FREE STANDING FILM OF POLYANILINE

WAN Meixiang; CAO Yong; LI Junchao; ZHOU Weixia; LI Suzhen

Your Location：

Home >

Browse articles >

FREE STANDING FILM OF POLYANILINE

Papers | Updated：2021-06-21

- FREE STANDING FILM OF POLYANILINE
- Vol. 9, Issue 3, Pages: 209-219(1991)
- Affiliations：
  
  1. Institute of Chemistry, Academia Sinica,Beijing
  2. Academia Sinica
  3. Beijing
- Author bio：
- Funds：
- DOI：
  CLC：
- Published：20 September 1991
- Accepted：
Scan QR Code
[1]万梅香,曹镛,李军朝,周维侠,李素珍.FREE STANDING FILM OF POLYANILINE[J].Chinese Journal of Polymer Science,1991,{4}(03):209-219.

WAN Meixiang, CAO Yong, LI Junchao, et al. FREE STANDING FILM OF POLYANILINE[J]. 1991, 9(3): 209-219.
[1]万梅香,曹镛,李军朝,周维侠,李素珍.FREE STANDING FILM OF POLYANILINE[J].Chinese Journal of Polymer Science,1991,{4}(03):209-219. DOI：

WAN Meixiang, CAO Yong, LI Junchao, et al. FREE STANDING FILM OF POLYANILINE[J]. 1991, 9(3): 209-219. DOI：

摘要

<正> A free standing film of polyaniline as large as 18 cm×18cm×0.002 cm can be obtained by evaporation of a solution of the chemically synthesized base in NMP. Its structure was examined by the elemental analysis

U.V.-visible spectra

XPS

DSC

SEM and X-ray scattering and its conducting behavior as well as electrochemical properties were studied. Results show that the composition

structure of main chain

physical properties of the free standing film of polyanilme is similar to that of the powder. However

some differences in its electronic structure

conductivity at room temperature and potential of redox couple between the flee standing film and powder are observed

which may be due to cross-linking of the film of polyaniline.

Abstract

A free standing film of polyaniline as large as 18 cm×18cm×0.002 cm can be obtained by evaporation of a solution of the chemically synthesized base in NMP. Its structure was examined by the elemental analysis

U.V.-visible spectra

XPS

DSC

SEM and X-ray scattering and its conducting behavior as well as electrochemical properties were studied. Results show that the composition

structure of main chain

physical properties of the free standing film of polyanilme is similar to that of the powder. However

some differences in its electronic structure

conductivity at room temperature and potential of redox couple between the flee standing film and powder are observed

which may be due to cross-linking of the film of polyaniline.

关键词

Keywords

references

Views

Downloads

CSCD

Alert me when the article has been cited

Submit

Tools

Publicity Resources

2026-9 Contents

One-handed Helical Poly(m-terphenyl acetylene)s with Broad Optical Activity Range from Ultraviolet-Visible to Near-infrared Regions

Upgrading Commercially Available Polyethylene to High-value Materials with Strong Mechanical Performance and Hydrophilicity by Blending with Ethylene/meta-Methoxystyrene Copolymers

pH-Responsive L-Cysteine-conjugated Polydopamine Nanocarriers for Controlled Release of Emamectin Benzoate against Pieris brassicae

Improvements of Hydrophobicity and Toughness of Epoxy Coatings Modified with Hydroxyl-terminated Fluororubber

Related Author

No data

Related Institution

No data

⁰