  3.   Wuhan 430072
- Author bio：
- Funds：
- DOI：
  CLC： O636.1
- Published：20 March 1995
- Accepted：
Scan QR Code
[1]张俐娜,严山红.STUDIES ON TUNG OIL COATED REGENERATED CELLULOSE FILMS WITH WATERRESISTANCE[J].Chinese Journal of Polymer Science,1995,{4}(01):78-83.

ZHANG Lina, YAN Shanhong. STUDIES ON TUNG OIL COATED REGENERATED CELLULOSE FILMS WITH WATERRESISTANCE[J]. 1995, 13(1): 78-83.
[1]张俐娜,严山红.STUDIES ON TUNG OIL COATED REGENERATED CELLULOSE FILMS WITH WATERRESISTANCE[J].Chinese Journal of Polymer Science,1995,{4}(01):78-83. DOI：

ZHANG Lina, YAN Shanhong. STUDIES ON TUNG OIL COATED REGENERATED CELLULOSE FILMS WITH WATERRESISTANCE[J]. 1995, 13(1): 78-83. DOI：

摘要

<正> Regenerated cellulose films with water-resistance were obtained by an improved method ofpreparing cellulose cuoxam solution from pulps of agricultural wastes （linters

wheat straw

reedand Bamao）. Experimental results showed that the mechanical properties of both the dry. and wetfilms were excellent. Data from IR

SEM and tensile strength measurements implied that thesignificant improvement of water-resistance of the films was due to the cohesion between the thinTung oil covers with hydrophobicity and the regenerated cellulose films. The films werecompletely biodegraded after being buried in soil for 100 days. The transmittance of the filmsderived from linter and reed in visible band range were 80-90%.

Abstract

Regenerated cellulose films with water-resistance were obtained by an improved method ofpreparing cellulose cuoxam solution from pulps of agricultural wastes （linters

wheat straw

reedand Bamao）. Experimental results showed that the mechanical properties of both the dry. and wetfilms were excellent. Data from IR

关键词

Keywords

references

Views

Downloads

CSCD

Alert me when the article has been cited

Submit

Tools

Publicity Resources

Advances in Polymer-based Circularly Polarized Luminescent Materials

Durable Anti-fogging and Abrasion-resistant Coatings Based on Polyoxometalates-Hydrophilic Resin Composites with Enhanced Cohesion and Adhesion

Tunable Circularly Polarized Luminescence of Helical Poly(phenylacetylene)s via Side-chain-to-Backbone Förster Resonance Energy Transfer

One-handed Helical Poly(m-terphenyl acetylene)s with Broad Optical Activity Range from Ultraviolet-Visible to Near-infrared Regions

2026-9 Contents

Related Author

No data

Related Institution

No data

⁰